Magnesium alloy and manufacturing method thereof

A manufacturing method and magnesium alloy technology, applied in the field of magnesium alloy materials and magnesium alloy material manufacturing, can solve problems such as poor weldability, overweight, and insufficient ductility of magnesium alloys, and achieve reduced material density, novel components, Reasonable and clear effect of the production process

Inactive Publication Date: 2018-02-23
叶秀兰
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the problems of insufficient ductility, poor weldability, and overweight caused by excessive density of existing magnesium alloys. The present invention provides a magnesium alloy and its manufacturing method. By changing its smelting process, its quality be improved to achieve the purpose of improving its quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below:

[0021] A magnesium alloy consisting of the following elements:

[0022] Magnesium element, its weight percentage is 85% of the total alloy composition;

[0023] Lithium element, its weight percentage is 12% of the total composition of the alloy;

[0024] Zinc element, its weight percentage is 2% of the total composition of the alloy;

[0025] Manganese element, its weight percentage is 0.3% of the total composition of the alloy;

[0026] Silicon element, its weight percentage is 0.2% of the total composition of the alloy.

[0027] A method for manufacturing a magnesium alloy, comprising the steps of:

[0028] (1) placing an alloy material comprising the magnesium element and the silicon element into a crucible of a vacuum induction melting furnace;

[0029] (2) Vacuumizing the vacuum induction melting furnace;

[0030] (3) heating the crucible of the vacuum induction melting furnace to melt the alloy materia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A magnesium alloy and a manufacturing method thereof, belonging to the technical field of metal materials and heat treatment, the magnesium element, whose weight percentage is 85% of the total composition of the alloy; the lithium element, whose weight percentage is 12% of the total alloy composition; the zinc element, whose weight percentage The percentage is 2% of the total composition of the alloy; the weight percentage of manganese element is 0.3% of the total composition of the alloy; the weight percentage of silicon element is 0.2% of the total composition of the alloy. The composition of the invention is novel, and the production process is reasonable and clear, so that after the alloy melt is solidified into an ingot and extruded into a magnesium-lithium alloy material, while reducing the material density, its overall structure is uniform and fine, and lithium and aluminum elements will The aluminum-lithium phase is precipitated by the reaction, or the magnesium silicide compound is precipitated by the reaction of the magnesium element and the silicon element, so as to improve the rigidity and strength of the magnesium alloy without damaging its ductility.

Description

technical field [0001] The invention belongs to the technical field of metal materials and heat treatment, and relates to a magnesium alloy material and a manufacturing method of the magnesium alloy material. Background technique [0002] With the development of science and technology, the design of various products is now moving towards the goal of light weight and environmental protection. Therefore, a considerable degree of consideration needs to be given to the development of product materials and the selection of characteristics. Among them, the application range of alloy materials is the most extensive. Taking magnesium alloy materials as an example, magnesium metal has the advantages of light weight, high shock resistance, and excellent recyclability among practical metals, and it can be combined with other metal elements. Combined to form a magnesium alloy material with a high strength-to-weight ratio, and good impact and wear resistance. [0003] Taking AZ80 magnes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/00C22C1/10
CPCC22C23/00C22C1/1036
Inventor 叶秀兰
Owner 叶秀兰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products