Special high-frequency water-based quenching liquid for induction gear and preparation method of special high-frequency water-based quenching liquid for induction gear

A water-based quenching and induction gear technology, applied in the field of quenching liquid, can solve the problems of insufficient hardness of the surface hardened layer, shallow hardened layer of the workpiece, general cooling performance, etc., achieve uniform hardness, deep hardened layer, and improve hardness not enough effect

Inactive Publication Date: 2018-01-30
郑州市欧普士科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The high-frequency quenching machine adopts induction heating to quench various gears. The quenching liquid currently used is made of general mineral base oil plus common refrigerants, antioxidants and other additives. In this case, it is prepared according to the current technology. The cooling performance of quenching oil is average, and the cooling rate is lower than the critical cooling rate. As a result, the hardened layer of the workpiece with low hardenability is shallow and the hardness of the surface hardened layer is not enough. The liquid cooling speed is extremely fast, and the water-based quenching liquid is used, which has good environmental protection performance and deepens the hardened layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A special high-frequency water-based quenching liquid for induction gears, including the following substances in parts by weight: 25 parts of high-molecular polyvinyl alcohol resin particles; 50 parts of deionized water; 1 part of high-efficiency brightener; 2.5 parts of anti-corrosion inhibitor 1.5 parts of surfactants; wherein, the high-efficiency brightener is a mixture of nonylphenol polyoxyethylene ether and polyurethane; A mixture of cycyl imidazolinyl succinate; the surfactant is a mixture of sodium linear alkylbenzene sulfonate and sodium lauryl sulfate.

[0015] A method for preparing a special high-frequency water-based quenching liquid for induction gears, comprising the following steps:

[0016] (1) Dissolve 25 parts of polymer polyvinyl alcohol resin particles in 50 parts of deionized water at room temperature, stir for 20 minutes, then heat to 80°C, and continue stirring for 2 hours at constant temperature;

[0017] (2) Filter out impurities, then add 1 p...

Embodiment 2

[0019] A special high-frequency water-based quenching liquid for induction gears, including the following substances in parts by weight: 26.5 parts of high-molecular polyvinyl alcohol resin particles; 55 parts of deionized water; 2.0 parts of high-efficiency brightener; 2.75 parts of anti-corrosion inhibitor 1.75 parts of surfactants; wherein, the high-efficiency brightener is a mixture of nonylphenol polyoxyethylene ether and imidazoline oleate; the anticorrosion inhibitor is N-oleic acid sarcosine stearylamine salt, heptadecyl imidazolidinyl succinate; the surfactant is a mixture of sodium linear alkylbenzene sulfonate and nonylphenol polyoxyethylene ether.

[0020] A method for preparing a special high-frequency water-based quenching liquid for induction gears, comprising the following steps:

[0021] (1) Dissolve 26.5 parts of polymer polyvinyl alcohol resin particles in 55 parts of deionized water at room temperature, stir for 23 minutes, then heat to 83°C, and continue s...

Embodiment 3

[0024] A special high-frequency water-based quenching liquid for induction gears, including the following substances in parts by weight: 30 parts of high-molecular polyvinyl alcohol resin particles; 60 parts of deionized water; 2.5 parts of high-efficiency brightener; 3 parts of anti-corrosion inhibitor 2 parts of surfactants; wherein, the high-efficiency brightener is a mixture of acrylic acid and sodium benzoate; The mixture of both base succinates; the surfactant is a mixture of sodium lauryl sulfate and nonylphenol polyoxyethylene ether.

[0025] A method for preparing a special high-frequency water-based quenching liquid for induction gears, comprising the following steps:

[0026] (1) Dissolve 30 parts of polymer polyvinyl alcohol resin particles in 60 parts of deionized water at room temperature, stir for 25 minutes, then heat to 85°C, and continue stirring for 2.5 hours at constant temperature;

[0027] (2) Filter out impurities, then add 2.5 parts of high-efficiency ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a special high-frequency water-based quenching liquid for an induction gear. The special high-frequency water-based quenching liquid for the induction gear is prepared from thefollowing substances in parts by weight: 25-30 parts of polymer polyvinyl alcohol resin particles, 50-60 parts of deionized water, 1-2.5 parts of an efficient brightener, 2.5-3 parts of an anticorrosion inhibitor and 1.5-2 parts of a surfactant. A preparation method of the special high-frequency water-based quenching liquid for the induction gear comprises the following steps of (1) in a normal temperature state, dissolving a proper amount of the polymer polyvinyl alcohol resin particles into a certain amount of the deionized water, performing stirring for 20-25min, then heating a mixture to80-85 DEG C, and performing continuous stirring for 2-2.5h at a constant temperature; and (2) filtering impurities from a mixture, then sequentially adding the efficient brightener, the anticorrosioninhibitor and the surfactant according to a ratio, performing continuous stirring for 40-60min, and performing uniform stirring to obtain the special high-frequency water-based quenching liquid for the induction gear. The special high-frequency water-based quenching liquid for the induction gear can greatly improve the cooling performance during quenching of the induction gear, is small in oil fume after quenching, pointedly solves the problem of insufficient hardness of quenching structures of various induction gears, is good in mechanism performance with a metallographic structure, is permanently sheeny and is liable to clean.

Description

technical field [0001] The invention relates to the technical field of quenching liquid, in particular to a special high-frequency water-based quenching liquid for induction gears and a preparation method thereof. Background technique [0002] The quenching liquid is made of polyether polymer materials with various surfactants added, and has many advantages, 1. It is safe and environmentally friendly because it is soluble in water. 2. Low cost and economical. 3. High calorific value. 4. 1. The processed workpiece has high hardness, less deformation, deep hardened layer, 5. Strong anti-corrosion performance, good anti-corrosion durability, 6. Long service life, so it is widely used in heat treatment of workpieces. [0003] The high-frequency quenching machine adopts induction heating to quench various gears. The quenching liquid currently used is made of general mineral base oil plus common refrigerants, antioxidants and other additives. In this case, it is prepared according...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/60C21D9/32
Inventor 乔传威郑金周耿再新孙志强
Owner 郑州市欧普士科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products