Wear-resistant belt material composition, and wear-resistant belt and preparation method thereof

Abstract

The invention discloses a wear-resistant belt material composition, and a wear-resistant belt and a preparation method thereof. The composition comprises styrene-butadiene rubber, nitrile-butadiene rubber, a coumarone indene resin, nano calcium carbonate, nano calcium oxide, paraffin, silicone oil and sulfur. Relative to 100 parts by weight of the styrene-butadiene rubber, the content of the nitrile-butadiene rubber is 30-60 parts by weight, the content of the coumarone indene resin is 10-30 parts by weight, the content of the nano calcium carbonate is 1-5 parts by weight, the content of the nano calcium oxide is 1-5 parts by weight, the content of the paraffin is 3-10 parts by weight, the content of the silicone oil is 5-15 parts by weight, and the content of the sulfur is 2-6 parts by weight. Through the design, the effects of effectively resisting wear, greatly lowering the replacement cost and use cost and enhancing the production efficiency are realized.

Description

technical field [0001] The invention relates to the field of belt materials, in particular to a wear-resistant belt material composition, a wear-resistant belt and a preparation method thereof. Background technique [0002] As an important part of the knitting machine, the belt is mainly responsible for transmission and other functions, and the frequency of use of the belt in the knitting machine is extremely high. Therefore, in long-term use, the belt is often damaged first, resulting in the need to disassemble the knitting machine. Replacing the belt greatly increases the replacement cost and maintenance cost of the belt. At the same time, the replacement of the belt will also cause production stoppage, thereby resulting in a reduction in production efficiency. [0003] Therefore, it is an urgent problem to be solved in the present invention to improve a wear-resistant belt material composition, a wear-resistant belt and a preparation method thereof that can effectively re...

AI Technical Summary

Problems solved by technology

[0004] In view of the above prior art, the purpose of the present invention is to overcome the fact that the belt in the knitting machine in the prior art is often damaged first, which leads to the need to replace the belt after the knitting machine is disassembled, which greatly increases the replacement cost and maintenance cost of the belt. At the same time, the replacement of the belt It will also cause production stoppage and reduce production efficiency, thereby providing a wear-resistant belt material composition, a wear-resistant belt and its preparation that can effectively wear and tear, greatly reduce replacement costs and use costs, and improve production efficiency method