Steel ladle composite down nozzle and preparation method thereof

A technology for ladle and molten steel, applied in the field of ladle composite sewers and their preparation, can solve the problems of sprue breakage, drop, and crack life, and achieve the effects of ensuring safe use, reducing costs, and low production costs

Inactive Publication Date: 2018-01-16
云南濮耐昆钢高温材料有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, aluminum-carbon material is mostly used for the ladle’s lower nozzle. The conventional method is to use one material. The lower nozzle is scoured and eroded by high-temperature molten steel during use, and the casting hole of the nozzle is enlarged, and the diameter of the enlarged hole is 3-10mm. , and the thickness of the inner wall of the nozzle is at least 20mm or more. In view of this phenomenon, some manufacturers use low-grade single material, which causes the phenomenon of breakage, cracks or life reduction of the nozzle during use, and there is a greater risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel ladle composite down nozzle and preparation method thereof
  • Steel ladle composite down nozzle and preparation method thereof
  • Steel ladle composite down nozzle and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of steel ladle composite drain, such as figure 1 As shown, it includes a body 2 and a composite body 1, the body 2 is in direct contact with the high-temperature molten steel, and the composite body 1 is arranged outside the body 2 and does not directly contact the molten steel. When the compound drain works, the body 2 is scoured and eroded by the molten steel, and the complex 1 is not in contact with the molten steel.

[0042] The ladle composite drain includes the following raw materials in parts by weight:

[0043] a Body 2: 94.5 parts of high alumina bauxite, 4 parts of graphite, 0.5 parts of metal aluminum powder, 1 part of metal silicon powder, and 3.2 parts of phenolic resin;

[0044] b Complex 1: 95 parts of recycled slide plate, 3.5 parts of graphite, 0.5 part of metal aluminum powder, 1 part of metal silicon powder, and 3.5 parts of phenolic resin.

[0045] The preparation method of the ladle composite nozzle comprises the following steps:

[0046] ...

Embodiment 2

[0052] A ladle composite drain, comprising the following raw materials in parts by weight:

[0053] a Body: 88 parts of high alumina bauxite, 3 parts of graphite, 0.2 parts of metal aluminum powder, 0.5 parts of metal silicon powder, 3.0 parts of phenolic resin;

[0054] b complex: 85 parts of recycled slide plate, 2 parts of graphite, 0.5 part of metal aluminum powder, 0.5 part of metal silicon powder, and 3.0 parts of phenolic resin.

Embodiment 3

[0056] A ladle composite drain, comprising the following raw materials in parts by weight:

[0057] a body: 96 parts of high alumina bauxite, 6 parts of graphite, 1 part of metal aluminum powder, 2 parts of metal silicon powder, 3.5 parts of phenolic resin;

[0058] b complex: 96 parts of recycled slide plate, 6 parts of graphite, 1 part of metal aluminum powder, 2 parts of metal silicon powder, 3.5 parts of phenolic resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel ladle composite down nozzle and a preparation method thereof. The steel ladle composite down nozzle comprises a body and a composite body, wherein the body comprises the following raw materials in parts by weight: 88-96 parts of high alumina bauxite, 3-6 parts of graphite, 0.2-1 part of metal aluminum powder, 0.5-2 parts of metal silicon powder, and 3.0-3.5 parts ofphenolic resin; and the composite body comprises the following raw materials in parts by weight: 85-96 parts of recycled slide plates, 2-6 parts of graphite, 0.5-1 part of metal aluminum powder, 0.5-2 parts of metal silicon powder, and 3.0-3.5 parts of phenolic resin. The steel ladle composite down nozzle obtained by the method has the advantages of high-temperature resistance, good thermal shockresistance, corrosion resistance, high thermal shock strength and low production costs, and meanwhile, the preparation method is simple and convenient for expanded production. According to the invention, composite forming is adopted, the body material is adopted around a casting hole, the composite material is adopted at other parts, thus service life is guaranteed, at the same time the materialcosts are reduced, and the cost performance is relatively high.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a ladle composite drain nozzle and a preparation method thereof. Background technique [0002] The ladle lower nozzle is the molten steel conveying part, installed at the bottom of the ladle, it forms the ladle flow control system with the upper nozzle and the slide plate, and is one of the most critical flow control system functional components in the continuous casting process. The drain must have high strength, strong oxidation resistance, excellent thermal shock stability, and excellent erosion resistance. [0003] In the prior art, aluminum-carbon material is mostly used for the ladle’s lower nozzle. The conventional method is to use one material. The lower nozzle is scoured and eroded by high-temperature molten steel during use, and the casting hole of the nozzle is enlarged, and the diameter of the enlarged hole is 3-10mm. , and the thickness of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/103C04B35/634C04B35/622B22D41/54
Inventor 唐兵张向前于宝童康云伟段忠诚
Owner 云南濮耐昆钢高温材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com