A kind of high remanence material and preparation method thereof

A high remanence, alloy material technology, applied in the direction of magnetic materials, inorganic material magnetism, magnetic objects, etc., can solve the problem of low remanence, and achieve the effect of improving remanence, eliminating direct contact and simple process

Active Publication Date: 2019-04-23
太原市迪辉磁材科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the advancement of technology, it seems that the remanence of this material is not high at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high remanence material and preparation method thereof
  • A kind of high remanence material and preparation method thereof
  • A kind of high remanence material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described below in conjunction with specific examples.

[0029] A high remanence material, which is composed of three alloy materials I, II, III and an oxide complex IV;

[0030] The weight percentage of each component in the alloy material I is: Ga 0.7-0.9%, Bi 3-5%, Cr 0.1-0.5%, W 0.02-0.05%, V 0.05-0.09%, B 2-4%, Nd 20-25%, the rest Fe;

[0031] The weight percentage of each component in the alloy material II is: Sm 18-21%, Pt 0.02%-0.05%, Ge 0.06%-0.09%, Be 0.02%-0.08%, B 2-4%, and the rest Fe;

[0032] The weight percentage of each component in the alloy material III is: Pr 2-5%, Al 3-6%, Si 6-10%, and the rest Fe;

[0033] The weight percentage of each component in the inorganic composite material IV is: BaO 3-7%, Ce 2 o 3 0.1-0.4%, CuO0.1-0.4%, SiO 2 0.1-0.4%, K 2 O 0.1-0.4%, Na 2 O 0.1-0.4%, the rest Fe 2 o 3 ;

[0034] The weight ratio of the alloy materials I, II, III to the oxide complex IV is 1.2:1:(0.02-0.05):...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-residual-magnetism material and a preparation method therefor. The high-residual-magnetism material consists of a combination of three kinds of alloy materials I, II and III, and an oxide complex IV; the materials are prepared separately, and the alloy materials I, II and III, and the oxide complex IV are prepared based on the weight ratio and added to a three-dimensional mixer to be mixed uniformly to obtain mixed powder; next, the mixed powder is subjected to orientation in a magnetic field press and shaped by adopting an isostatic pressing mode; and the formed blank is put into a sintering furnace under argon protection to be subjected to sintering treatment to obtain a high-residual-magnetism product. The alloy preparation process is simple and convenient, the process is simple, and the produced alloys have high performance, so that industrial production can be realized very conveniently.

Description

technical field [0001] The invention relates to the field of materials, in particular to a high remanence material and a preparation method thereof. Background technique [0002] At present, in the field of high remanence materials, the process technology still needs to be improved. For example, the invention patent with the patent application number CN201610781202.3 involves a high coercive force RFeB system sintered magnet and its preparation method. Prepare R-Fe-B based sintered magnets with a thickness of 1-15mm, and then cover the surface of the magnet evenly with a mixed slurry made of ultra-fine terbium powder with an average powder particle size SMD of 1-2.5μm, an organic solvent, and an antioxidant , and heat treatment, this method can improve the coercive force of the magnet> 10kOe, and the remanence reduction is less than 0.2kGs. [0003] However, with the advancement of technology, it seems that the remanence of this material is not high. Aiming at the above...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/09H01F1/059H01F1/147C22C38/32C22C38/22C22C38/24C22C38/06C22C38/02
Inventor 李庆芳董英华陶昭灵赵浩峰
Owner 太原市迪辉磁材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com