Scrubbing-resistant shell powder paint for efficiently decomposing formaldehydes

A technology of shell powder and scrub resistance, which is applied in the fields of environmental protection and resource recycling, and can solve problems such as not being resistant to scrubbing, difficult to remove or even decompose toxic and harmful gases, and difficult to solve problems such as powder falling.

Active Publication Date: 2017-12-15
中科海洋生物再生资源(天津)有限公司
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Most of the existing shell powder coatings rely on porous structures to absorb toxic and harmful gases, but it is difficult to achieve the effect of removing or even decomposing toxic and harmful gases
Existing shell powder coatings also have the disadvantages that it is difficult to solve the problem of powder falling off and not resistant to scrubbing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, the preparation steps of the rare earth antibacterial agent in its components include:

[0029] In parts by weight, 1 part of 2-(5-norbornene-2,3-dicarboximido)-1,1,3,3-tetramethylurea tetrafluoroborate quaternary ammonium salt was dispersed in In 100 parts of ethanol, add 7 parts of tris(cyanodienyl) cerium, 0.04 part of S-allethrin, 0.03 part of tetramethylguanidine trifluoromethanesulfonate, 0.03 part of benzoyl peroxide, 0.04 part of polyvinyl alcohol, heated up, and reacted at 70°C for 8 hours, and the product was filtered and dried to obtain the rare earth antibacterial agent.

[0030] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, comprising the following components:

[0031] by weight,

[0032] Shell Powder 100

[0033] Burnt Shell Powder 0.3

[0034] Nanoscale titanium dioxide 0.6

[0035] latex powder 18

[0036] Zinc oxide 0.04

[0037] Ra...

Embodiment 2

[0041] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, the preparation steps of the rare earth antibacterial agent in its components include:

[0042] In parts by weight, 0.5 parts of 2-(5-norbornene-2,3-dicarboximido)-1,1,3,3-tetramethyluronium tetrafluoroborate quaternary ammonium salt was dispersed in In 100 parts of ethanol, add 5 parts of tris(cyanodienyl) cerium, 0.01 part of S-allethrin, 0.01 part of tetramethylguanidine bisulfate, 0.01 part of benzoyl peroxide, 0.05 part of polyethylene Alcohol, heat up, react at 60°C for 15 hours, filter the product, and dry to obtain the rare earth antibacterial agent.

[0043] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, comprising the following components:

[0044] by weight,

[0045] Shell Powder 100

[0046] Burnt Shell Powder 0.1

[0047] Nanoscale titanium dioxide 0.1

[0048] latex powder 13

[0049] Zinc oxide 0.01

[0050] Rare earth antibacterial ag...

Embodiment 3

[0054] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, the preparation steps of the rare earth antibacterial agent in its components include:

[0055] In parts by weight, 0.5-2 parts of 2-(5-norbornene-2,3-dicarboximido)-1,1,3,3-tetramethyluronium tetrafluoroborate quaternary ammonium salt Disperse in 100 parts of ethanol, add 5-15 parts of tris(cyanodienyl) cerium, 0.01-0.1 part of S-allethrin, 0.01-0.1 part of tetramethylguanidine lactate, 0.01-0.05 part Benzoyl peroxide, 0.05-0.1 part of polyvinyl alcohol, heating up, reacting at 60-80°C for 6-15 hours, filtering and drying the product to obtain the rare earth antibacterial agent.

[0056] A scrub-resistant shell powder coating that efficiently decomposes formaldehyde, comprising the following components:

[0057] by weight,

[0058] Shell Powder 100

[0059] Burnt Shell Powder 1

[0060] Nanoscale Titanium Dioxide 1

[0061] latex powder 22

[0062]Zinc oxide 0.1

[0063] Rare earth ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides scrubbing-resistant shell powder paint for efficiently decomposing formaldehydes. The scrubbing-resistant shell powder paint is characterized by being prepared from the following ingredients in parts by weight: 100 parts of shell powder, 0.1 to 1 part of fired shell powder 0.1 to 1 part of nanometer titanium dioxide, 13 to 22 parts of emulsion powder, 0.01 to 0.1 part of zinc oxide, 0.5 to 2 parts of rare earth antibacterial agents and 0.1 to 1 part of silica sol.

Description

technical field [0001] The invention relates to the fields of environmental protection and recycling of resources, in particular to a scrub-resistant shell powder coating that decomposes formaldehyde efficiently. technical background [0002] At present, the coating building materials represented by latex paint are mainly composed of fillers and adhesives. The base materials are mainly chemical products. During construction and use, the paint will release toxic and harmful gases to the human body, such as formaldehyde, TVOC, etc., which seriously endanger human health. [0003] The main component of shells is calcium compounds, including 95% calcium carbonate, and a small amount of trace elements, chitin and amino acids. The shell powder coating prepared with shell powder as the main raw material is green and environmentally friendly. Due to its porous structure and slightly alkaline characteristics, the shell powder coating has the functions of bactericidal and antibacteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/14C09D7/12
CPCC09D1/00C09D5/14
Inventor 梁友白玉桂彬梁伟东王丽冉党辉刘永占
Owner 中科海洋生物再生资源(天津)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com