A light-storing and luminescent polyvinyl chloride extrusion composition and preparation method thereof

A polyvinyl chloride, light-emitting technology, applied in the field of polymer material processing and application, can solve the problems of poor high temperature resistance of light-storing light-emitting powder, blackening of products, etc., and achieve the effects of alleviating adverse effects, bright light, and promoting dispersion effect.

Active Publication Date: 2020-11-17
CHINA PETROLEUM & CHEM CORP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, light-storing materials are mostly used in powder coatings and plastic spraying materials, and no reports on PVC extrusion compositions have been found. The main reason is that light-storing luminescent powders have poor high temperature resistance and high hardness. After strong friction on the metal wall of the machine, it is easy to make the product black

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Examples 1-5 are specific implementations of a light-storing and light-emitting polyvinyl chloride extrusion composition of the present invention. Wherein embodiment 1 is the best embodiment. The titanate coupling agent used in Examples 1-5 is the titanate coupling agent KR-36S produced by Kenrich Petrochemicals, Inc. (Kenrich Petrochemicals, Inc.), the main component of which is coordination-type tetraisopropyl Bis(dilauryl phosphite) titanate. The light-storage luminescent material used in Examples 1-5 is 100-300 mesh rare earth long-acting aluminate light-storage luminescent powder.

[0028] The proportioning of table 1 embodiment and comparative example (by weight)

[0029] .

[0030] The preparation method of embodiment 1~5 adopts following steps:

[0031] 1) Under normal temperature conditions, mix the titanate coupling agent by weight with the light-storing luminescent material for coupling treatment, then put it into the plasticizer to mix and infiltrate t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention provides a light-retaining and light-emitting type polyvinyl chloride extrusion composition and a preparation method thereof, belonging to the technical field of processing applications of polymeric materials. The light-retaining and light-emitting type polyvinyl chloride extrusion composition is composed of the following raw materials in parts by weight: 100 parts of polyvinyl chloride, 1.5 to 10 parts of a plasticizer, 1 to 7 parts of a stabilizer, 1 to 6 parts of an auxiliary stabilizer, 6 to 10 parts of an anti-impact modifier, 0.5 to 3.0 parts of a lubricant, 5 to 30 parts of a light-retaining type luminescent material and 0.03 to 0.9 part of a titanate coupling agent. The preparation method comprises the following steps: 1) mixing the titanate coupling agent with the light-retaining type luminescent material, then carrying out mixing with the plasticizer, carrying out impregnation, adding the lubricant, carrying out mixing, and carrying out three-roller grinding so as to obtain a light-retaining and light-emitting premix; and 2) mixing polyvinyl chloride, the stabilizer, the auxiliary stabilizer and the anti-impact modifier under stirring at 90 to 110 DEG C, adding the light-retaining and light-emitting premix, carrying out heating to 110 DEG C, carrying out stirring at a low speed, carrying out cooling to 40 DEG C or below, and carrying out discharging. The light-retaining and light-emitting type polyvinyl chloride extrusion composition has the advantages of long light-emitting time, bright lighting, insusceptibility to blackening, good flexibility, and capability of being wrapped at the exterior of curved surface.

Description

technical field [0001] The invention belongs to the technical field of polymer material processing and application, and in particular relates to a light-storing and light-emitting polyvinyl chloride extrusion composition and a preparation method thereof. Background technique [0002] Light-storing materials refer to materials that store energy in materials after being irradiated by sunlight or light, and release energy in the form of light at night or in dark places. They are mainly used for safety signs, billboards, handicrafts, traffic instructions, guardrails and fences, etc. use. Most of the light-storage materials are light-storage and light-emitting paint products. Due to the characteristics of light-storage materials, there are few light-storage products used for extrusion molding. [0003] The patent publication number is CN101817961A, which discloses a technology for preparing articles with the effect of releasing negative ions by using PVC paste resin, Anion serie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/12C08K3/34C08K5/524C08K5/58
CPCC08L27/06C08L2205/03C08L91/06C08K13/02C08K5/12C08K3/34C08K5/524C08K5/58
Inventor 桂俊杰李静刘浩刘容德张桦王秀丽孙丽朋孙培培
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products