A kind of inorganic fireproof and thermal insulation rock mud and using method thereof

A technology of fire prevention and thermal insulation and rock mud, which is applied in the fields of fireproof materials, sound insulation, and internal and external thermal insulation of wall building structures. It can solve the problems of non-circulation of cold and hot water, easy pulverization and cracking, poor weather resistance, etc. Scientific and reasonable, good thermal insulation performance, scientific and reasonable preparation effect

Active Publication Date: 2019-04-23
JILIN LONGYANG BUILDING MATERIALS CO LTD +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical disadvantages of the organic insulation board material building structure system are: at the junction of the organic insulation board material and the wall structure, the cold and hot water does not circulate to produce condensation, resulting in freeze-thaw damage, cracking and falling off of the material structure, especially when some organic insulation board materials are used. Combustible insulation materials, if a fire occurs, toxic and harmful gases will be produced, which will easily cause heavy casualties and property losses
[0005] There are also 5% to 10% inorganic fireproof and thermal insulation mortar construction system materials; such as: a modified expanded perlite thermal insulation mortar and a kind of inorganic vitrified microbead external wall thermal insulation mortar as representatives: poor thermal insulation performance and its thermal conductivity Generally W / (m.K)=0.06, the use of a single ingredient for inorganic fibers is unreasonable and the amount of organic colloidal materials is too large, which makes the material poor weather resistance, easy to pulverize, crack, fall off, and out of sync with the life of the building structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic fireproof and thermal insulation rock mud and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0038] Inorganic fireproof and thermal insulation rock mud: A (fiber powder synthetic and gelled) material: B1 aggregate (expanded perlite) = 1:1.3-1.5 ratio and mix evenly.

[0039] A component fiber gelling powder material weight percentage includes:

[0040] Portland cement 97.55% ~ 92.1%; fly ash 0.5--1%; silica fume 1--2%; mineral fiber (CaSiO 3 )2~3%; polypropylene fiber 0.05~0.2%; wood fiber 0.05~0.1%; fiber sepiolite 0.05~0.1%; ultrafine inorganic fiber 0.1~0.4%; hydroxypropyl methylcellulose (HPMC) 0.1~0.3%; base inhibitor 0.3~0.5%; redispersible latex powder 0.2%; water repellent: 0.1%

[0041] B1 aggregate expanded perlite vibration weight 90㎏~120㎏ / m 3 ;

[0042] More preferably, mineral fibers (CaSiO 3 ); aspect ratio (aspect ratio) 20:1, melting point 1540°C, hardness (Mohs) 4.5-4.7, capacity 560kg / m 3 .

[0043] More preferably, polypropylene fiber; the fiber length is 3mm.

[0044] Preferably, wood fiber (Methyl Cellulose); natural flocculent fibrous subs...

Embodiment approach 2

[0056] Inorganic fireproof and thermal insulation rock mud: A (fiber powder synthetic and gelled) material: B2 aggregate (closed-cell perlite) = 1:1.5-2 ratio and mix evenly.

[0057] A component fiber gelling powder material weight percentage includes:

[0058] Portland cement 97.55% ~ 92.1%; fly ash 0.5--1%; silica fume 1--2%; mineral fiber (CaSiO 3 )2~3%; polypropylene fiber 0.05~0.2%; wood fiber 0.05~0.1%; fiber sepiolite 0.05~0.1%; ultrafine inorganic fiber 0.1~0.4%; hydroxypropyl methylcellulose (HPMC) 0.1~0.3%; base inhibitor 0.3~0.5%; redispersible latex powder 0.2%; water repellent: 0.1%

[0059] B2 aggregate closed-cell perlite vibration weight 95㎏~140㎏ / m 3 .

[0060] More preferably, mineral fibers (CaSiO 3 ); aspect ratio (aspect ratio) 20:1, melting point 1540°C, hardness (Mohs) 4.5-4.7, capacity 560kg / m 3 .

[0061] More preferably, polypropylene fiber; the fiber length is 3mm.

[0062] Preferably, wood fiber (Methyl Cellulose); natural flocculent fibrous ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
lengthaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the fields of heat insulation, sound insulation and a fireproof material for internal and external parts of wall building construction, and relates to an inorganic fireproof insulation rock mud and an application method thereof. The inorganic fireproof insulation rock mud comprises the following components by weight ratio: a component A fiber gelling powder material comprising 97.55-92.1% of Portland cement, 0.5-1% of fly ash, 1-2% of silicon ash, 2-3% of mineral fiber, 0.05-0.2% of polypropylene fiber, 0.05-0.1% of wood fiber, 0.05-0.1% of fiber meerschaum, 0.1-0.4% of ultrafine inorganic fiber, 0.1-0.3% of hydroxypropyl methyl cellulose, 0.3-0.5% of an alkali resistance agent, 0.2% of re-dispersible latex powder, and 0.1% of a water repellent; and a lightweight aggregate B comprising B1 aggregate expanded perlite with vibration compaction weight being 90-120 kg / <3>, or B2 aggregate closed cell perlite with vibration compaction weight being 95-140 kg / <3>. The application method is characterized by smearing and machinery spray processes. According to the invention, a plurality of materials can be used for preparation in a scientific and reasonable mode, after moulding, the rock mud has a fiber disordered and netted multidimensional stereo tensioning structure, the fireproof grade of the material is high, the heat conduction coefficient is low, the heat insulation performance is good, and the weatherability is strong.

Description

technical field [0001] The invention belongs to the field of thermal insulation, sound insulation, and fireproof materials for wall building structures, in particular to an inorganic fireproof and thermal insulation rock mud composite wall construction material, in particular to an inorganic fireproof and thermal insulation rock mud and its use method . Background technique [0002] In recent years, my country's high-rise buildings have developed rapidly, and the number ranks first in the world. These high-rise buildings are high in height, large in size, and have complex functions and structural insulation systems. The fire safety of the building, stable economy, heat preservation and environmental protection. [0003] At present, my country's construction market is divided into organic and inorganic according to categories; organic such as: EPS polystyrene board, polyurethane, XPS extruded board, phenolic board and other thermal insulation material building construction sy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/20C04B2111/28C04B2111/76C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B18/146C04B14/38C04B16/0633C04B18/26C04B14/46C04B24/26C04B24/383C04B2103/603C04B2103/0068C04B14/185
Inventor 李元魁李华荣
Owner JILIN LONGYANG BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products