Plasticizer composition, resin composition and preparation method thereof

一种组合物、增塑剂的技术，应用在有机化学等方向，能够解决耐光性和迁移性差、增塑剂吸收速率低、增塑效率低等问题，达到优异性能、拉伸强度优异、优异吸收速率的效果

Active Publication Date: 2019-07-05
LG CHEM LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] For example, in a plasticizer composition suitable for PVC, when cheap diethylhexyl terephthalate is used, the plasticizing efficiency is low, the absorption rate of the plasticizer is relatively low, and the light resistance and migration also bad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plasticizer composition, resin composition and preparation method thereof
  • Plasticizer composition, resin composition and preparation method thereof
  • Plasticizer composition, resin composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0040] Preparation Example 1: Preparation of bis(2-ethylhexyl) isophthalate (DEHIP)

[0041] 498.0 g of purified isophthalic acid (IPA), 1170 g of 2-ethylhexanol (2-EH) (molar ratio of IPA:2-EH=1.0:3.0) and 1.54 g (relative to 100 parts by weight of IPA 0.31 parts by weight) titanium-based catalyst (tetraisopropyl titanate (TIPT)) was added to a 3L four-neck reactor equipped with a cooler, condenser, decanter, reflux pump, temperature controller, stirrer, etc. , and slowly raise the temperature of the reactor to about 170 °C. Produced water starts to be produced at about 170°C, and the esterification reaction is carried out at a reaction temperature of about 220°C under atmospheric pressure for about 4.5 hours while continuously introducing nitrogen, and the reaction is terminated when the acid value reaches 0.01.

[0042] After the reaction is completed, vacuum distillation extraction is performed for 0.5 to 4 hours to remove unreacted raw materials. In order to remove unre...

preparation Embodiment 2

[0043] Preparation Example 2: Preparation of Epoxidized Fatty Acid Butyl Ester (eFABE)

[0044] Using 500 g of epoxidized soybean oil and 490 g of butanol as reaction raw materials, transesterification was carried out to finally obtain 510 g of epoxidized butyl soybean oil (yield: 95%).

preparation Embodiment 3

[0045] Preparation Example 3: Preparation of epoxidized fatty acid 2-ethylhexyl ester (eFAEHE)

[0046] 584 g of epoxidized 2-ethylhexyl soybean oleate (yield: 95%) was obtained in the same manner as in Preparation Example 2 except that 490 g of 2-ethylhexanol was used instead of 490 g of butanol.

[0047] Examples and Comparative Examples listed in Tables 1-3 below were prepared using the materials prepared in Preparation Examples 1 to 3.

[0048] [Table 1]

[0049] Isophthalate-based materials eFAAE material Mixing weight ratio Example 1-1 DEHIP eFABE 7:3 Example 1-2 DEHIP eFABE 5:5 Example 1-3 DEHIP eFABE 3:7 Example 1-4 DEHIP eFAEHE+eFABE(5:5) 7:3 Example 1-5 DEHIP wxya 7:3 Examples 1-6 DEHIP wxya 5:5 Example 1-7 DEHIP wxya 3:7

[0050] [Table 2]

[0051]

[0052]

[0053] [table 3]

[0054] first component second component Mixing weight ratio Comparative e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a plasticizer composition, a method for preparing the plasticizer composition, and a resin composition comprising the plasticizer composition, the plasticizer composition comprising: isophthalate-based material; and an epoxy-based alkyl ester compound represented by the following Chemical Formula 1, wherein the weight ratio of the isophthalate-based material to the epoxy-based alkyl ester compound is 99:1 to 1:99, and the epoxy-based alkyl ester compound is a single compound or a mixture of two or more compounds. (In chemical formula 1, R 1 is an alkyl group having 8 to 20 carbon atoms or an alkyl group containing at least one epoxy group, and R 2 is an alkyl group having 4 or 8 carbon atoms. ) The present invention can provide a plasticizer capable of improving plasticization when used as a resin composition by improving poor physical properties caused by structural constraints and a resin composition comprising the plasticizer. Physical properties such as tensile strength, migration resistance, and heat loss are required in the formulation. [chemical formula 1]

Description

technical field [0001] Cross References to Related Applications [0002] This application claims the priority and benefit of Korean Patent Application No. 10-2015-0105324 filed on July 24, 2015 and Korean Patent Application No. 10-2016-0092874 filed on July 21, 2016, which The disclosure is incorporated herein by reference in its entirety. [0003] technical field [0004] The invention relates to a plasticizer composition, a resin composition and a method for preparing the plasticizer composition. Background technique [0005] Typically, plasticizers form esters through the reaction of alcohols and polycarboxylic acids such as phthalic acid or adipic acid. In addition, considering domestic and international regulations on phthalate-based plasticizers that are harmful to humans, plasticizer compositions that can replace phthalate-based plasticizers, such as based on Terephthalate-based plasticizers, adipate-based plasticizers and other polymer-based plasticizers. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/00C08K5/12C08K5/1515C08L23/08C08L23/06C08L23/12C08L27/06C08L25/06C08L75/04C08L73/00
CPCC08K5/0016C08K5/12C08K5/1515C08L23/06C08L23/0853C08L23/12C08L25/06C08L27/06C08L73/00C08L75/04C07D303/16C08L101/00C08L2203/202C08L2203/16C08K5/101C08L101/025C08L101/06
Inventor 金显圭李美然文正周金宙镐郑锡琥
Owner LG CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com