Resin concrete-based mechanical part and preparation method thereof

A technology for resin concrete and mechanical parts, applied in the field of machine tool parts, can solve the problems of prolonged production cycle, complicated equipment installation and debugging, large thermal expansion coefficient of metal materials, etc., to improve impact toughness and split resistance, and easy installation and debugging process. Easy to do, effect of high heat distortion temperature

Active Publication Date: 2017-11-28
常州高鼎新材料科技有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many deficiencies in the method of processing equipment or accessories with metal materials: 1. The shock absorption capacity of metal materials is weak, so it cannot effectively absorb the vibration generated by the equipment during operation; 2. The coefficient of thermal expansion of metal materials is relatively large , the installation and debugging process of the equipment is very complicated, and the processing accuracy of related accessories is also greatly limited; 3. The corrosion resistance of metal materials is poor (especially chemical equipment), which requires frequent anti-corrosion treatment and high maintenance costs; 4. The processing technology is complicated, which makes the production cost higher; 5. There are problems such as large energy consumption and serious pollution in the processing process
Although the comprehensive strength of machine tools and equipment bases made of resin concrete in 200610044905.4 is better than that of artificial granite and marble mechanical parts in 200510043683.X, the coefficient of thermal expansion of the former is far greater than that of the latter, which fails to solve the complex installation and debugging of equipment , The problem of limited processing accuracy of accessories
Moreover, the addition of reinforcing materials not only increases the process steps, but also prolongs the production cycle
In addition, the existing epoxy resin concrete is easy to degrade and break the chain after being exposed to sunlight, so most of them have problems such as easy discoloration and powdering, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin concrete-based mechanical part and preparation method thereof
  • Resin concrete-based mechanical part and preparation method thereof
  • Resin concrete-based mechanical part and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] The preparation method of the above-mentioned resin concrete-based mechanical parts includes the following steps:

[0056] S1. Weigh seven kinds of granite or marble particles according to the proportion by weight, mix them evenly and dry the moisture, and use them as aggregate for later use;

[0057] S2. Weigh fly ash, quartz powder, talc powder, granite powder or marble powder according to the proportion of parts by weight, and use them as fillers for later use;

[0058] S3. Weigh bisphenol S type epoxy resin, hydrogenated bisphenol A type epoxy resin and alicyclic epoxy resin according to the proportion of parts by weight, stir evenly at room temperature, and use it as the epoxy resin component for later use;

[0059] S4. Weigh the aliphatic polyamine curing agent, tertiary amine curing agent and imidazole curing agent according to the proportion by weight, stir evenly at room temperature, and use it as the curing agent component for later use;

[0060] S5. Mix the epoxy resin...

Embodiment 1

[0065] Example 1: Preparation of mechanical parts based on resin concrete.

[0066] Prepare materials according to the following table:

[0067]

[0068] Preparation:

[0069] S1. Put seven kinds of granite particles with different sizes in seven hoppers 1, and weigh them by the precision electronic scale in hopper 1 according to the dosage in the above table. After weighing, the seven kinds of particles will fall into The mixing conveyor belt 11 is transported to the mixing box 2 for mixing. The uniformly stirred mixture is transported to the drying box 3 for drying, and the dried mixture is transported to the aggregate storage box. 4, as an aggregate spare;

[0070] S2. Weigh fly ash according to the amount in the above table and use it as a filler for later use;

[0071] S3. Weigh bisphenol S type epoxy resin, hydrogenated bisphenol A type epoxy resin and bis(2,3-epoxycyclopentyl) ether according to the amount in the above table, and stir it evenly at room temperature as epoxy resi...

Embodiment 2

[0076] Example 2: Preparation of mechanical parts based on resin concrete.

[0077] Prepare materials according to the following table:

[0078]

[0079] Preparation:

[0080] S1. Put seven kinds of granite particles with different sizes in seven hoppers 1, and weigh them by the precision electronic scale in hopper 1 according to the dosage in the above table. After weighing, the seven kinds of particles will fall into The mixing conveyor belt 11 is transported to the mixing box 2 for mixing. The uniformly stirred mixture is transported to the drying box 3 for drying, and the dried mixture is transported to the aggregate storage box. 4, as an aggregate spare;

[0081] S2. Weigh talcum powder according to the amount in the above table, as a filler for later use;

[0082] S3. Weigh bisphenol S type epoxy resin, hydrogenated bisphenol A type epoxy resin and 2,3-epoxycyclopentylcyclopentyl ether according to the amount in the above table, and stir it evenly at room temperature as epoxy re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a resin concrete-based mechanical part and a preparation method thereof. The mechanical part is prepared from the following raw materials: aggregate, filler, an epoxy resin component and a curing agent component, wherein the aggregate is prepared from the following granite or marble particles in parts by weight: 10-15 parts of 19-20mm particles, 25-30 parts of 16-17mm particles, 15-20 parts of 13-14mm particles, 10-15 parts of 10-11mm particles, 5-10 parts of 7-8mm particles, 5-10 parts of 4-5mm particles and 10-15 parts of 1-2mm particles; the filler is prepared from powder such as 15-25 parts by weight of pulverized fuel ash; the epoxy resin component is prepared from 3-4 parts by weight of bisphenol S type epoxy resin, 4-6 parts by weight of hydrogenated bisphenol A type epoxy resin and 1-2 parts by weight of cycloaliphatic epoxy resin; the curing agent component is prepared from 1.0-1.5 parts by weight of an aliphatic polyamine curing agent, 0.3-0.5 part by weight of a tertiary amine curing agent and 0.7-1.0 part by weight of an imidazole curing agent.

Description

Technical field [0001] The invention belongs to the technical field of machine tool accessories, and relates to a resin concrete-based mechanical accessory and a preparation method thereof. Background technique [0002] At present, most of the existing processing equipment and testing equipment are made of metal materials. However, the method of processing equipment or accessories with metal materials has many shortcomings: 1. The shock absorption capacity of metal materials is weak, so it cannot effectively absorb the vibration generated by the equipment during operation; 2. The thermal expansion coefficient of metal materials is large , The installation and debugging process of the equipment is very complicated, and the processing accuracy of related accessories is also greatly restricted; 3. The corrosion resistance of metal materials (especially chemical equipment) is poor, and it needs frequent anti-corrosion treatment and high maintenance cost; 4. The processing technology...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/14C04B24/12
CPCC04B24/121C04B24/128C04B26/14C04B2201/20C04B2201/30C04B2201/50C04B14/048C04B18/08C04B24/023C04B14/042C04B14/06
Inventor 邵如意
Owner 常州高鼎新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com