A kind of waterproof erosion plugging agent and its preparation method and application
A technology of plugging agent and waterproof flushing, which is applied in the field of oil drilling, which can solve the problems of strong cohesive force of lost formation, erosion of plugging agent, high bearing strength, etc., and achieve effective sealing of lost channels, high bearing strength, The effect of simple ingredients
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] The waterproof erosion plugging agent of the present embodiment comprises the following components in parts by weight:
[0033] Solid water glass powder: 35 parts by weight
[0034] Acrylate: 8 parts by weight
[0035] Grade G cement: 30 parts by weight
[0036] Sodium hydroxide: 0.5 parts by weight
[0037] Cement early strength agent: 0.2 parts by weight.
[0038] The waterproof erosion plugging agent of the present embodiment is prepared as follows:
[0039] 1) In parts by weight, 35 parts by weight of solid water glass powder is added to 140 parts by weight of water at 80° C., fully stirred and hydrated under a pressure of 5 MPa to prepare the first aqueous solution;
[0040] 2) Mix 30 parts by weight of grade G cement, 0.5 parts by weight of sodium hydroxide, and 0.2 parts by weight of cement reinforcing agent to obtain the second part of the mixture.
[0041] 3) Add 8 parts by weight of acrylate to 20 parts by weight of water at room temperature and normal pr...
Embodiment 2
[0044] The waterproof erosion plugging agent of the present embodiment comprises the following components:
[0045] Solid water glass powder: 35 parts by weight
[0046] Acrylate: 10 parts by weight
[0047] Grade G cement: 30 parts by weight
[0048] Sodium hydroxide: 0.5 parts by weight
[0049] Cement early strength agent: 0.2 parts by weight.
[0050] The waterproof erosion plugging agent of the present embodiment is prepared as follows:
[0051] 1) Add 35 parts by weight of solid water glass powder to 140 parts by weight of water at 80° C., fully stir and hydrate under a pressure of 5 MPa to prepare the first aqueous solution;
[0052]2) Mix 30 parts by weight of grade G cement, 0.5 parts by weight of sodium hydroxide, and 0.2 parts by weight of cement reinforcing agent to obtain the second part of the mixture.
[0053] 3) Add 10 parts by weight of acrylate to 25 parts by weight of water at room temperature and normal pressure, fully stir, and thoroughly emulsify to ...
Embodiment 3
[0056] The waterproof erosion plugging agent of the present embodiment comprises the following components:
[0057] Solid water glass powder: 38 parts by weight
[0058] Acrylate: 10 parts by weight
[0059] Grade G cement: 50 parts by weight
[0060] Sodium hydroxide: 0.7 parts by weight
[0061] Cement early strength agent: 0.4 parts by weight.
[0062] The waterproof erosion plugging agent of the present embodiment is prepared as follows:
[0063] 1) Add 38 parts by weight of solid water glass powder to 152 parts by weight of water at 100° C., fully stir and hydrate under a pressure of 6 MPa to prepare the first aqueous solution;
[0064] 2) Mix 50 parts by weight of grade G cement, 0.7 parts by weight of sodium hydroxide, and 0.4 parts by weight of cement reinforcing agent to obtain the second part of the mixture.
[0065] 3) Add 10 parts by weight of acrylate to 25 parts by weight of water at room temperature and pressure, fully stir and thoroughly emulsify to make t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com