A kind of anti-aging and anti-hardening two-component water-based spray glue and its preparation method

A two-component, anti-aging technology, applied in adhesives, acidic copolymer adhesives, polymer adhesive additives, etc., can solve the problems of poor oil resistance of spray glue, edge hardening of joints, easy hardening of the glue layer, etc.

Active Publication Date: 2018-04-24
GUANGDONG TAIQIANG TECH IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing two-component spray glue urgently needs to solve the following problems: After the traditional two-component spray glue is connected and cured, the glue layer is easy to harden, especially the hardening at the edge of the joint is particularly serious; in addition, for oily leather and imitation leather materials , the traditional spray glue has poor oil resistance, especially the initial adhesion and final adhesion are not ideal, which directly affects the firmness and stability of the radian bonding between leather and sponge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-aging and anti-hardening two-component water-based spray glue and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A two-component water-based spray glue resistant to aging and hardening, including component A and component B, wherein:

[0024] Component A includes the following components in parts by weight: 39 parts of water-based neoprene latex, 40 parts of acrylic emulsion, 7 parts of water-based terpene tackifying resin, and 10 parts of sodium dodecylbenzenesulfonate;

[0025] Component B is composed of the following components in parts by weight: 5 parts of rosin resin, 5 parts of isocyanate, 1 part of fumed silica, and 40 parts of deionized water.

[0026] The preparation method is as follows: step 1: preparation of component A: stir the raw materials in component A according to the proportion; step 2: preparation of component B: stir the raw materials in component B according to the proportion; step 3: stir Under certain conditions, slowly add component B to component A.

Embodiment 2

[0028] A two-component water-based spray glue resistant to aging and hardening, including component A and component B, wherein:

[0029] Component A includes the following components in parts by weight: 41 parts of water-based neoprene latex, 30 parts of acrylic emulsion, 9 parts of water-based terpene tackifying resin, and 2 parts of sodium dodecylbenzenesulfonate;

[0030] Component B is composed of the following components in parts by weight: 10 parts of rosin resin, 1 part of isocyanate, 3 parts of fumed silica, and 30 parts of deionized water.

[0031] The preparation method is the same as in Example 1.

Embodiment 3

[0033] A two-component water-based spray glue resistant to aging and hardening, including A component and B component, wherein: A component includes the following components by weight: 40 parts of water-based neoprene latex, 35 parts of acrylic emulsion, water-based terpene 8 parts of vinyl tackifying resin, 6 parts of sodium dodecylbenzenesulfonate;

[0034] Component B is composed of the following components in parts by weight: 7 parts of rosin resin, 3 parts of isocyanate, 2 parts of fumed silica, and 35 parts of deionized water.

[0035] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the fields of adhesives and particularly relates to an ageing resistant and hardening resistant double-component waterborne adhesive spray. The ageing resistant and hardening resistant double-component waterborne adhesive spray comprises a component A and a component B, wherein the component A comprises the following components by weight: 39-41 parts of a waterborne chloroprene rubber emulsion, 30-40 parts of an acrylic emulsion, 7-9 parts of waterborne terpene tackifying resin, and 2-10 parts of sodium dodecylbenzene sulfonate; the component B comprises the following components by weight: 5-10 parts of rosin resin, 1-5 parts of isocyanate, 1-3 parts of gel amorphous silica, and 30-40 parts of deionized water. The adhesive spray has an excellent ageing resistance property, and has quite excellent effects of bonding strength, speed and stability on leather and sponges.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to an anti-aging and anti-hardening two-component water-based spray glue and a preparation method thereof. Background technique [0002] Two-component spray glue is mainly used for bonding between sponge, wood, leather, cloth, foam and other materials, especially for the curved bonding of sponge and leather, sponge and wood board. The existing two-component spray glue urgently needs to solve the following problems: After the traditional two-component spray glue is connected and cured, the glue layer is easy to harden, especially the hardening at the edge of the joint is particularly serious; in addition, for oily leather and imitation leather materials , The traditional spray glue has poor oil resistance, especially the initial adhesion and final adhesion are not ideal, which directly affects the firmness and stability of the arc bonding between leather and sponge. Contents of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/02C09J111/00C09J11/08C09J11/06C09J11/04C08G18/48C08G18/50
CPCC08G18/482C08G18/5024C08L2201/08C08L2205/035C09J11/04C09J11/06C09J11/08C09J111/00C09J133/02C08L11/00C08L93/04C08K5/42C08K3/36C08L33/02C08K3/34C08L75/08
Inventor 李满林
Owner GUANGDONG TAIQIANG TECH IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com