A technology of concrete and lithium slag pump, applied in the field of concrete preparation, can solve the problems of difficult hydration, slow C-S-H gel speed, etc., and achieves the effects of good workability, less loss of slump over time and good durability

Inactive Publication Date: 2017-09-22
SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It takes a certain process and time for this reaction to change from physical adsorption to chemical reaction. With the increase of hydration age, for the coagulation without lithium slag, the hydration product layer deposited on the surface of cement particles becomes thicker. , its hydration becomes more and more difficult, and the speed of forming C-S-H gel in its hydration product becomes slower and slower

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance lithium slag pump concrete
  • High-performance lithium slag pump concrete
  • High-performance lithium slag pump concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A high-performance lithium slag pumping concrete, the concrete is based on the component unit kg / m 3 The mixing ratio is: cement: water: mineral powder: fly ash: lithium slag: sand: gravel: synergist: admixture = [340~520]: [165~200]: [0~50]: [ 0~50]: [40~150]: [700~850]: [1000~1100]: [2~3.5]: [7~12]. . The performance parameters of the resulting concrete are:

Embodiment 2

[0043] A high-performance lithium slag pumping concrete, the concrete is based on the component unit kg / m 3 The mixing ratio is: cement: water: fly ash: lithium slag: sand: gravel: synergist: admixture = [340~500]: [170~200]: [0~50]: [40~100 ]: [720~830]: [1050~1100]: [2~3]: [9.8]. The performance parameters of the resulting concrete are:

Embodiment 3

[0045] A high-performance lithium slag pumping concrete, the proportion of the concrete raw materials by weight is: 270 parts of cement, 170 parts of water, 36 parts of fly ash, 56 parts of lithium slag powder, 820 parts of sand, 1061 parts of gravel, Synergist 2.16 parts, polycarboxylate additive 7.56 parts. C40 grade high-performance lithium slag pumped concrete with slump / expansion of 220mm / 510mm, 28d compressive strength of 49.7MPa and 60d compressive strength of 57.0MPa can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-performance lithium slag pump concrete. The proportion of mixture of the concrete is cement:water:mineral powder:fly ash:lithium slag:sand:gravel:synergist: additive being (340-520):(165-200):(0-50):(0-50):(40-150):(700-850):(1,000-1,100):(2-3.5):(7-12) according to the component unit of kg / m<3>. By means of selection of the raw materials and design of proportioning, the high-performance lithium slag concrete which is good in working performance, mechanical performance and durability and can be used for pumping is obtained.

Description

technical field [0001] The invention relates to the technical field of concrete preparation, in particular to a high-performance lithium slag pumping concrete. Background technique [0002] Usually contains SiO 2 , Al 2 o 3 All industrial waste residues are potentially active, and through appropriate technical means, the inherent deficiencies of waste residues can be made up for. At present, at home and abroad, alkali components are used to activate various slag bodies through chemical and physical methods to prepare clinker-free and clinker-less cementitious materials, eliminating the need for calcination and multiple grinding processes. At the same time, it also promotes the sustainable development of cement and concrete not only to obtain good economic and social benefits, but also to achieve good environmental benefits, and is expected to develop concrete materials into new environmental materials that are coordinated with the environment. [0003] With the developm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/34
CPCC04B28/04C04B2111/00017C04B2111/00146C04B2111/343C04B2201/50C04B18/141C04B18/08C04B18/0427C04B14/06C04B14/02C04B2103/302C04B2103/0068
Inventor 刘登贤吴鑫向鹏麻鹏飞江晓君关素敏杨奉源
Owner SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products