Environment-friendly flame-retardant rubber floor and manufacturing method thereof

A flame retardant rubber and floor technology, applied in the field of building decoration materials, can solve the problems of weak flame retardant performance, difficult to clean, serious color difference, etc., and achieve good flame retardant performance, avoid dust accumulation, and improve the effect of strong adhesion

Inactive Publication Date: 2017-08-25
合肥市老海新材料有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rubber floor materials have seams in the pavement, serious color difference, difficult to clean, smelly, weak flame retardant and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of environment-friendly flame-retardant rubber floor of the present embodiment comprises the following raw materials in parts by weight:

[0034] 20 parts of styrene-butadiene rubber, 50 parts of nitrile rubber, 6 parts of titanium dioxide, 4 parts of vulcanizing agent, 1 part of zinc oxide, 0.5 parts of stearic acid, 4 parts of white carbon black, 0.8 parts of accelerator, 1 part of weather resistance agent, three 3 parts of antimony oxide, 5 parts of flame retardant, 1 part of antistatic agent, 20 parts of reinforcing filler.

[0035] The vulcanizing agent in this embodiment includes a mixture of sulfur and bis-penta vulcanizing agent in a weight ratio of 2:1.

[0036] The accelerator in this embodiment is a mixture of sulfenic acid amine accelerator and dithiocarbamate accelerator.

[0037] The weather resistance agent in this embodiment is a mixture of ozone anti-aging agent MB, diaryl secondary amine anti-aging agent and p-phenylenediamine anti-aging agent ...

Embodiment 2

[0046] A kind of environment-friendly flame-retardant rubber floor of the present embodiment comprises the following raw materials in parts by weight:

[0047] 30 parts of styrene-butadiene rubber, 60 parts of nitrile rubber, 8 parts of titanium dioxide, 6 parts of vulcanizing agent, 3 parts of zinc oxide, 2 parts of stearic acid, 6 parts of white carbon black, 1.4 parts of accelerator, 2 parts of weather resistance agent, three 5 parts of antimony oxide, 7 parts of flame retardant, 3 parts of antistatic agent, 30 parts of reinforcing filler.

[0048] The vulcanizing agent in this embodiment includes a mixture of sulfur and bis-penta vulcanizing agent in a weight ratio of 2:1.

[0049] The accelerator in this embodiment is a mixture of sulfenic acid amine accelerator and dithiocarbamate accelerator.

[0050] The weather resistance agent in this embodiment is a mixture of ozone anti-aging agent MB, diaryl secondary amine anti-aging agent and p-phenylenediamine anti-aging agent...

Embodiment 3

[0059] A kind of environment-friendly flame-retardant rubber floor of the present embodiment comprises the following raw materials in parts by weight:

[0060] 25 parts of styrene-butadiene rubber, 55 parts of nitrile rubber, 7 parts of titanium dioxide, 5 parts of vulcanizing agent, 2 parts of zinc oxide, 1.3 parts of stearic acid, 5 parts of white carbon black, 1.1 parts of accelerator, 1.5 parts of weather resistance agent, three 4 parts of antimony oxide, 6 parts of flame retardant, 2 parts of antistatic agent, 25 parts of reinforcing filler.

[0061] The vulcanizing agent in this embodiment includes a mixture of sulfur and bis-penta vulcanizing agent in a weight ratio of 2:1.

[0062] The accelerator in this embodiment is a mixture of sulfenic acid amine accelerator and dithiocarbamate accelerator.

[0063] The weather resistance agent in this embodiment is a mixture of ozone anti-aging agent MB, diaryl secondary amine anti-aging agent and p-phenylenediamine anti-aging a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses environment-friendly flame-retardant rubber floor. The environment-friendly flame-retardant rubber floor is prepared from the following raw materials in parts by weight: 20-30 parts of butadiene styrene rubber, 50-60 parts of acrylonitrile-butadiene rubber, 6-8 parts of titanium dioxide, 4-6 parts of a vulcanizing agent, 1-3 parts of zinc oxide, 0.5-2 parts of stearic acid, 4-6 parts of white carbon black, 0.8-1.4 parts of an accelerant, 1-2 parts of a weather resistant, 3-5 parts of antimonous oxide, 5-7 parts of a flame retardant, 1-3 parts of an antistatic agent and 20-30 parts of reinforcing filler. The rubber floor disclosed by the invention has the advantages of stronger wear resistance, static electricity resistance, low smoke, low toxicity, low corrosion, good flame resistance, high tensile strength, good skid resistance, good resilience and the like. A manufacturing method for the rubber floor adopts safe and reliable raw material components, is harmless on environment, adopts easily available raw materials, is relatively low in cost, is simple in process, is easy to operate and realize industrial production, and has relatively high practical value and a good application prospect.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to an environmentally friendly flame-retardant rubber floor and a preparation method thereof. Background technique [0002] The market has a strong demand for floor decoration materials. Common ground decoration materials include wooden floors, floor tiles, [0003] Plastic flooring, rubber flooring, etc., among which wooden flooring and floor tiles are the most used, and are the main materials for residential buildings. However, for some special places, such as workshops of electronics factories, large-scale offices, some public places such as schools, airports, and transportation vehicles such as airplanes and trains, wooden floors and tiles are not suitable because people walk on wooden floors. It will make a loud noise when it is placed on or on tiles, and it is not slippery. In addition, in these places, such as workshops for producing and assembling el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L9/06C08L25/06C08K13/02C08K5/521C08K3/22C08K3/32C08K3/36C08K5/09C08K3/06C08K5/14E04F15/10E04F15/18B29B7/00B29C35/02B29C43/24B29L7/00
CPCB29B7/002B29C35/02B29C43/24B29L2007/002C08K2003/2224C08K2003/2296C08K2003/327C08L9/02C08L2201/02C08L2201/04C08L2205/02C08L2205/03C08L2205/035E04F15/10E04F15/181E04F2290/045C08L9/06C08L25/06C08K13/02C08K5/521C08K3/22C08K3/32C08K3/2279C08K3/36C08K5/09C08K3/06C08K5/14
Inventor 牛淑美
Owner 合肥市老海新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com