Preparation method of nylon composite material

A nylon composite material, nylon technology, applied in the nylon field, can solve the problems of poor thermal stability, impact resistance needs to be improved, etc., and achieve the effects of good compatibility, excellent aging resistance, and good thermal stability.

Inactive Publication Date: 2017-08-18
ANHUI CHUNHUI INSTR CABLE GROUP
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it also has some shortcomings, such as poor thermal stability and impact resistance need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nylon composite material
  • Preparation method of nylon composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The preparation method of a kind of nylon composite material that the present invention proposes, comprises the following steps: add nylon PA66, epoxy resin E-51, maleic anhydride polyolefin elastomer, polyvinyl alcohol into high-speed mixer, drop into dilauric acid Dibutyltin, chlorinated paraffin, mix, add succinic anhydride complex, coupling agent KH550 and continue to stir, add medium alkali glass fiber, magnesium hydroxide, aluminum hydroxide, ammonium polyphosphate, antioxidant, lubricant and continue to stir, then Add it into a twin-screw extruder, mix evenly, melt and extrude, and cool to obtain a nylon composite material.

Embodiment 2

[0016] The preparation method of a kind of nylon composite material that the present invention proposes comprises the following steps: comprising the following steps: adding nylon PA66, epoxy resin E-51, maleic anhydride polyolefin elastomer, polyvinyl alcohol into a high-speed mixer, dripping Add dibutyltin dilaurate, chlorinated paraffin, mix for 20 minutes, add succinic anhydride complex, coupling agent KH550 and continue stirring for 15 minutes, add medium alkali glass fiber, magnesium hydroxide, aluminum hydroxide, ammonium polyphosphate, antioxidant, Continue to stir the lubricant for 15 minutes, then add it to the twin-screw extruder and mix evenly, melt and extrude, the extrusion temperature is 265°C, the twin-screw aspect ratio is 47, the host speed is 485r / min, and the nylon composite material is obtained after cooling.

[0017] The succinic anhydride complex is prepared by the following process: mix succinic anhydride and acetone evenly, add 4-dimethylaminopyridine a...

Embodiment 3

[0019] A kind of preparation method of nylon composite material that the present invention proposes, comprises the steps: by weight 40 parts of nylon PA66, 40 parts of epoxy resin E-51, 15 parts of maleic anhydride polyolefin elastomers, 30 parts of polyvinyl alcohol Add a high-speed mixer, drop 1 part of dibutyltin dilaurate, 2 parts of chlorinated paraffin, mix for 15 minutes, add 2 parts of succinic anhydride complex, 1 part of coupling agent KH550 and continue stirring for 20 minutes, add 10 parts of medium-alkali glass fiber , 4 parts of magnesium hydroxide, 1 part of aluminum hydroxide, 3 parts of ammonium polyphosphate, 1 part of antioxidant, 2 parts of lubricant and continue to stir for 10 minutes, then add to the twin-screw extruder and mix evenly, melt extrude, extrude The temperature is 280°C, the aspect ratio of the twin-screw is 45, the rotation speed of the main engine is 500r / min, and the nylon composite material is obtained by cooling.

[0020] The succinic anh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a nylon composite material. The preparation method of the nylon composite material comprises the following steps: adding nylon PA66, epoxy resin E-51, maleic anhydride elastomer and polyvinyl alcohol in a high-speed mixing machine; and dropwise adding dibutyltin dilaurate and chlorinated paraffin, mixing, adding a succinic anhydride compound and a coupling agent KH550, continuing stirring, adding medium-alkali glass fibers, magnesium hydroxide, aluminium hydroxide, ammonium polyphosphate, oxidation inhibitor and a lubricant, continuing stirring, then adding the material in a double-screw extruder, mixing evenly, carrying out melt extrusion, and cooling to obtain the nylon composite material. By the preparation method of the nylon composite material, the obtained nylon composite material has strengthened rigidity and hardness, the heat resistance, the size stability and the ageing property are excellent, and the nylon composite material is suitable for blow molding, and can meet requirements of various structural components such as automobiles, instruments and apparatuses and electronic and electrical products to high performance.

Description

technical field [0001] The invention relates to the technical field of nylon, in particular to a preparation method of a nylon composite material. Background technique [0002] As the largest and most important variety of engineering plastics, nylon has strong vitality, mainly because it has excellent mechanical properties, high strength, high rigidity, wear resistance, and excellent chemical resistance, oil resistance, and alkali resistance. After modification, it can achieve high performance, so it is widely used in automobiles, electrical equipment, mechanical parts, transportation equipment, textiles, and papermaking machinery. But it also has some disadvantages, such as poor thermal stability and impact resistance needs to be improved. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a method for preparing a nylon composite material. The obtained nylon composite material has enhanced rigid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/06C08L63/00C08L51/06C08L29/04C08K13/06C08K9/02C08K9/04C08K7/14C08K5/544C08K5/1539C08K3/22C08K3/32B29C47/92B29C48/92
CPCC08L77/06B29C48/92B29C2948/9258B29C2948/92704C08K2003/2224C08K2003/2227C08K2003/323C08L63/00C08L2201/08C08L2205/035C08L51/06C08L29/04C08K13/06C08K9/02C08K9/04C08K7/14C08K5/544C08K5/1539C08K3/22C08K3/32C08K13/04
Inventor 沈必亮
Owner ANHUI CHUNHUI INSTR CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More