Pretreatment method for preparing Dendrocalamus latiflorus unbleached pulp
A technology of pretreatment and hemp bamboo, applied in washing/replacing pulp treatment liquid, non-woody plant/crop pulp, pulp dewatering, etc., to achieve the effect of high strength, simple process and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0032] In an embodiment, the preparation method of described hemp bamboo natural color pulp comprises the following steps:
[0033] S1: Cut Mazhu into pieces with a size of 24-28×3-3.6mm×1.4-2mm, and transport them to the primary pretreatment infusion A, the weight of the hemp bamboo is equal to the volume of the primary pretreatment infusion A The ratio is 1:2-4, and the primary pretreatment immersion liquid A includes the following raw materials in parts by weight: 4-8 parts of alkylphenol polyoxyethylene ether, 0.3-0.6 parts of triethanolamine, 0.5-0.5 parts of stearic acid 1 part, 0.4-1.2 parts of oleic acid, 0.8-1.5 parts of lauric acid, 42-90 parts of water, soak for 30-45 minutes at an ultrasonic power of 30-50W and a temperature of 43-48°C, and then filter to obtain the soaking material A;
[0034] S2: Transport the soaking material A prepared in step S1 to the secondary pretreatment immersion liquid B, the ratio of the weight of the immersion material A to the volume...
Embodiment 1
[0039] A preparation method of hemp bamboo natural color pulp, comprising the following steps:
[0040] S1: Cut the bamboo into pieces with a size of 26×3.4mm×1.8mm, and transport them to the primary pretreatment infusion A, the ratio of the weight of the hemp bamboo to the volume of the primary pretreatment infusion A is 1:2 , the primary pretreatment immersion solution A is in parts by weight, including the following raw materials: 4.1 parts of alkylphenol polyoxyethylene ether, 0.3 part of triethanolamine, 0.5 part of stearic acid, 0.4 part of oleic acid, 0.8 part of lauric acid, 42 parts of water, soaked for 45 minutes at an ultrasonic power of 30W and a temperature of 44°C, and then filtered to obtain the impregnated material A;
[0041] S2: Transport the steeping material A prepared in step S1 to the secondary pretreatment immersion liquid B, the ratio of the weight of the steeping material A to the volume of the secondary pretreatment immersion liquid B is 1:6, and the ...
Embodiment 2
[0046] A preparation method of hemp bamboo natural color pulp, comprising the following steps:
[0047]S1: Cut Mazhu into pieces with a size of 24×3mm×1.4mm, and transport them to the primary pretreatment infusion A, the ratio of the weight of the hemp bamboo to the volume of the primary pretreatment infusion A is 1:4, The primary pretreatment immersion solution A is in parts by weight and includes the following raw materials: 8 parts of alkylphenol polyoxyethylene ether, 0.6 part of triethanolamine, 1 part of stearic acid, 1.2 parts of oleic acid, 1.5 parts of lauric acid, water 90 parts were soaked for 32 minutes at an ultrasonic power of 50W and a temperature of 48°C, and then filtered to obtain the impregnated material A;
[0048] S2: Transport the soaking material A prepared in step S1 to the secondary pretreatment immersion liquid B, the ratio of the weight of the immersion material A to the volume of the secondary pretreatment immersion liquid B is 1:13, and the seconda...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com