High-voltage-resistant insulation material and preparation method thereof

An insulating material and high-voltage-resistant technology, applied in the field of high-voltage-resistant insulating materials and their preparation, can solve the problems of motor insulation aging failure, poor corona performance, and threaten the life insulation reliability of variable frequency motors, and achieve corona resistance and anti-corona performance. The effect of increased ablative power

Inactive Publication Date: 2017-07-25
HARBIN UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For motor insulation, polyimide film is currently the most important insulating material in variable frequency motors, but because of its poor corona performance as a polymer polymer, it is easily corroded by corona aging and causes aging failure of motor insulation, which is seriously Threatening the life of the inverter motor and the reliability of the insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-voltage-resistant insulation material and preparation method thereof
  • High-voltage-resistant insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0025] A high-voltage resistant insulating material, the high-voltage resistant insulating material is mainly composed of trimellitic anhydride, 5-norbornane-2,3-dicarboxylic acid monomethyl ester, N-methylpyrrolidone, xylene, N,N-dicarboxylate Methylacetamide, phenol, 4,4'-diphenylmethane diisocyanate, modified nanoparticles, modified nanofibers, including 15 parts by weight of trimellitic anhydride, 20 parts of 5-norbornane- 2,3-dicarboxylic acid monomethyl ester, 30 parts of N-methylpyrrolidone, 10 parts of xylene, 15 parts of N,N-dimethylacetamide, 5 parts of phenol, 40 parts of 4,4 '-Diphenylmethane diisocyanate, 1 part of modified nanoparticles, 1 part of modified fibers.

[0026] In the high-voltage insulating material described in this embodiment, the modified nanoparticles are modified nano-SiO 2 and modified nano-Al 2 o 3 A mixture in which the modified nano-SiO 2 and modified nano-Al 2 o 3 The mass ratio is 0.2:1, and the modifying liquid is KH902 silane coupl...

specific Embodiment approach 2

[0034] According to the high-voltage-resistant insulating material described in the first specific embodiment, it includes the following steps:

[0035] Step 1, the weighed nano-SiO 2 and nano Al 2 o 3 Place the modified liquid in the alcohol solution of KH902 silane coupling agent, mix and stir for 120 minutes, let it stand for 24 hours, filter the mixture obtained after suction, and dry it in vacuum to obtain modified nanoparticles, which are ready for use;

[0036] Step 2. Put the weighed glass fiber in the KH902 silane coupling agent alcohol solution as the modification liquid, mix and stir for 120 minutes, then let it stand for 24 hours, filter the mixture obtained after suction, dry it in a vacuum, and carry out surface mechanical grinding. Obtain modified fiber, stand-by;

[0037] Step 3. Add the weighed trimellitic anhydride, 5-norbornane-2,3-dicarboxylic acid monomethyl ester, and N-methylpyrrolidone into a three-necked beaker equipped with nitrogen protection, mec...

specific Embodiment approach 3

[0045] A high-voltage resistant insulating material, the high-voltage resistant insulating material is mainly composed of trimellitic anhydride, 5-norbornane-2,3-dicarboxylic acid monomethyl ester, N-methylpyrrolidone, xylene, N,N-dicarboxylate Methylacetamide, phenol, 4,4'-diphenylmethane diisocyanate, modified nanoparticles, modified nanofibers, including 30 parts by weight of trimellitic anhydride, 30 parts of 5-norbornane- 2,3-dicarboxylic acid monomethyl ester, 70 parts of N-methylpyrrolidone, 20 parts of xylene, 30 parts of N,N-dimethylacetamide, 10 parts of phenol, 100 parts of 4,4 '-Diphenylmethane diisocyanate, 5 parts of modified nanoparticles, 1 part of modified fiber.

[0046] In the high-voltage insulating material described in this embodiment, the modified nanoparticles are modified nano-SiO 2 and modified nano-Al 2 o 3 A mixture in which the modified nano-SiO 2 and modified nano-Al 2 o 3 The mass ratio is 1:10, and the modifying liquid is KH902 silane coup...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-voltage-resistant insulation material and a preparation method thereof, and belongs to the field of insulation material preparation. The high-voltage-resistant insulation material is mainly prepared from the following raw materials in parts by weight: 15 to 30 parts of trimellitic anhydride, 20 to 30 parts of 5-norbornene-2,3-dicarboxylic monomethylester, 30 to 70 parts of N-methyl pyrrolidone, 10 to 20 parts of xylene, 15 to 30 parts of N,N-dimethylacetamide, 5 to 10 parts of phenol, 20 to 100 parts of 4,4'-diphenylmethane diisocyanate, 0.5 to 10 parts of modified nanometer particles and 0.5 to 10 parts of modified fiber. The high-voltage-resistant insulation material has the advantages that the high-voltage-resistant performance is unchanged; the corona-resistant capability and the ablation-resistant capability are improved.

Description

technical field [0001] The invention belongs to the field of insulating material preparation, and in particular relates to a high-voltage resistant insulating material and a preparation method thereof. Background technique [0002] Polyimide is one of the organic polymer materials with the best comprehensive properties. It can withstand high temperatures above 400°C and has a long-term service temperature range of -200 to 300°C. It has no obvious melting point and high insulation performance. As a special engineering material, polyimide has been widely used in aviation, aerospace, microelectronics, nanometer, liquid crystal, separation membrane, laser and other fields. However, the traditional polyimide film monomers have low reactivity, and it is difficult to prepare high molecular weight polyimide resins, resulting in a significant decline in the overall performance of its film products and low mechanical properties, hindering further promotion of the product. [0003] In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/08C08K9/06C08K7/14C08K3/22C08K3/36C08J7/12C08J5/18C08G73/10
CPCC08J7/126C08G73/1003C08J5/18C08J2379/08C08K3/22C08K3/36C08K7/14C08K9/06C08K2003/2227C08K2201/003C08K2201/004C08K2201/011C08L2203/16C08L79/08C08L79/085
Inventor 曹铁男
Owner HARBIN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com