Pbat-based biodegradable composites with high water vapor barrier properties

A water vapor barrier and biodegradable technology, applied in the field of polymer materials, can solve the problems of unverified coating layer stability, affecting the service life of the barrier film, and easy deformation quality, so as to achieve easy large-scale application and popularization, and maintain biological Strong degradability and operability

Active Publication Date: 2019-03-22
SHANGHAI HONGRUI CHEM PROD CO LTD
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method uses polycarbonate polymer as the base material, and the glass transition temperature of polycarbonate is only 35°C. It is easy to deform and unstable in summer at high room temperature, and the stability of the coating layer has not been verified. , affecting the service life of the barrier film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pbat-based biodegradable composites with high water vapor barrier properties
  • Pbat-based biodegradable composites with high water vapor barrier properties
  • Pbat-based biodegradable composites with high water vapor barrier properties

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The present invention will be described in detail below in conjunction with specific embodiments. The following examples will help those skilled in the art to further understand the present invention, but do not limit the present invention in any form. It should be noted that those skilled in the art can make several modifications and improvements without departing from the concept of the present invention. These all belong to the protection scope of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a PBAT-based biodegradable composite material with high vapor barrier property. The composite material comprises the following components: PBAT, organic modification material, inorganic modification material, an initiator, a compatilizer and a catalyst. Compared with the prior art, the PBAT-based biodegradable composite material has the following beneficial effects: the compatibility and dispersity of the inorganic material in PBAT can be greatly improved by bridging PBAT with the inorganic material; the bridging action, generated due to combination of the compatilizer and the initiator, of the inorganic material is partially directionally distributed by layers in a blending system, the pass route of water molecules can be prolonged, and the motion time of the water molecules in the material can be prolonged, so that the water retention property of the material can be remarkably improved, the water vapor permeability of the composite material 10mum thin film material is reduced to 320g / m<2>.24h from 280g / m<2>.24h of the original-specification thin film, which is obviously superior to the similar materials.

Description

technical field [0001] The invention relates to a PBAT-based biodegradable composite material with high water vapor barrier properties, belonging to the technical field of polymer materials. Background technique [0002] After the use of traditional plastic packaging film products, it is not easy to recycle due to the variety of types, and most of them are incinerated after recycling, which increases greenhouse gases (such as CO 2 gas) and harmful substances (such as dioxins), so biodegradable materials and their packaging products have gradually become a hot spot in current research and development. [0003] PBAT is a copolymer of butylene adipate and butylene terephthalate. It has the characteristics of both PBA and PBT. It has good ductility and elongation at break, as well as good heat resistance. and impact performance. In addition, PBAT is also an excellent biodegradable material, so it is widely used in the production of film and sheet packaging products. However, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L67/04C08L69/00C08K13/02C08K3/34C08K5/1539
CPCC08K2201/011C08L67/02C08L2201/06C08L2205/02C08L2205/025C08L67/04C08K13/02C08K3/34C08K5/1539C08K3/346C08L69/00
Inventor 徐友利张伟阳李
Owner SHANGHAI HONGRUI CHEM PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com