A ceramic material and a processing method thereof

A ceramic material and processing method technology, applied in the field of electronic ceramics, can solve the problems of high cost, inconsistent inside and outside, high cobalt price, etc., and achieve the effects of good size consistency, good wear resistance, and good toughness

Inactive Publication Date: 2017-06-23
谢扬平
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, a large amount of cobalt dioxide is also added on this basis, so that the price of cobalt is quite expensive, and the cost is greatly increased. Although the color is better than the original, it is blue-black, and the inside and outside are still inconsistent.
There are also some companies that directly purchase the black color base and add α-alumina to make products after grinding and mixing. The blackness of the product has improved, but it is not pure black, and the inside and outside are still inconsistent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides a ceramic material, which has the following components in weight percentage:

[0029] α-alumina 77.5~95.0wt%,

[0030] Ferric oxide 2.5~7.5wt%,

[0031] Zinc dioxide 2.0~10.0wt%,

[0032] Zinc oxide 0.5~5.0wt%.

[0033] Among them, the chemical molecular formula of α-alumina is α-Al 2 o 3 , mainly using 95-Al 2 o 3 ; The chemical molecular formula of ferric oxide is Fe 2 o 3 ; The chemical formula of zinc dioxide is MnO 2 ; The chemical formula of zinc oxide is NiO 2 .

Embodiment 2

[0035] This embodiment provides a ceramic material, which has the following components in weight percentage:

[0036] α-alumina 86.5~92.5wt%,

[0037] Ferric oxide 3.5~5.5wt%,

[0038] Zinc dioxide 3.0~5.0wt%,

[0039] Zinc oxide 1.0~3.0wt%.

Embodiment 3

[0041] This embodiment provides a ceramic material, which has the following components in weight percentage:

[0042] α-alumina 92.5wt%,

[0043] Ferric oxide 3.5wt%,

[0044] Zinc dioxide 3.0wt%,

[0045] Zinc Oxide 1.0wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic material, which has the following components in weight percent: 77.5-95.0 wt% of α-alumina, 2.5-7.5 wt% of ferric oxide, and 2.0-10.0 wt% of zinc dioxide %, zinc oxide 0.5~5.0wt%. The invention also discloses a processing method of the ceramic material. By mixing ferric oxide, zinc dioxide, zinc oxide and α-alumina according to the designed ratio, the consistency of the inside and outside of the ceramic material is greatly improved, and it is pure black. And the product after sintering has low shrinkage and good consistency.

Description

technical field [0001] The invention relates to the technical field of electronic ceramics, in particular to a ceramic material and a processing method thereof. Background technique [0002] Ceramics that can use electricity and magnetic properties in the electronics industry are called electronic ceramics. Electronic ceramics are ceramics with new functions obtained through the control of surface, grain boundary and size structure. It can be widely used in energy, household appliances, automobiles, etc. [0003] At present, black electronic ceramic materials are usually mixed and finely ground by iron, manganese, chromium + α-alumina ball mills, then made into wax cakes, and then made into products. The appearance of its products is: coffee black, while the inside is iron red and black. In addition, a large amount of cobalt dioxide is also added on this basis, so that the price of cobalt is quite expensive, and the cost is greatly increased. Although the color is better ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/10
CPCC04B35/10C04B35/6261C04B2235/3272C04B2235/3284
Inventor 谢扬平
Owner 谢扬平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products