A kind of high-strength tarpaulin and its production method and application

A production method and high-strength technology, applied in chemical instruments and methods, layered products, coatings, etc., can solve problems such as poor flame retardancy, substandard warp and weft breaking tension and elongation, and large weight, and achieve the best flame retardancy Sex and anti-aging properties, beneficial to industrial applications, and beneficial to environmental protection

Active Publication Date: 2020-01-21
上海昶勤实业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of tarpaulin has disadvantages such as low strength, heavy weight, rough surface, narrow surface width, easy aging, short service life, poor flame retardancy, low softness, warp and weft breaking tension and elongation rate are not up to standard during use, making the tarpaulin The cloth is easily damaged during use, which reduces the service life and increases the cost of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength tarpaulin and its production method and application
  • A kind of high-strength tarpaulin and its production method and application
  • A kind of high-strength tarpaulin and its production method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0053] The preparation method of the above resin material comprises the following steps: uniformly mixing 80-88 parts of thermoplastic resin, 6-10 parts of antioxidant, 3-5 parts of anti-ultraviolet light stabilizer and 3-5 parts of flame retardant to obtain the resin material.

[0054] [core layer]

[0055] The thickness of the core layer 3 can be 0.36-0.90mm, preferably 0.5-0.6mm, and it can be made of fiber-reinforced thermoplastic resin prepreg, and the fiber-reinforced thermoplastic resin prepreg is made of more than two fiber-reinforced thermoplastic resin prepregs The belt is laid layer by layer according to the laying method of 0° and 90°.

[0056] The fiber-reinforced thermoplastic resin prepreg tape may include the following components and the parts by weight of each component may be as follows:

[0057] 45-50 parts of continuous fiber;

[0058] 50-55 parts of thermoplastic resin.

[0059] Wherein, the continuous fiber can be selected from any one or more of inorg...

Embodiment 1

[0082] Embodiment one (polypropylene tarpaulin)

[0083] This embodiment provides a polypropylene tarpaulin, which includes a surface layer, a core layer and a bottom layer arranged sequentially from top to bottom.

[0084] Wherein, both the surface layer and the bottom layer are made of resin-coated non-woven fabric on one side, and the thickness thereof is 0.2 mm. The grammage of the resin-coated non-woven fabric on one side is 180g / m 2 .

[0085] Both the surface layer and the bottom layer include a resin sublayer and a nonwoven fabric sublayer, and the weight ratio of the resin sublayer to the nonwoven fabric sublayer is 2:1.

[0086] The resin sublayer is made of a resin material, and the resin material includes the following components and the parts by weight of each component are as follows:

[0087]

[0088] Among them, the antioxidant is 2,6-tertiary butyl-4-methylphenol, the anti-ultraviolet light stabilizer is phenyl hydroxybenzoate, and the flame retardant is...

Embodiment 4

[0133] Embodiment four (polypropylene tarpaulin)

[0134] This embodiment provides a polypropylene tarpaulin, which includes a surface layer, a core layer and a bottom layer arranged sequentially from top to bottom.

[0135] Wherein, both the surface layer and the bottom layer are made of single-side coated resin non-woven fabric, and the thickness thereof is 0.26mm. The grammage of the resin-coated non-woven fabric on one side is 200g / m 2 .

[0136] Both the surface layer and the bottom layer include a resin sublayer and a nonwoven fabric sublayer, and the weight ratio of the resin sublayer to the nonwoven fabric sublayer is 1.8:1.

[0137] The resin sublayer is made of a resin material, and the resin material includes the following components and the parts by weight of each component are as follows:

[0138]

[0139] Among them, the antioxidant is tetrakis(β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) pentaerythritol ester, and the anti-ultraviolet light stabilizer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a piece of tarpaulin with high strength as well as a preparation method and an application thereof. The tarpaulin with high strength comprises a surface layer, a core layer and a bottom layer; the surface layer and the bottom layer are prepared from non-woven fabrics with resin coated on one side, and the core layer is prepared by a fiber enhanced thermoplastic resin prepreg. The preparation method of the tarpaulin with high strength comprises the following steps: two or more fiber enhanced thermoplastic resin prepreg tapes are laminated and laid on the other side of the non-woven fabrics with resin coated on one side where the resin material is not coated layer by layer in a 0 degree and 90 degrees alternated mode, the other non-woven fabric with resin coated on one side is laid on an uncombined surface of the fiber enhanced thermoplastic resin prepreg tape which is laid at last, so that the other side of the non-woven fabric with resin coated on one side where the resin material is not coated and the uncombined surface are attached, and after post processing, the tarpaulin with high strength is obtained. The tarpaulin with high strength not only has good strength, and has flame retardation, aging resistance, other performances, and long service life; in addition, the preparation method has simple process and high production efficiency.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and relates to a high-strength tarpaulin and its production method and application. Background technique [0002] At present, the tarpaulins used on trucks in our country are based on polyester staple fiber woven fabrics, which are coated with plastic to make double-sided artificial leather, and then sewn. This kind of tarpaulin has disadvantages such as low strength, heavy weight, rough surface, narrow surface width, easy aging, short service life, poor flame retardancy, low softness, warp and weft breaking tension and elongation rate are not up to standard during use, making the tarpaulin The cloth is easily damaged during use, thereby reducing the service life and increasing the cost of use. Contents of the invention [0003] The invention aims at the deficiencies of the prior art, and the main purpose is to provide a high-strength tarpaulin with high strength, light weight, tea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B5/26B32B37/06B32B37/08B32B37/10C08L23/12C08L23/06C08L67/00C08K13/02
CPCB32B5/26B32B37/06B32B37/08B32B37/10B32B2255/02B32B2255/26B32B2260/021B32B2260/046B32B2307/3065B32B2307/5825B32B2307/712C08K13/02C08L23/06C08L23/12C08L67/00C08L2201/02C08L2205/035
Inventor 杨桂生刘旭李兰杰
Owner 上海昶勤实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap