A kind of preparation method of bio-based water-based UV curing environment-friendly nail polish

A nail polish, bio-based technology, applied in the field of material chemistry, can solve the problems of life and health and environmental threats, not being environmentally friendly, non-toxic, human health hazards, etc., achieving good transparency, fast curing speed, and good adhesion.

Active Publication Date: 2020-06-16
BAOJI UNIV OF ARTS & SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, water-based nail polish uses resins such as water-based polyurethane or water-based acrylic acid as an adhesive, and water as a solvent, which has the disadvantage of slow drying at room temperature. Some formulas still contain nitrocellulose, which is not truly environmentally friendly and non-toxic. Containing alcohol ester twelve as film-forming aids, antifreeze agents such as ethylene glycol and propylene glycol, these ingredients pose a threat to life, health and the environment; commercially available UV nail polish refers to UV-curable nail polish containing active diluents, although not Contains organic solvents, but the main component prepolymer has a relatively high viscosity, and a reactive diluent must be used to adjust the viscosity, especially the commonly used acrylic ester reactive diluents have a strong stimulating effect and carcinogenicity. During the preparation process and drying hazards to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of bio-based water-based UV curing environment-friendly nail polish

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method for bio-based water-based UV curing environment-friendly nail polish, comprising the following steps:

[0035] 1) By mass percentage, weigh 8% of oligomer polyol, 6% of dry vegetable oil, 45% of diisocyanate compound, 1.2% of trimethylolpropane, 2% of hydrophilic chain extender, and 4.5% of reactive diluent %, neutralizing salt-forming agent 3%, water-based photoinitiator 0.1% and deionized water 30.2%;

[0036] 2) Add oligomer polyol and drying vegetable oil to the reactor and dehydrate in vacuum at 110° C. for 2 hours to obtain mixture a; add diisocyanate compound, trimethylolpropane, hydrophilic chain extender and solvent to mixture a, React at 60°C for 4 hours to obtain prepolymer b;

[0037] Wherein, the quality of solvent is 33% of the total mass of oligomer polyol, vegetable oil with dryness, diisocyanate compound, trimethylolpropane and hydrophilic chain extender;

[0038] The oligomer polyol is polycaprolactone diol;

[0039] The describ...

Embodiment 2

[0055] A preparation method for bio-based water-based UV curing environment-friendly nail polish, comprising the following steps:

[0056] 1) By mass percentage, weigh 22% of oligomer polyol, 4% of dry vegetable oil, 20% of diisocyanate compound, 2.4% of trimethylolpropane, 10% of hydrophilic chain extender, and 4.5% of reactive diluent %, neutralizing salt-forming agent 5%, water-based photoinitiator 0.3% and deionized water 31.8%;

[0057] 2) Add oligomer polyol and drying vegetable oil to the reactor and dehydrate in vacuum at 120° C. for 1 hour to obtain mixture a; add diisocyanate compound, trimethylolpropane, hydrophilic chain extender and solvent to mixture a, React at 90°C for 1 hour to obtain prepolymer b;

[0058] Wherein, the quality of solvent is 33% of the total mass of oligomer polyol, vegetable oil with dryness, diisocyanate compound, trimethylolpropane and hydrophilic chain extender;

[0059] The oligomer polyol is polytetrahydrofuran diol;

[0060] The desc...

Embodiment 3

[0076] A preparation method for bio-based water-based UV curing environment-friendly nail polish, comprising the following steps:

[0077] 1) By mass percentage, weigh 8% of oligomer polyol, 4.8% of dry vegetable oil, 20% of diisocyanate compound, 2% of trimethylolpropane, 2% of hydrophilic chain extender, and 5% of reactive diluent %, neutralizing salt-forming agent 3%, water-based photoinitiator 0.2% and deionized water 55%;

[0078] 2) Add oligomer polyol and drying vegetable oil to the reactor and dehydrate in vacuum at 110°C for 1.5h to obtain mixture a; add diisocyanate compound, trimethylolpropane, hydrophilic chain extender and solvent to mixture a , reacted at 70°C for 3 hours to obtain prepolymer b;

[0079] Wherein, the quality of solvent is 33% of the total mass of oligomer polyol, vegetable oil with dryness, diisocyanate compound, trimethylolpropane and hydrophilic chain extender;

[0080] The oligomer polyol is a mixture of polycarbonate diol and polyhexamethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of bio-based water-based UV curing environment-friendly nail polish, by weighing 30-50% of bio-based water-based UV curing environment-friendly nail polish resin, 5-10% of deionized water, 40-60% of pigment, moistening Wet dispersant 0.1-0.5%, leveling agent 0.1-0.5%, defoamer 0.2-0.5% and thickener 1.0-2.0%; add pigment, wetting and dispersing agent, leveling agent, defoamer to the ball mill Grind with deionized water to obtain color paste a; add bio-based water-based UV curing environmentally friendly nail polish resin to color paste a, add thickener after high-speed stirring, and filter through a 200-mesh filter to obtain bio-based water-based UV curing environmental protection nail polish. The nail polish prepared by the invention has the characteristics of fast curing speed, good transparency, storage stability, high gloss, good adhesion, etc. The method of the invention is green, environmentally friendly, non-toxic and tasteless, and reduces product cost.

Description

technical field [0001] The invention relates to the technical field of material chemistry, in particular to a preparation method of a bio-based water-based UV curing environment-friendly nail polish resin. Background technique [0002] As a kind of make-up, nail polish can form a film on the nails with bright color and give the nails a sense of beauty. There are two types of environmentally friendly nail polishes on the market today: water-based nail polish and UV nail polish. Although these two kinds of nitro nail polishes contain a large amount of esters, ketones, alcohol ethers and other volatile organic solvents in the early stage, compared with nitrocellulose modified resins as binders, they have no organic solvents, such as ethyl acetate, etc. , reducing the harm to nails and the human body, and environmental pollution. However, water-based nail polish uses resins such as water-based polyurethane or water-based acrylic acid as an adhesive, and water as a solvent, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/85A61K8/92C08G18/66C08G18/36C08G18/67C08G18/08A61Q3/02
CPCA61K8/85A61K8/922A61K2800/48A61Q3/02C08G18/36C08G18/6696C08G18/672C08G18/675C08G18/0823C08G18/6662
Inventor 杜娟顾洪溪窦树梅
Owner BAOJI UNIV OF ARTS & SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com