A copolymer with electrical storage properties, its preparation method and its application in electrical storage

A technology of electric storage and copolymers, applied in the field of copolymers, can solve the problems of few types of materials, inability to produce large-scale industrial production, storage stability cannot be guaranteed, etc., and achieve the effect of unsatisfactory solution and excellent stability

Active Publication Date: 2019-03-29
新纶电子材料(常州)有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are currently materials for electrical storage, most of them are still in the laboratory stage and cannot be mass-produced industrially. In addition, there are few types of materials that can be used for electrical storage, and their storage stability cannot be guaranteed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A copolymer with electrical storage properties, its preparation method and its application in electrical storage
  • A copolymer with electrical storage properties, its preparation method and its application in electrical storage
  • A copolymer with electrical storage properties, its preparation method and its application in electrical storage

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] In this Example 1, a preparation method of the above-mentioned copolymer with electrical storage properties, 0.5 g of monomer X, 0.8 g of monomer Y, 0.02 g of azobisisobutyronitrile and 2 mL of cyclohexanone were added to In the polymerization tube, react in an oxygen-free environment at 80°C for 12 h to 20 h, then pour the reaction product into methanol to precipitate a solid, and dry it to obtain the copolymer. Wherein, azobisisobutyronitrile is used as a catalyst for the polymerization reaction; cyclohexanone is used as a solvent, and any one or more of cyclohexanone, toluene, dimethylformamide or dichloroethane can also be used to replace; none The oxygen environment can be realized by introducing an inert gas into the reaction vessel, and the inert gas that can be used includes any one or more of nitrogen, argon, and helium.

[0036] In this example 1, monomer X can be purchased from the market, and can also be prepared by the following method: the parts mentioned ...

Embodiment 2

[0040] An electric storage device with a copolymer having electric storage properties obtained in Example 1, such as figure 1 As shown, it includes a first electrode layer 1, an active layer 2 and a second electrode layer 3 from bottom to top, wherein the active layer 2 is the copolymer obtained in Example 1 with electrical storage properties. In this embodiment 2, the thickness of the active layer 2 is 100 nm to 200 nm; the first electrode layer 1 and the second electrode layer 3 are conductive glass or metal electrodes, further, the first electrode layer 1 and the second electrode layer 3 is a magnesium electrode, a silver electrode, a calcium electrode or an aluminum electrode.

Embodiment 3

[0042] A method for preparing the electrical storage device of Example 2, using ITO glass as the first electrode layer 1, using an organic solvent to ultrasonically clean the ITO glass, and drying to remove the organic solvent. In this Example 3, chloroform, Acetone and isopropanol were used to ultrasonically clean the ITO glass in sequence; at room temperature, the copolymer with electrical storage properties prepared in Example 1 was dissolved in chloroform to form a solution of 10 mg / mL to 20 mg / mL , the solution was stirred at a stirring speed of 200 rpm to 1200 rpm for 6 h to 10 h to ensure that the copolymer with electrical storage properties was fully dissolved; the prepared solution was spin-coated on ITO glass at a speed of 600 rpm to 4000 rpm On one side, form the active layer 2 that thickness is 150 nm, in this embodiment 3, spin-coating rotational speed is preferably 1500 rpm; After the ITO conductive glass with active layer 2 is dried, in 5 * 10 -4 A 100 nm alumi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
concentrationaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a copolymer, in particular to a copolymer with electrical storage properties, which is formed by copolymerization of monomer X and monomer Y, monomer X is a carbazole group, and monomer Y is an azo group ; The mass percentage of monomer X is 30%-90%, and the mass percentage of monomer Y is 10%-70%; the number average molecular weight of the copolymer is 5000-15000. The invention also relates to a process for preparing the copolymer. The invention also relates to an electric storage device prepared by using the copolymer, and a preparation method of the electric storage device. The copolymer with electrical storage characteristics of the present invention and the electrical storage device prepared by the copolymer can realize binary storage and have excellent stability, and the large-scale application of organic electrical storage materials and devices provides more choices. To a certain extent, it solves the problem that the types of materials currently available for electrical storage are relatively small and the effect is not ideal.

Description

technical field [0001] The invention relates to a copolymer, in particular to a copolymer with electrical storage properties and a preparation method thereof. [0002] The invention also relates to an electric storage device prepared by using the copolymer, and a preparation method of the electric storage device. Background technique [0003] Traditional information storage methods mainly use inorganic silicon semiconductor materials. However, due to the high production cost of silicon and other inorganic materials, complex processes, and the inability to manufacture large areas, they cannot meet the needs of today's society for information storage. So it motivates us to look for materials with lower cost, which can be manufactured in large area and have higher information storage capacity. Compared with silicon devices that record data by marking "0" and "1" states, the data storage of organic electrical memory devices is a new mode, which changes organic materials from a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/14H01L51/05H01L51/30H01L51/40
CPCC08F212/14H10K85/151H10K10/00
Inventor 张盼
Owner 新纶电子材料(常州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com