Corrosion resistant epoxy resin paint

An epoxy resin coating and epoxy resin technology, applied in epoxy resin coatings, anti-corrosion coatings, polyamide coatings, etc., can solve the problems of unavoidable anti-corrosion and mechanical measures, and achieve low cost, good corrosion resistance, and high adhesion. Strong effect

Active Publication Date: 2017-05-31
安徽浩丰特种电子材料有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the current rapid economic development, the mechanical properties and corrosion of outdoor metals have attracted more and more attention. Due to the harsh working environment for a long time, especially in some working environments in areas exposed to the sun for a long time, the anti-corrosion and mechanical measures of metals are not enough. Avoid, the general practice is to paint on the metal surface, but the corrosion resistance and mechanical properties of conventional epoxy coatings cannot meet the needs of harsh working environments. How to prepare a epoxy coating with strong adhesion, good corrosion resistance and excellent mechanical properties Coatings for outdoor metals have become a technical problem that needs to be solved at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A corrosion-resistant epoxy resin coating, including A component and B component;

[0023] The raw materials of component A include by weight: 60 parts of bisphenol A epoxy resin, 15 parts of polyamide resin, 18 parts of E-44 epoxy resin, 2 parts of silane coupling agent, 8 parts of zeolite powder, sodium antimonate 1 part, 15 parts of modified bamboo powder, 0.5 part of epoxy soybean oil, 4 parts of dibutyl ester, 1 part of anti-settling agent, 2 parts of leveling agent, 1 part of dispersant, 2 parts of defoamer;

[0024] The raw materials of component B include by weight: 15 parts of dihexyltriamine, 25 parts of hexamethylenediamine, 15 parts of butanol, and 10 parts of xylene;

[0025] The weight ratio of component A to component B is 10:2.

Embodiment 2

[0027] A corrosion-resistant epoxy resin coating, including A component and B component;

[0028] The raw materials of component A include by weight: 40 parts of bisphenol A epoxy resin, 35 parts of polyamide resin, 10 parts of E-44 epoxy resin, 4 parts of silane coupling agent, 2 parts of zeolite powder, sodium antimonate 5 parts, 5 parts of modified bamboo powder, 1.5 parts of epoxy soybean oil, 2 parts of dibutyl ester, 2 parts of anti-settling agent, 1 part of leveling agent, 2 parts of dispersant, 1 part of defoamer;

[0029] The raw materials of component B include by weight: 25 parts of dihexyltriamine, 15 parts of hexamethylenediamine, 20 parts of butanol, and 2 parts of xylene;

[0030] The weight ratio of component A to component B is 10:4.

Embodiment 3

[0032] A corrosion-resistant epoxy resin coating, including A component and B component;

[0033] The raw materials of component A include by weight ratio: 52 parts of bisphenol A epoxy resin, 20 parts of polyamide resin, 15 parts of E-44 epoxy resin, 3 parts of silane coupling agent, 6 parts of zeolite powder, sodium antimonate 2 parts, 12 parts of modified bamboo powder, 1 part of epoxy soybean oil, 3.4 parts of dibutyl ester, 1.2 parts of anti-settling agent, 1.6 parts of leveling agent, 1.2 parts of dispersant, 1.6 parts of defoamer;

[0034] The raw materials of component B include by weight: 20 parts of dihexyltriamine, 20 parts of hexamethylenediamine, 16 parts of butanol, and 8 parts of xylene;

[0035] The weight ratio of component A to component B is 10:3.

[0036] The modified bamboo powder is prepared by the following process: mix 20 parts of bamboo powder and 5 parts of rice bran evenly by weight, add water until the water content is 35wt%, add 0.01 part of EM ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion resistant epoxy resin paint. The corrosion resistant epoxy resin paint comprises a component A and a component B; the component A contains the following raw materials according to weight ratio: 40-60 parts of bisphenol A epoxy resin, 15-35 parts of polyamide resin, 10-18 parts of E-44 epoxy resin, 2-4 parts of a silane coupling agent, 2-8 parts of a zeolite powder, 1-5 parts of sodium antimonate, 5-15 parts of a modified bamboo powder, 0.5-1.5 parts of epoxidized soybean oil, 2-4 parts of dibutyl ester, 1-2 parts of an anti-settling agent, 1-2 parts of a leveling agent, 1-2 parts of a dispersant and 1-2 parts of a defoaming agent; the component B contains the raw materials in parts by weight: 15-25 parts of di-hexyl triamine, 15-25 parts of hexamethylene diamine, 15-20 parts of butanol and 2-10 parts of dimethylbenzene; the weight ratio of the component A to the component B is 10: 2-4. The corrosion resistant epoxy resin paint disclosed by the invention has the advantages of strong adhesive force, good corrosion resistance and excellent mechanical property.

Description

technical field [0001] The invention relates to the technical field of epoxy coatings, in particular to a corrosion-resistant epoxy resin coating. Background technique [0002] With the current rapid economic development, the mechanical properties and corrosion of outdoor metals have attracted more and more attention. Due to the harsh working environment for a long time, especially in some working environments in areas exposed to the sun for a long time, the anti-corrosion and mechanical measures of metals are not enough. Avoid, the general practice is to paint on the metal surface, but the corrosion resistance and mechanical properties of conventional epoxy coatings cannot meet the needs of harsh working environments. How to prepare a epoxy coating with strong adhesion, good corrosion resistance and excellent mechanical properties Coatings for outdoor metals have become a technical problem to be solved at present. Contents of the invention [0003] The invention provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D177/00C09D191/00C09D197/02C09D7/12C09D5/08
CPCC08L2205/025C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D7/70C09D163/00C08L77/00C08L63/00C08L91/00C08L97/02C08K13/02C08K5/54C08K7/26C08K3/24C08K5/12
Inventor 凡来权
Owner 安徽浩丰特种电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com