A kind of preparation method of reactive flame retardant containing phosphorus, nitrogen and sulfur in epoxy resin

A reactive flame retardant, epoxy resin technology, applied in chemical instruments and methods, compounds of Group 5/15 elements of the periodic table, organic chemistry, etc., can solve the problem of poor polymer matrix compatibility and decreased matrix mechanical properties. and other problems, to achieve the effects of easy post-processing, improved flame retardant performance, easy control and industrialized production

Active Publication Date: 2018-06-12
FUJIAN NORMAL UNIV
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the operation is simple, it is accompanied by some problems in use, such as poor compatibility with the polymer matrix, resulting in a decrease in the mechanical properties of the matrix, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of reactive flame retardant containing phosphorus, nitrogen and sulfur in epoxy resin
  • A kind of preparation method of reactive flame retardant containing phosphorus, nitrogen and sulfur in epoxy resin
  • A kind of preparation method of reactive flame retardant containing phosphorus, nitrogen and sulfur in epoxy resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In a container equipped with a condenser tube and a stirrer, 13.42g p-hydroxybenzaldehyde, 16.5g 2-aminobenzothiazole and 200ml ethanol were added successively under stirring, nitrogen gas was fed into it, and after 2 hours of reaction at 50°C, 23.76g DOPO was added and the reaction was continued for 24 hours. After the reaction, the system was suction filtered, washed 3 times with ethanol, and dried to obtain the white product 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-(4-hydroxyphenyl) (2 -iminobenzothiazole)methane-10-oxide (D-P-ABZ), yield 89%.

Embodiment 2

[0023] In a container equipped with a condenser tube and a stirrer, 16.10 g of p-hydroxybenzaldehyde, 19.8 g of 2-aminobenzothiazole and 120 ml of acetone were added successively under stirring, nitrogen gas was introduced, and after 1.8 hours of reaction at 52 ° C, Add 23.76g DOPO, continue to react for 26 hours. After the reaction is complete, filter the solution with suction, wash with acetone for 3 to 4 times, and dry to obtain the white product 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-(4-hydroxyphenyl) (2-Iminobenzothiazole)methane-10-oxide (D-P-ABZ), yield 78%.

Embodiment 3

[0025] In a container equipped with a condenser tube and a stirrer, 14.76g of p-hydroxybenzaldehyde, 18.15g of 2-aminobenzothiazole and 250ml of acetone were added successively under stirring, nitrogen gas was introduced, and after 2.2 hours of reaction at 48°C, Add 23.76g DOPO, continue to react for 26 hours. After the reaction, the system was suction filtered, washed 3 times with acetone, and dried to obtain the white product 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-(4-hydroxyphenyl) (2 -iminobenzothiazole)methane-10-oxide (D-P-ABZ), yield 70%.

[0026] The test and analysis results of the flame retardant D-P-ABZ prepared by the present embodiment are as follows:

[0027] 1 H NMR (400MHz, DMSO-d 6 ), δ (ppm): 9.54, 9.51 (s, 1H), 8.98-9.10 (m, 1H), 8.14-8.21 (m, 2H), 7.44-7.78 (m, 4H), 7.13-7.41 (m, 6H ), 6.96-7.08(m, 2H), 6.69-6.74(m, 2H), 5.57-5.85(m, 1H);

[0028] 31 P-NMR (162MHz, DMSO-d 6 ), δ (ppm): 28.59, 29.96;

[0029] HRMS (EI + ): calcd.for C 26 h 20...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing nitrogen phosphate sulfur-containing reactive flame retardant applied to epoxy resin. The preparation method comprises the following steps: sequentially adding p-hydroxy benzaldehyde, aminothiazole and a solvent into a reactor which is provided with a condensing pipe and a stirrer, and introducing inert gas to perform first reaction; adding 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide to carry out second reaction; and pumping, filtering, washing and drying the system to obtain white or light brown nitrogen phosphate sulfur-containing reactive flame retardant after the reaction is completed. The method has the advantages that 1, the synthesizing process is short, the cycle is short, post-treatment is easy, and control and industrial production are easy; 2, the prepared flame retardant contains nitrogen, phosphate and sulfur three flame-retardant elements at the same time, has a synergistic flame-retardant effect, and can be used for remarkably improving the flame retarding performance of epoxy resin; and 3, the prepared flame retardant is a reactive flame retardant, and can be used for keeping stability and mechanical performance of cured epoxy resin while improving the flame retarding effect of the cured epoxy resin.

Description

technical field [0001] The invention relates to a preparation method of a reactive flame retardant, in particular to a preparation method of a phosphorus, nitrogen and sulfur reactive flame retardant used in epoxy resin. Background technique [0002] As a typical thermosetting polymer, epoxy resin has excellent adhesion, mechanical properties, electrical insulation and corrosion resistance, as well as low shrinkage, easy processing and low cost, etc. It is used in integrated circuits, transportation , Aerospace and other high-tech fields have been widely used. However, epoxy resin is a flammable material, and when it burns, it has a large heat release rate, high calorific value, fast flame propagation speed, is not easy to extinguish, and sometimes produces dense smoke and toxic gases, causing harm to the environment and endangering people's lives and property. Security poses a huge threat. Therefore, improving the flame retardant properties of epoxy resins has become a ho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07F9/6574C08G59/62C08G59/56
CPCC07F9/657172C08G59/56C08G59/621
Inventor 简荣坤王盼夏龙余小琴郑雪琳
Owner FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com