Weather-resistant coating and preparation method thereof

A coating and coating technology, which is applied in the field of weather-resistant coating coating and its preparation for pre-laying anti-adhesive waterproof coil protection layer, can solve the problems of inability to achieve 100% continuous coverage, inability to shield ultraviolet rays, etc., and achieve improved shielding of ultraviolet rays Performance, improvement of anti-channeling performance, effect of improving waterproof performance

Inactive Publication Date: 2017-05-24
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the protective layer made by this method can partially block and shield ultraviolet rays, it cannot achieve a complete ultraviolet shielding effect because the mineral particles cover the surface of the adhesive layer and cannot achieve 100% continuous coverage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Weather-resistant coating and preparation method thereof
  • Weather-resistant coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Preparation of Coil Protective Coating with UV Resistance

[0021] The protective coating for coils with high UV resistance contains the following components in parts by weight:

[0022] water Deionized water 25 copies acrylic emulsion Rohm and Haas AC-261P 35 copies filler Heavy Calcium Jiangxi Guangyuan CC800 30 copies UV absorber Ciba UV Absorber 326 1.0 copies Nano Zinc Oxide Shanghai Zecheng ZEC Slurral ZNO30W 5.0 copies Dispersant DP270 1.0 copies D CF10 0.5 parts Defoamer NXZ 0.5 parts leveling agent ASE-60 0.5 parts thickener RM-8W 1.0 copies preservative MV 0.5 parts

[0023] A method for preparing a coil protection coating with high UV resistance, comprising the following steps:

[0024] (1) Accurately weigh water of the same quality as the nano-zinc oxide powder according to the formula, add half of the total mass of the dispersant and pre-mix...

Embodiment 2

[0027] Example 2: Coil protective coating with high UV resistance

[0028] The protective coating for coils with high UV resistance contains the following components in parts by weight:

[0029]

[0030]

[0031] The preparation method of the coil protective coating with high UV resistance is the same as that in Example 1.

Embodiment 3

[0032] Example 3: Coil protective coating with high UV resistance

[0033] The protective coating for coils with high UV resistance contains the following components in parts by weight:

[0034] water Deionized water 15 copies acrylic emulsion Rohm and Haas AC-261P 30 copies filler Heavy Calcium Jiangxi Guangyuan CC800 42 copies UV absorber Ciba UV Absorber 326 2.0 copies Nano Zinc Oxide Shanghai Zecheng ZEC Slurral ZNO 30W 7.0 copies Dispersant DP270 0.5 parts D CF10 0.5 parts Defoamer NXZ 1.0 copies leveling agent ASE-60 0.5 parts thickener RM-8W 1.0 copies preservative MV 0.5 parts

[0035] The preparation method of the coil protection coating with high UV resistance is the same as that in Example 1.

[0036] The performance test results corresponding to the above embodiments are shown in Table 1.

[0037] Table 1 - performance test results of each embodiment

[0038...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a weather-resistant coating and a preparation method thereof. The weather-resistant coating comprises the following components in parts by weight: 10-40 parts of water, 10-50 parts of an acrylic acid emulsion, 20-70 parts of packing, 0.1-1 part of an ultraviolet absorbent, 1-30 parts of nano zinc oxide, 0.1-5 parts of a dispersing agent, 0.1-5 parts of a wetting agent, 0.5-5 parts of a defoaming agent, 0.1-5 parts of a leveling agent, 0.1-5 parts of a thickening agent and 0.1-5 parts of a preservative. The invention further discloses a preparation method of the weather-resistant coating. By adopting the weather-resistant coating, the ultraviolet light shielding property of a coated layer can be protected, meanwhile, the density of the coated layer can be greatly increased, the water resistance property of the coated layer can be improved, and thus the water movement prevention property of a pre-installed and inverted adhered waterproof roll can be improved; and in addition, the tensile strength and break elongation of the coated layer can be remarkably improved, and thus the waterproof property of the pre-installed and inverted adhered waterproof roll can be improved.

Description

technical field [0001] The invention relates to a weather-resistant coating and a preparation method thereof, in particular to a weather-resistant coating for pre-laying a protective layer of an anti-adhesive waterproof coil and a preparation method thereof. Background technique [0002] Since it was introduced into the Chinese market in the 1990s, the pre-laid anti-adhesive waterproof membrane has developed rapidly in China due to its excellent anti-channeling performance, and has been widely used in underground projects, open-cut tunnel projects, and underground tunnel projects. Key projects such as underground pipe gallery waterproofing works. The typical structure of pre-laid anti-adhesive waterproof membrane includes the main waterproof layer, adhesive layer and protective layer. The main function of the protective layer is to protect the adhesive layer from external pollution, isolate ultraviolet rays and oxygen environment, and protect the adhesive layer. Chain sciss...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D125/14C09D133/04C09D169/00C09D7/12
CPCC09D131/04C08K2201/011C08L2201/08C08L2205/035C09D7/61C09D7/62C09D7/63C09D7/65C09D125/14C09D133/04C09D143/04C09D169/00C08L25/14C08L33/04C08L43/04C08L69/00C08L33/02C08K13/06C08K9/00C08K2003/2296C08K2003/265C08K2003/2241C08K3/346C08K5/1345
Inventor 徐恩顺熊玉钦
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com