A frosted lens and its preparation method

A frosted and lens technology, applied in the field of frosted lenses and its preparation, can solve the problems of glue failure, substrate peeling off, increased cost and process of bonding materials, etc., and achieve the effect of firm bonding

Active Publication Date: 2019-09-06
丹阳市大尧光学眼镜有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in the preparation process of this kind of frosted lens, it is often necessary to use adhesive materials such as glue to bond the frosted substrate and the smooth substrate to achieve the above effect, but the loss rate of this preparation method is high, and the bonding The use of materials also increases the cost and process. After a long time of use, it is easy to cause the glue to fail and cause the substrate to fall off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A frosted lens, the inner surface is concave, the outer surface is convex, the frosted lens is a multi-layer composite structure, and from the inside to the outside is a PC substrate with a thickness of 1 mm, a coating layer, and a leveling layer whose outer surface has been frosted.

[0021] Among them, the coating layer is an ultraviolet absorbing layer and a transparent anti-reflection layer from the inside to the outside.

[0022] The UV absorbing layer consists of 65wt% stearyl methacrylate, 1.5wt% benzofuran-2-one, 16wt% acrylic acid-2-(4-benzoyl-3-hydroxyl-phenoxy) Ethyl ester and the balance of absolute ethanol are formed by spraying, with a thickness of 15 microns;

[0023] The transparent anti-reflection layer is formed by magnetron sputtering from 23wt% aluminum oxide, 28wt% titanium dioxide, 25wt% titanium nitride and the rest aluminum nitride, with a thickness of 15 microns.

[0024] The preparation method of above-mentioned frosted lens:

[0025] (1) fro...

Embodiment 2

[0034] A frosted lens, the inner surface is concave, the outer surface is convex, the frosted lens is a multi-layer composite structure, from the inside to the outside is a CR-39 substrate with a thickness of 0.75mm, a polarizing film, and the thickness of the outer surface that has been frosted. 0.75mm CR-39 substrate, coating layer, leveling layer,

[0035] Wherein, the coating layer is a photochromic layer,

[0036] The photochromic layer consists of 58wt% polyacrylate, 0.56wt% 1,3-diphenyl-4-m-bromobenzoyl-5-pyrazolone, 0.5wt% naphthopyran, 1.2wt% The benzofuran-2-one, 0.45wt% of 2-hydroxy-4-methoxy-4'-chlorobenzophenone and the rest of absolute ethanol were formed by spraying, with a thickness of 20 microns.

[0037] The preparation method of above-mentioned frosted lens:

[0038] (1) frosting the outer surface of the outer substrate;

[0039] (2) coating on the frosted surface obtained in step (1);

[0040] (3) the coating surface obtained in step (2) is subjected to...

Embodiment 3

[0046] A frosted lens, the inner surface is concave, the outer surface is convex, the frosted lens is a multi-layer composite structure, and from the inside to the outside is a nylon substrate with a thickness of 1 mm, a coating layer, and a leveling layer whose outer surface has been frosted.

[0047] Wherein, the coating layer is an AR layer with a thickness of 15 microns.

[0048] The preparation method of above-mentioned frosted lens:

[0049] (1) frosting the outer surface of the substrate, and dyeing on the frosted surface;

[0050] (2) plate AR film on the frosted surface obtained in step (1);

[0051] (3) the coating surface obtained in step (2) is subjected to ion gun spraying treatment:

[0052] The ion source is bombarded with a voltage of 120V and a filament current of 30A, and 30 argon gas flows per minute are sent to the coating surface of the lens, and the processing time is 4s;

[0053] (3) Carry out hardening and leveling to the coating surface treated by s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of glasses lenses and particularly relates to a frosted lens and a preparation method thereof. The preparation method comprises the following steps: carrying out frosting treatment on the outer surface of a substrate, carrying out film plating on a frosted surface, carrying out ion gun spraying on a film plated surface and filling the film plated surface subjected to the ion gun spraying treatment. According to the frosted lens provided by the invention, tight and form combination of the frosted surface, a film plated layer and a filling layer of the substrate is successfully realized; and the ideal frosted effect of the lens is still kept.

Description

technical field [0001] The invention belongs to the technical field of spectacle lenses, in particular to a frosted lens and a preparation method thereof. Background technique [0002] People usually rely on adjusting the pupil size to adjust the luminous flux in the sun. When the light intensity exceeds the adjustment ability of the human eye, it will cause damage to the human eye. Therefore, in outdoor activities, especially in summer, it is necessary to use sunshade mirrors to block the sun, so as to reduce the fatigue caused by eye adjustment or the damage caused by strong light stimulation. Today, the role of sunglasses is far more than just protecting the eyes, and it has become more and more a fashionable decoration and is accepted by consumers. [0003] Lens is the core of the quality of glasses. With the development of sunglasses technology, frosted lenses have appeared, that is, the outer surface of the lens substrate (the outer surface faces the object to be obse...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G02C7/02G02B1/14
Inventor 陶津
Owner 丹阳市大尧光学眼镜有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap