A technology of volatile organic and volatile organic compounds, which is applied in the field of new adsorbent-modified sepiolite-based molecular sieve and its preparation, can solve the problems of reduced adsorption, poor formability, and easy cracking of the surface, and achieve fast adsorption speed, Good adsorption effect, good treatment effect

Active Publication Date: 2017-04-05
SHANGHAI LANBAO ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the pore size of sepiolite fiber without activation treatment is small, some pores are filled with adsorbed water and zeolite water, and some pores collapse, the channel is narrow, the thermal stability is poor, and there are other impurities, which directly affect its adsorption. It can be directly applied to the purification treatment of industrial organic waste gas
[0004] Therefore, the sepiolite must be activated before use, and acid modification is commonly used. During acid modification, the acid concentration and modification time must be controlled, so that the activated pore size is aimed at the main components of organic waste gas. The sea foam prepared under this condition The pore size of pumice is relatively uniform, and sepiolite has strong adsorption selectivity and strong adsorption to polar molecules, but the composition of industrial waste gas discharged in the industry is relatively complex, except for the main components, there are othe...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel adsorbent used for purifying volatile organic waste gas
  • Novel adsorbent used for purifying volatile organic waste gas

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The fibrous α-sepiolite is pulverized into powder with a particle size of 325 mesh by roller milling, and the obtained sepiolite powder is placed in a reaction kettle, and hydrochloric acid with a concentration of 0.2mol / L is added. The liquid-solid ratio is 10 (L / kg), the mixture is stirred at room temperature for 8 hours, filtered, washed, and dried to obtain hydrochloric acid activated sepiolite.

[0035] Add 80% by mass aluminum dihydrogen phosphate solution and 30% by mass silica sol to sepiolite activated by hydrochloric acid and mix uniformly. The active ingredient accounts for 100 parts by weight, and the mixture contains aluminum dihydrogen phosphate. 2 parts by weight, 3 parts by weight of silica sol solids, 2 parts by weight of polyvinyl butyral, and 2 parts by weight of KH560. After the mixture was placed in a closed container for 24 hours, it was pressed into a honeycomb structure blank in a mold, cured at 110°C for a curing time of 12 hours, and then placed i...

Embodiment 2

[0038] The fibrous α-sepiolite is pulverized into powder with a particle size of 325 mesh by roller milling, and the obtained sepiolite powder is placed in a reaction kettle, and hydrochloric acid with a concentration of 0.2mol / L is added. The liquid-solid ratio is 10 (L / kg), the mixture is stirred at room temperature for 8 hours, filtered, washed, and dried to obtain hydrochloric acid activated sepiolite.

[0039] The activated carbon powder with a mass fraction of 15% is added to the hydrochloric acid activated sepiolite, and the particle size of the activated carbon powder is 325 mesh to obtain a mixed raw material.

[0040] Add 80% by mass aluminum dihydrogen phosphate solution and 30% by mass silica sol to sepiolite activated by hydrochloric acid and mix uniformly. The active ingredient accounts for 100 parts by weight, and the mixture contains aluminum dihydrogen phosphate. 2 parts by weight, 3 parts by weight of silica sol solids, 2 parts by weight of polyvinyl butyral, and ...

Embodiment 3

[0042] The fibrous α-sepiolite is pulverized into powder with a particle size of 325 mesh by roller milling, and the obtained sepiolite powder is placed in a reaction kettle, and hydrochloric acid with a concentration of 0.2mol / L is added. The liquid-solid ratio is 10 (L / kg), the mixture is stirred at room temperature for 8 hours, filtered, washed, and dried to obtain hydrochloric acid activated sepiolite.

[0043] The mesoporous zeolite molecular sieve with a mass fraction of 15% is added to the hydrochloric acid activated sepiolite, and the particle size of the zeolite is 325 mesh to obtain a mixed raw material.

[0044] Add 80% of the mass fraction of aluminum dihydrogen phosphate solution and 30% of the mass fraction of silica sol to the mixed raw materials and mix evenly. Based on 100 parts by weight of the active ingredient, the mixture accounts for 2 parts by weight of aluminum dihydrogen phosphate , The silica sol solid matter accounts for 3 parts by weight, polyvinyl butyr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of environmental protection, and particularly relates to a novel adsorbent-modified sepiolite base molecular sieve used for purifying volatile organic waste gas and a preparation method and application thereof. Modified sepiolite serves as the base material of the adsorbent and can be used for purifying industrial organic waste gas. The preparation method of the novel volatile organic compound adsorbent provided by the invention includes the steps that the sepiolite is ground into powder particles and then is acid-activated; and an inorganic binder solution is added to be evenly stirred so that a mixture can be obtained, the mixture is aged to be squeezed to be of a granular or honeycomb structure, and the novel volatile organic compound adsorbent can be prepared by means of solidifying and roasting. The novel volatile organic compound adsorbent prepared through the method is used for purifying the industrial organic waste gas, the method for solving the VOCs pollution problem is provided, and meanwhile the rich sepiolite resources in China can be efficiently utilized.

Description

Technical field [0001] The invention belongs to the technical field of environmental protection, and specifically relates to a novel adsorbent-modified sepiolite-based molecular sieve for purifying volatile organic waste gas and a preparation method thereof. The adsorbent substrate is modified sepiolite and can be used for Purify industrial organic waste gas. Background technique [0002] The purification and treatment of industrial waste gas containing volatile organic compounds (VOCs) is a hot spot in air pollution control. Among many methods for purifying industrial organic waste gas, the adsorption method is widely used because of its simple process, convenient operation and high purification efficiency. [0003] Sepiolite is a kind of water-containing magnesium-rich silicate clay mineral. In the fibrous crystal structure of sepiolite, there are many tubular through channels consistent with the extension direction of the fibers, making the sepiolite up to 900m 2 / g theoretical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/12B01J20/30B01D53/02
CPCB01D53/02B01D2257/708B01J20/12
Inventor 许永童
Owner SHANGHAI LANBAO ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap