Method for doping trace boron element into weld metal and welding method

A weld metal and trace technology, which is used in the field of welding metallurgy and alloying to achieve the effects of improving service safety, toughness and development promotion.

Inactive Publication Date: 2017-03-22
江苏立新焊接材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the field of welding material application, there is no report on the use of borides for boronizing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for doping trace boron element into weld metal and welding method
  • Method for doping trace boron element into weld metal and welding method
  • Method for doping trace boron element into weld metal and welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] According to the metallurgical method of the present invention, the matching manual electrode design for 12MnCrNi steel is implemented. According to the technical requirements of the 12MnCrNi steel matching manual welding rod (see Table 1), design and make three batches of 12MnCrNi steel matching manual welding rods containing borax (sodium tetraborate, Na2B4O7. Middle), the composition of the steel core and coating powder used in the three batches of electrodes are shown in Table 2 and 3, respectively. The base metal and welding process parameters of the three batches of electrodes are shown in Table 4. After welding, the mechanical properties of the deposited metal were tested, and the test results are shown in Table 5. As a comparison, see Table 6 for the test data of 12MnCrNi steel supporting manual electrodes that do not contain borides on the original drug skin.

Embodiment ——12

[0014] Table 1 embodiment - technical requirements for 12MnCrNi steel supporting manual welding rod

[0015] Deposited Metal Mechanical Properties

[0016]

[0017] Table 2 embodiment——12MnCrNi steel matching manual electrode steel core composition (weight, %) (specification 4mm)

[0018]

[0019] Table 3 embodiment - 12MnCrNi steel matching manual electrode coating composition (weight, %)

[0020]

[0021] Potassium sodium mixed with water glass is used for bonding, and the outer diameter of the coating is 6.0mm.

[0022] The embodiment of table 4 - the base metal and welding process parameters of three batches of welding rods

[0023]

[0024] Table 5 Example - three batches of electrode deposited metal chemical composition and mechanical properties

[0025]

[0026] Table 6 Chemical composition and mechanical properties of deposited metal of 12MnCrNi steel with manual electrode without boride coating

[0027]

[0028] It can be seen that compared with ...

Embodiment 2

[0030] The metallurgical method according to the present invention was implemented in an improved design of 350 flux. Design and make three batches of flux containing B 2 o 3 The 350G flux, the flux production method is the same as the original 350 flux. The components of the three batches of flux are shown in Table 7, respectively. The welding wire for the three batches of flux is 12MnCrNi (size 4mm), and the base metal and welding process parameters are shown in Table 8. After welding, the mechanical properties of the deposited metal were tested, and the test results are shown in Table 9.

[0031] Table 7 Example - 350G flux composition (weight, %)

[0032]

[0033] Table 8 Example - Base metal and welding process parameters welded by three batches of flux 350G

[0034]

[0035] Table 9 Examples - Chemical Composition and Mechanical Properties of Deposited Metal

[0036]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for doping the trace boron element into weld metal and a welding method. The method for doping the trace boron element into the weld metal includes the step that the boride is added into a welding material, and the mass ratio of the boride to the welding material is 0.1-2:100. When the boride-containing welding material is used for welding, elemental boron can be decomposed in the welding arc space from the boride, and the elemental boron is doped into the weld metal. The welding material is a manual electrode coating or the flux-core of a flux-cored wire and submerged-arc welding flux.

Description

technical field [0001] The invention relates to a welding metallurgical alloying method, in particular to a metallurgical method for infiltrating a trace amount of boron element into a weld metal by means of a coating of an electrode, a flux core of a flux-cored wire and a submerged arc flux. Background technique [0002] Microalloying the weld metal of low-carbon low-alloy steel with titanium (Ti) and boron (B) can make the weld metal obtain very high toughness. Therefore, Ti-B treatment is an important metallurgical means for toughening steel weld metal today. At present, in the application field of welding materials, the method of directly infiltrating a small amount of B into the weld metal by ferroboron alloy is generally used. That is to add iron-boron alloy to the coating of the electrode, the core of the flux-cored wire and the submerged arc welding flux. The metal is infiltrated with a trace amount of boron. In the field of surface chemical heat treatment, boroni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/18B23K35/36C23C8/68
CPCB23K9/18B23K35/36C23C8/68
Inventor 桂赤斌
Owner 江苏立新焊接材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com