A technology of active ceramics and bottom glaze, which is applied in the field of daily necessities, can solve the problems of unusable raw materials, weak field effect, and reduced physiotherapy effect, and achieve the effects of protecting bone growth, strong field effect, and relieving discomfort

Inactive Publication Date: 2017-03-08
青岛首创嘉业工贸有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are currently ceramic magnetic health products on the market with weak field effects. This is because the magnetic fields of various raw materials with field effects in the powder state go their own way, and do not form a unified energy field like the whole raw material, resulting in mutual interference. Decreases the effect of physiotherapy, resulting in little overall effect
In the field of ceramics, only powder or slurry can be used in the process of blanking and glazing, and high-temperature firing is required, so it is impossible to use a whole piece of raw material with field effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1) The surface glaze raw materials are composed by weight: 400 parts of kaolin, 125 parts of clay, 65 parts of talc, 65 parts of feldspar, 50 parts of dolomite, 20 parts of zinc oxide, and 10 parts of pigment. Weigh the materials and mix them for later use;

[0030] 2) According to the weight of energy powder: 5.3 parts of diamond medicine stone, 2.5 parts of black tourmaline, 1.3 parts of lapis lazuli, 3.5 parts of coral stone, 1.7 parts of obsidian, 0.05 parts of citrine, 3.6 parts of medical stone, 3.8 parts of calcium gluconate , 0.5 parts of meteorites, 0.013 parts of zinc glutamate, and 0.25 parts of keels Weigh the materials and mix them thoroughly; then grind them with a grinder at a temperature of 550 ° C to obtain energy powder of 2000 mesh to 6000 mesh;

[0031] 3) 22.6 parts of energy powder of 2000 mesh to 6000 mesh and 745 parts of the surface glaze raw materials prepared in step 1) are weighed in parts by weight and ground together in a grinder to obtain t...

Embodiment 2

[0034] 1) The composition of surface glaze raw materials in parts by weight includes 350 parts of kaolin, 150 parts of clay, 50 parts of talc, 80 parts of feldspar, 30 parts of zinc oxide, and 10 parts of pigment. Weigh the materials and mix them for later use;

[0035] 2) The composition of the energy powder by weight is: 5.2 parts of diamond medicine stone, 2.4 parts of black tourmaline, 1.5 parts of lapis lazuli, 3.5 parts of coral stone, 1.7 parts of obsidian, 0.04 parts of citrine, 3.6 parts of medical stone, and 3.9 parts of calcium gluconate , 0.5 parts of meteorites, 0.013 parts of zinc glutamate, and 0.27 parts of keels Weigh the materials and mix them thoroughly; then grind them with a grinder at a temperature of 545°C to obtain energy powder of 2000 mesh to 6000 mesh;

[0036] 3) 22.7 parts of energy powder of 2000 mesh to 6000 mesh and 710 parts of traditional bottom glaze raw materials are weighed in parts by weight and ground together in a grinder to obtain the bo...

Embodiment 3

[0039] 1) The composition of surface glaze raw materials by weight includes 450 parts of kaolin, 100 parts of clay, 80 parts of talc, 50 parts of feldspar, 60 parts of dolomite, 10 parts of zinc oxide, and 10 parts of colorant. Weigh the materials and mix them for later use;

[0040] 2) The composition of energy powder by weight is: 10.6 parts of diamond medicine stone, 5.0 parts of black tourmaline, 2.4 parts of lapis lazuli, 6.8 parts of coral stone, 3.4 parts of obsidian, 0.10 parts of citrine, 6.8 parts of medical stone, and 7.6 parts of calcium gluconate , 1.0 parts of meteorites, 0.022 parts of zinc glutamate, and 0.46 parts of keels Weigh the materials and mix them thoroughly; then use a grinder to grind at a temperature of 540 ° C to obtain energy powder of 2000 mesh to 6000 mesh;

[0041] 3) 22.2 parts of 2000-6000-mesh energy powder and 800 parts of traditional bottom glaze raw materials are weighed by weight and ground together in a grinder to obtain the bottom glaze...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an active ceramic and a preparation method thereof, and belongs to the field of articles for daily life. The active ceramic is characterized by comprising a bottom blank layer, a ground glaze layer and an overglaze layer. The ground glaze layer and/or the overglaze layer comprises energy powder added in a raw glaze raw material and/or a glaze frit, and a certain amount of auxiliary materials consisting of calcium gluconae, stone needle, zinc glutamate and Os Draconis which are matched with various raw mineral materials are added in the energy powder. The activity of the energy powder can be stimulated well, and coordinated and unified comprehensive energy field can be formed by energy fields of the energy powder. The preparation method is characterized in that the specific temperature, which is 520-580 DEG C, in a grinding process of the added energy powder is kept, when the energy powder is ground at the temperature, the various materials are ground and mixed under the specific stimulating state of the energy fields of the various materials, and therefore, a high field effect is shown in a final ceramic product.

Description

technical field [0001] An active ceramic and a preparation method thereof belong to the field of daily necessities. Background technique [0002] It is now known that many ores can produce energy fields that have a certain effect and influence on the physiological functions of organisms. This energy field includes the magnetic field and infrared rays emitted by the mineral itself, and its specific mechanism of action is still unclear. But the positive impact on the human body does exist objectively. The effect that this substance can have an effect on the biological function is collectively referred to as the energy field effect or the field effect for short in the present invention. Now there are more products using this energy field effect to prepare medical and health care products. [0003] Ceramic materials are widely used as traditional sintered materials, not only for architectural decoration, but also for daily life, such as water cups, water cup liners, pots, mass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B41/86
CPCC03C8/20C04B41/5022C04B41/86C04B41/0072
Inventor 荆玉松
Owner 青岛首创嘉业工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap