Lithium ferric manganese phosphate-tungsten disulfide nanometer lithium cell positive material and preparation method thereof

A technology of lithium iron manganese phosphate and tungsten disulfide, which is applied in battery electrodes, batteries, nanotechnology and other directions, can solve the problems of poor cycle stability, low temperature stability, and high temperature stability of layered manganese oxide lithium structure, and achieves charging and discharging. Stable circulation structure, excellent high and low temperature resistance, buffer volume expansion effect

Active Publication Date: 2017-02-22
HENAN LI POWER SUPPLY
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the defects of low electrical conductivity, poor low-temperature stability, and low capacitance in the existing olivine-type lithium iron phosphate as the positive electrode material of lithium-ion batteries, and the defects of poor cycle stability and high-temperature stability of the layered manganese oxide lithium structure, the present invention provides A lithium iron manganese phosphate-tungsten disulfide nanosheet lithium battery cathode material. The two-dimensional structure of the tungsten disulfide nanosheet layer structure provides a short-distance open channel for lithium ion intercalation and deintercalation. It has high electrical conductivity and high and low temperature resistance. Excellent performance, high capacitance density, effective buffer volume expansion of the battery structure, improved cycle stability and high rate performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ferric manganese phosphate-tungsten disulfide nanometer lithium cell positive material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) The molar ratio of lithium hydroxide, ferric chloride and phosphoric acid Li:Fe:P= 1:0.99:1.08 is mixed and dissolved in water, and the molar ratio of the amount of water to the lithium atom in the lithium compound used is 30:1, Stir and disperse at a high speed of 1400rpm in a high-speed mixer for 5min to form a lithium iron phosphate precursor;

[0035] (2) Mix manganese dioxide, manganese tetroxide and lithium carbonate in a molar ratio of manganese dioxide: manganese tetroxide: lithium carbonate = 1:0.4:0.92, and stir at a high speed of 1400rpm in a high-speed mixer Disperse for 3min to obtain manganese oxide lithium precursor;

[0036] (3) At room temperature, first mix sodium tungstate, hydroxylamine hydrochloride and thiourea in a molar ratio of sodium tungstate:hydroxylamine hydrochloride:thiourea=1:1.5:3, add a certain amount of surfactant trimethyl ten Hexaalkylammonium bromide, reacted at a constant temperature of 100 °C for 10 hours, and slowly grown to o...

Embodiment 2

[0042] (1) Mix and dissolve lithium acetate, ferric chloride and ammonium phosphate in a molar ratio Li:Fe:P= 1:1:1 in water, and the molar ratio of the amount of water to the lithium atom in the lithium compound used is 100:1 , in a high-speed mixer at a speed of 2000rpm for high-speed stirring and dispersing for 5min to form a lithium iron phosphate precursor;

[0043] (2) Mix manganese dioxide, manganese tetroxide and lithium carbonate in a molar ratio of manganese dioxide: manganese tetroxide: lithium carbonate = 1:0.5:1, and stir at a high speed of 5000rpm in a high-speed mixer Disperse for 5min to obtain manganese oxide lithium precursor;

[0044] (3) At room temperature, first mix sodium tungstate, hydroxylamine hydrochloride and thiourea in a molar ratio of sodium tungstate: hydroxylamine hydrochloride: thiourea = 1:2:3, add a certain amount of surfactant dodecyl Sodium sulfonate, react at 150 ℃ constant temperature for 8 hours to obtain tungsten disulfide nanosheets;...

Embodiment 3

[0050] (1) Mix and dissolve lithium nitrate, ferric sulfate, and ammonium dihydrogen phosphate in a molar ratio Li:Fe:P= 1:1.03:1.08 in water, and the molar ratio of the amount of water to the lithium atom in the lithium compound used is 300: 1. Stir and disperse at a high speed of 1400rpm in a high-speed mixer for 3min to form a lithium iron phosphate precursor;

[0051] (2) Mix manganese dioxide, manganese tetroxide, and lithium carbonate in a molar ratio of manganese dioxide: manganese tetroxide: lithium carbonate = 1:0.8:0.92, and stir at a high speed of 5000rpm in a high-speed mixer Disperse for 4min to obtain manganese oxide lithium precursor;

[0052] (3) At room temperature, firstly mix sodium tungstate, hydroxylamine hydrochloride and thiourea in a molar ratio of sodium tungstate: hydroxylamine hydrochloride: thiourea = 1: 1.5: 3.5), and add a certain amount of surfactant polyethylene glycol Alcohol 400, reacted at a constant temperature of 200 °C for 8 hours to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application provides lithium ferric manganese phosphate-tungsten disulfide nanometer lithium cell positive material and preparation method thereof, the method, in the process of lithium ferric manganese phosphate formation by lithium iron phosphate and lithium manganese oxide, creatively draws support from the induction of layer construction of lithium manganese oxide and two dimension construction tungsten disulfide nanometer, and forms stratiform lithium ferric manganese phosphate-tungsten disulfide nanometer lithium cell positive material. Two dimension construction tungsten disulfide nanometer stratiform construction supplies short distance open tunnel for lithium ion intercalation and deintercalation, possesses high electric conductivity rate, good high-low temperature resistance, and large electric capacity intensity, buffers effectively the volume expansion of cell construction, enhances cycling stability and rate discharge capability.

Description

technical field [0001] The invention relates to the field of battery materials, in particular to a lithium iron manganese phosphate-tungsten disulfide nanosheet electrode material and a preparation method. Background technique [0002] The development and application of electric vehicles can effectively alleviate the energy crisis and environmental pollution. Lithium-ion batteries are considered to be the most likely high-performance batteries to meet the needs of electric vehicles and hybrid electric vehicles in today's society due to their high energy density, long service life, and no pollution to the environment. Lithium-ion battery is a new type of secondary energy storage battery developed in the 1990s. It is widely used in mobile phones, notebook computers, video cameras, digital cameras, electric automotive and other fields. [0003] In the industrialization promotion of lithium-ion batteries, the requirements for battery capacity, safety and comprehensive cost ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/58B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00H01M4/5815H01M4/5825H01M2220/20Y02E60/10
Inventor 陈庆曾军堂王镭迪
Owner HENAN LI POWER SUPPLY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com