Removable hot-melt pressure-sensitive adhesive and preparation method

A hot-melt pressure-sensitive adhesive and pressure-sensitive adhesive technology, used in adhesives, film/sheet adhesives, adhesive additives, etc., can solve the problems of tearing off the rubber sleeve, large peeling force, and inability to open normally and repeatedly. , to achieve the effect of easy peeling, good die-cutting and good retention

Active Publication Date: 2017-01-11
河北方大新材料股份有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since water-based sealing adhesives are limited in PE or PP film products, hot-melt pressure-sensitive adhesives can also be coated on both sides of the substrate, but the existing sealing tapes of the same type of adhesives cannot work normally after the adhesive strips are placed. The problem that the rubber sleeve will be torn off after repeated opening and the peeling force is slightly large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Removable hot-melt pressure-sensitive adhesive and preparation method
  • Removable hot-melt pressure-sensitive adhesive and preparation method
  • Removable hot-melt pressure-sensitive adhesive and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the above-mentioned hot-melt pressure-sensitive adhesive is carried out according to the following steps:

[0025] a. Weigh the components of the raw materials according to the formula, take dioctyl terephthalate, liquid petroleum resin, antioxidant 1076 and antioxidant 168 and put them into the reactor, heat and stir, and pour into the reactor while stirring Introduce nitrogen for protection to prevent aging and degradation of raw materials;

[0026] b. When the heating temperature reaches 135±5°C, slowly add SIS and 1 / 3 of the amount of C5 petroleum resin, and stir for 5 minutes; continue to stir and heat to 165±5°C, and keep the temperature at 25 rpm Stir for 120 minutes; keep the temperature range of 165±5°C because if the temperature is too low, it will cause incomplete melting and SIS agglomeration; if the temperature is too high, it will cause thermal oxidation and degradation at high temperature due to unsaturated double bonds in SIS ,...

Embodiment 1

[0038] The hot-melt pressure-sensitive adhesive is prepared according to the following formula in units of parts by mass in kg.

[0039] Formulation list of table 1 hot-melt pressure-sensitive adhesive

[0040]

[0041]

[0042] The preparation method of hot melt pressure sensitive adhesive is as follows:

[0043] a. take each component by the proportioning ratio of embodiment 3, get dioctyl terephthalate (DOTP), liquid petroleum resin, antioxidant 1076 and antioxidant 168 and all drop in the reactor, stir and heat, At the same time, nitrogen protection was introduced.

[0044] b. When the heating temperature reaches 135°C, slowly add 1 / 3 part of C5 petroleum resin 3200, which is 11kg and all SIS 1105, and stir for 5 minutes; continue to stir and heat to 165°C, and stir with temperature control (25 rpm minutes) 120 minutes;

[0045] c. Add polyethylene wax and UV531 under the condition of temperature control and stirring, and add the remaining C5 petroleum resin in 2 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a removable hot-melt pressure-sensitive adhesive and belongs to the technical field of adhesives. The pressure-sensitive adhesive is prepared from raw materials in parts by mass as follows: 35-45 parts of matrix resin, namely, a styrene-isoprene-styrene triblock copolymer, 30-40 parts of a tackifier, namely, C5 petroleum resin, 8-13 parts of a softener, namely, dioctyl terephthalate, 3-8 parts of a peel strength modifier, namely, polyethylene wax, 7-15 parts of a viscosity modifier, namely, liquid petroleum resin, 0.6-1.4 parts of an antioxidant and 0.4 parts of an ultraviolet absorbent. An adhesive tape prepared from the pressure-sensitive adhesive can be peeled and pasted repeatedly, and the adhesive cannot be transferred after the pressure-sensitive adhesive is pasted with paper, PE films, PP films and the like. The pressure-sensitive adhesive meets the environmental protection requirement of European Union REACH and RoHS on the basis of detection of specialized agencies and can completely meet the requirement of production of sealing labels, labels and removable adhesive bags.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a hot-melt pressure-sensitive adhesive suitable for labels, adhesive bags, sealing labels and the like. Background technique [0002] Sealing tape is mainly used for sealing plastic bags such as envelopes, stationery, and clothing. The sealing adhesives mainly include hot-melt pressure-sensitive adhesive sealing adhesives, oil-based sealing adhesives and water-based sealing adhesives. The earliest oil-based sealing adhesives generally use toluene as solvents, and the main raw materials are rubber, terpene resin, rosin, etc., which have a strong smell and cause great damage to the operators; the water-based sealing adhesives developed in the past ten years are those that will The main raw materials such as polymers and water-soluble resins are dissolved in solvent water, and the odor is small. However, due to the energy consumption of drying water, and most PE and PP films are n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J153/02C09J11/08C09J11/06C09J7/02
CPCC08L2205/025C08L2205/035C09J11/06C09J11/08C09J153/02C09J2301/124C09J2301/312C09J2301/408C08L57/02C08L23/06C08K5/00C08K5/12C08K5/1345C08K5/526C08K5/132
Inventor 杨志杜中泰
Owner 河北方大新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com