Cr1-series hot work die steel and heat treatment method thereof

A technology of hot work die steel and heat treatment method, applied in the field of iron-based alloys, which can solve the problems of easy cracking, poor thermal strength and wear resistance of 5CrNiMo die steel, etc.

Active Publication Date: 2016-12-14
YINGKOU SPECIAL STEEL FORGING
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] 5CrNiMo and 5CrNiMoV are the main mold materials in the current industry (GB / T11880-89 Die Forging Hammer and Large Mechanical Forging Machine Module Technical Specifications); GB1299-2000 Alloy Tool Steel; "my country's Hot Work Die Steel Performance Dataset", Zhu Zongyuan , Mechanical Engineering Materials, Volume 25, Issue 12, P12; Among them, 5CrNiMo die steel has poor thermal strength and wear resistance
my country has developed 45Cr2NiMoVSi (45Cr2), 5Cr2NiMoVSi (5Cr2), 3Cr2MoVNi (B2) and 3Cr2MoWVNi (B3) (JBT8431-1996 "Hot Forging Forming Die Steel and Its Heat Treatment Technical Conditions") and other large-section hot-working die steels, which are compatible with 5CrNiMo Compared with 45Cr2 and 5Cr2 steel, the hardenability, high temperature strength and thermal stability are improved, while the impact toughness is equivalent, and the thermal wear resistance and thermal fatigue resistance are also better than 5CrNiMo, but 45Cr2 and 5Cr2 are easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cr1-series hot work die steel and heat treatment method thereof
  • Cr1-series hot work die steel and heat treatment method thereof
  • Cr1-series hot work die steel and heat treatment method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0100] The preparation method of Cr1 series hot working die steel is characterized in that it comprises steps: electric furnace smelting, LF furnace refining (LADLE FURNACE is the ladle refining furnace), vacuum degassing (VD), die casting, annealing, electroslag remelting (ESR ), slow cooling, annealing, forging, normalizing, high temperature tempering, hydrogen expansion, roughing, inspection, finishing, quenching and tempering, finishing, inspection, and put into production to obtain modules or molds.

[0101] By controlling the composition of molten steel, the prepared die steel contains C0.43%, Si0.23%, Mn0.90%, P0.003%, S0.001%, Cr0.93%, Ni1. 41%, Mo1.03%, V0.16%, Al0.020%, Nb0.03%, the balance Fe. and inevitable inclusions.

Embodiment 2

[0103] The method of smelting is with embodiment 1. By controlling the composition of molten steel, the prepared mold steel contains 0.44% C, 0.36% Si, 0.88% Mn, 0.007% P, 0.002% S0, 0.93% Cr, 1.54% Ni, Mo1. 45%, V 0.17%, Al 0.030%, Nb 0.039%, the balance of Fe and inevitable inclusions.

Embodiment 3

[0105] The mold was prepared by heat treatment with the steel of Example 2YD1, and the specification was: 1000×910×270.

[0106] The heat treatment process is:

[0107]S1 Quenching: Furnace at ≤680°C, keep isothermal at 680°C, the isothermal time is calculated according to the effective size of the workpiece (the same below) as 0.6min / mm, and the temperature rises to 890-930°C with the furnace, and the holding time is 1.2min / mm Calculate, the oil is cooled for 60-70 minutes, and tempered immediately after cooling to 150-180 °C after the oil is released;

[0108] S2 Primary tempering: Furnace at ≤280°C, keep at 280°C and the isothermal time is calculated as 0.6min / mm, (under laboratory conditions, the temperature of Φ25mm samples is usually 10-50°C higher than that under industrial conditions) and heat up to 540~ 640°C, the holding time is calculated according to 2.4min / mm, oil cooling until the surface temperature is 100-150°C and then cooling (there are various cooling metho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact toughnessaaaaaaaaaa
Longitudinal impact workaaaaaaaaaa
Lateral impact energyaaaaaaaaaa
Login to View More

Abstract

The invention provides Cr1-series hot work die steel. The Cr1-series hot work die steel is characterized by comprising, by weight, 0.40%-0.48% of C, 0.17%-0.40% of Si, 0.80%-1.20% of Mn, 0-0.020% of P, 0-0.010% of S, 0.80%-1.60% of Cr, 1.00%-1.70% of Ni, 0.80%-1.60% of Mo, 0.05%-0.30% of V, 0.010%-0.050% of Al, 0.02%-0.20% of Nb and the balance Fe. According to the chemical component formula of the novel Cr1-series hot work die steel, the material name is YD1. Compared with existing Cr1-series (5CrNiMo and 5CrNiMoV) hot work die steel, the YD1-series die steel reduces the content of carbon, the contents of the Mn and Cr are increased, the content of the Mo is greatly increased, the content of the Ni is slightly decreased, and the Nb element and Al element are added. Hence, high-temperature strength and creep resistance are improved, and toughness is also improved.

Description

technical field [0001] The invention belongs to the field of iron-based alloys, and in particular relates to an alloy used for forging dies and its preparation and application. Background technique [0002] 5CrNiMo and 5CrNiMoV are the main mold materials in the current industry (GB / T11880-89 Die Forging Hammer and Large Mechanical Forging Machine Module Technical Specifications); GB1299-2000 Alloy Tool Steel; "my country's Hot Work Die Steel Performance Dataset", Zhu Zongyuan , Mechanical Engineering Materials, Volume 25, Issue 12, P12; among them, 5CrNiMo die steel has poor thermal strength and wear resistance. There are few varieties of forging die materials in my country, and the most widely used are 5CrNiMo, 5CrNiMoV, 4Cr2MoVNi (B2) in GB / T11880-89; , low, low, lack of varieties with intermediate hardness, 5Cr2NiMoVSi in GB / T11880-89 is a variety with moderate hardness, but it is not widely used because of its high brittleness and easy cracking. Therefore, it is necessa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/18C22C38/08C22C38/12C22C38/06C21D1/18
CPCC21D1/18C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/18
Inventor 潘孝忠于成文
Owner YINGKOU SPECIAL STEEL FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More