Preparation method of bimetallic composite plate
A bimetallic and composite plate technology, applied in chemical instruments and methods, lamination devices, lamination auxiliary operations, etc., can solve the problems of weak diffusion ability of metal atoms, low melting point of magnesium alloy, low interface strength, etc., and achieve the goal of inhibiting element Long-range diffusion, high interfacial bonding strength, and the effect of improving interfacial bonding strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0024] The preparation method of the high-strength bimetal composite plate of the present invention comprises the following steps:
[0025] Ⅰ. Pre-treatment of raw materials: the base material and the composite material are processed and leveled separately, and then polished to remove burrs and flashes;
[0026] Ⅱ. Coating of release agent: apply release agent on one side of the composite material;
[0027] Ⅲ. Coating of infiltration agent: apply infiltration agent on one side of the substrate and at least one side of the composite material not coated with release agent;
[0028] Ⅳ. Blank assembly: Symmetrical blank assembly in the form of base material-composite material-composite material-base material or base material-metal transition layer-composite material-composite material-metal transition layer-base material, and then weld around the blank Combining and vacuuming to obtain a combined blank; wherein, the two sides of the composite material coated with the release agen...
Embodiment 1
[0041] Prepare the titanium-steel clad plate with nickel as the intermediate layer, and its preparation method is as follows:
[0042] Ⅰ The Q235 steel base material and the TA2 titanium composite material are respectively processed on a lathe to be flattened, and polished to remove burrs and flashes. Leveling and cleaning the nickel metal transition layer. The thickness of the Q235 steel substrate is 10mm, the thickness of the TA2 titanium composite material is 3mm, and the thickness of the nickel transition layer is 1mm.
[0043]Ⅱ Coating release agent on one side of two TA2 titanium composites.
[0044] Ⅲ Coat the penetrating agent on the side of the TA2 titanium composite material that is not coated with the release agent. Osmotic agent is 5% Y 2 o 3 , 2% NaF and 1.5% NH 4 Cl, 40% titanium metal powder and 51.5% nickel powder.
[0045] Ⅳ According to the method of Q235 steel base material-nickel transition layer-TA2 titanium composite material-TA2 titanium composite ...
Embodiment 2
[0051] Prepare aluminum-magnesium composite board, its preparation method is as follows:
[0052] Ⅰ The AZ31B magnesium alloy and the 5052 aluminum alloy are respectively processed on a lathe to be flattened and polished to remove burrs and flashes. 5052 aluminum alloy is 5mm thick, and AZ31B magnesium alloy is 2mm thick.
[0053] Ⅱ Coating release agent on one side of two AZ31B magnesium alloys.
[0054] Ⅲ Apply infiltration agent on the side of AZ31B magnesium alloy that is not coated with release agent. Osmotic agent is 2% Y 2 o 3 ,1%LaCl 3 , 2.5% NaF and 0.5% NH 4 Cl, 47% magnesium powder and 47% aluminum powder.
[0055] ⅣAccording to the way of 5052 aluminum alloy-AZ31B magnesium alloy-AZ31B magnesium alloy-5052 aluminum alloy magnesium alloy, the billets are assembled symmetrically. Then the surroundings of the blank are welded and evacuated to obtain a combined blank, and the vacuum degree of 0.1Pa exceeds that of the claim and is less than 1×10 -2 Pa range. W...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap