Wear-proof and anti-seismic tile and preparation method thereof

A technology for ceramic tiles and waste clay bricks, which is used in the production of clay products, other household appliances, and ceramic materials. and thermal stability, long service life

Inactive Publication Date: 2016-11-09
安徽省亚欧陶瓷有限责任公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of my country's construction industry and the continuous improvement of people's living standards, people have increasingly stringent requirements on the performance of ceramic tiles, and the wear resistance and earthquake resistance of existing ceramic tiles are increasingly unable to meet the needs of the existing market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A wear-resistant and anti-seismic ceramic tile made of the following raw materials in weight (kg): waste clay brick 30, marine dredging mud 27, yellow phosphorus slag 26, halloysite 22, Benshan green clay 24, leucite 29, volcano Stone 25, metallurgical waste slag 32, periclase 34, brown corundum slag 24, aluminum diboride 13, dihydrate gypsum 20, diamond grinding wheel waste 22.

[0015] A method for preparing wear-resistant and shock-resistant ceramic tiles, comprising the following steps:

[0016] (1) Mix yellow phosphorus slag, halloysite, brown corundum slag, and volcanic rock, pulverize, pass through a 150-mesh sieve, add an appropriate amount of water and stir to make a 55% slurry, grind at a speed of 4000r / min for 20min, Then the slurry after the ball milling is sent to spray granulation in the spray drying granulator with a pressure of 0.25Mpa. Pass the obtained particles through a 150-mesh sieve, then calcinate at 905°C for 3 hours, and cool to room temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-proof and anti-seismic tile and a preparation method thereof. The tile is prepared from raw materials in parts by weight as follows: 25-35 parts of waste clay bricks, 22-33 parts of marine dredged mud, 19-31 parts of yellow phosphorus slag, 14-26 parts of indianite, 18-30 parts of Huanglong mountain green mud, 23-34 parts of leucite, 16-28 parts of vesuvianite, 24-36 parts of metallurgy waste residues, 27-39 parts of periclase, 17-29 parts of brown fused alumina residues, 8-16 parts of aluminum diboride, 15-25 parts of dihydrate gypsum and 18-26 parts of diamond grinding wheel wastes. The added diamond grinding wheel wastes, waste clay bricks and other raw materials can improve the wear resistance and the weather resistance of the tile, the added brown fused alumina residues, aluminum diboride and other raw materials can improve the anti-seismic property and the heat stability of the tile. The prepared tile has the advantages of being high in mechanical strength, wear-proof, anti-seismic, resistant to high temperature, weather-resistant, ageing-resistant and the like and is long in service life and good in environmental suitability.

Description

technical field [0001] The invention relates to a tile and a preparation method thereof, in particular to a wear-resistant and earthquake-resistant tile and a preparation method thereof. Background technique [0002] The development of my country's modern ceramic tile industry originated in the 20th century. At first, there was a single variety of ceramic tile products, only interior wall tiles (commonly known as tiles), with a small output and a low degree of automation. Later, mosaic tiles, acid-resistant bricks, Glazed tiles and other products. Since the 1980s, the ceramic tile industry began to develop rapidly, and now the industry has become a major force in building materials. Ceramic tile products have been widely used in homes, commercial buildings and public facilities, and the products have also shown multi-functionality. , multi-color varieties, multi-decorative effect development trend. With the rapid development of my country's construction industry and the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/132C04B33/135C04B33/138
CPCC04B33/13C04B33/132C04B33/1321C04B33/1324C04B33/135C04B33/138C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3472C04B2235/3804C04B2235/96Y02P40/60
Inventor 郑辉郭孝建王俊武
Owner 安徽省亚欧陶瓷有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products