A kind of water-soluble silicone coating

A silicone coating, water-soluble technology, applied in the direction of fire-resistant coatings, coatings, etc., can solve the problems of poor thermal hardness and other physical properties, and achieve the effects of high wear resistance, avoiding agglomeration, and good thermal hardness

Active Publication Date: 2018-05-18
FOSHAN POLIMA ADVANCED TECH & SUPPLIES CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The water-based paint prepared by the invention has a good decorative effect, but the thermal hardness and other physical properties are relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-soluble silicone coating
  • A kind of water-soluble silicone coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Preparation of water-based silicone resin: Add 20g of trihydric alcohol, 30g of dihydric alcohol, 35g of dibasic acid and 15g of epoxy resin into the reactor, heat it to 170°C, and add 0.4g of phosphoric acid after the material is dissolved and kept for 1 hour Triphenyl ester, control the temperature at 200°C, react until the acid value is less than 8.0, add 75g of methylphenyl silicone resin intermediate, 0.5g of tetrabutyl titanate to react, the reaction temperature is 180°C, and the reaction time is 4 Hours, when the reaction acid value is lower than 8mgKOH / g, dropwise add 5g of trimellitic anhydride to carry out water-based capping, keep the reaction temperature, react for 2 hours, when the acid value is 25 ± 10mgKOH / g, the reaction is completed, and water-based silicone resin A is prepared.

[0046] Preparation of water-soluble silicone coating: 70g of water-based silicone resin A, 4g of nano-silica (a powder with a particle size of 200 nanometers) was blended for 1...

Embodiment 2

[0048] Preparation of water-based silicone resin: Add 25g of trihydric alcohol, 25g of dihydric alcohol, 40g of dibasic acid and 10g of epoxy resin into the reactor, heat it to 170°C, and add 0.3g of phosphoric acid after the material is dissolved and kept for 1 hour Triphenyl ester, control the temperature at 200°C, react until the acid value is less than 8.0, add 75g of methylphenyl silicone resin intermediate, 0.5g of tetrabutyl titanate to react, the reaction temperature is 180°C, and the reaction time is 4 Hours, when the reaction acid value is lower than 8mgKOH / g, dropwise add 5g of trimellitic anhydride to carry out water-based capping, keep the reaction temperature, react for 2 hours, when the acid value is 25 ± 10mgKOH / g, the reaction is completed, and the water-based silicone resin B is prepared.

[0049] Preparation of water-soluble silicone coating: 75g of water-based silicone resin B and 1g of nano-silica (a powder with a particle size of 200 nm) were blended at a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a water-soluble organic silicon coating which comprises aqueous organic silicon resin, nano silicon dioxide, titanium dioxide, an additive and the balance of water, wherein the weight ratio of the aqueous organic silicon resin to the nano silicon dioxide to the titanium dioxide to the additive is (70-80):(1-5):(0.5-1):(5-20), wherein the nano silicon dioxide is powder of which the average particle size is 100-300 nanometers; the fineness of the titanium dioxide is greater than 6000 meshes; and the aqueous organic silicon resin is modified by using polyester and epoxy resin and has the acid value of 25+ / -10mgKOH / g. The prepared water-soluble organic silicon coating is relatively high in thermal hardness.

Description

technical field [0001] The invention belongs to the field of water-based paints, in particular to a water-soluble silicone paint. Background technique [0002] Silicone resin is a polyorganosiloxane with a highly cross-linked network structure, which has the dual characteristics of organic resin and inorganic materials, and has unique physical and chemical properties. Silicone resin is one of the four major organosilicon materials (organosilicon is mainly Divided into four categories: silicone oil, silicone rubber, silicone resin and silane coupling agent), it has high temperature resistance, weather resistance and chemical resistance that are difficult to achieve with general organic resins. The research work on silicone resins has progressed quite rapidly this year. The following results Has been used in industry. [0003] In recent years, due to the deterioration of the ecological environment, environmental protection has attracted more and more attention from the world....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D187/00C09D7/61C08G81/00
CPCC08G81/00C08K3/22C08K3/36C08K13/02C08K2003/2241C08K2201/011C09D5/18C09D7/61C09D187/00C08L1/284
Inventor 曾志玲梁文波
Owner FOSHAN POLIMA ADVANCED TECH & SUPPLIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com