Bentonite-modified mould-proof cardboard and preparation method thereof

A cardboard and soil reform technology, applied in the field of cardboard, can solve the problems of product quality decline, reduction of mechanical strength of carton boxes, and damage to the waterproof effect of coating layer.

Active Publication Date: 2016-09-07
铜陵锋帆彩色印务股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mildew will not only damage the waterproof effect of the paint layer and reduce the mechanical strength of the carton, but also cause a decline in the quality of the products inside the carton.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] The invention provides a method for preparing bentonite-modified mildew-proof cardboard, comprising:

[0017] 1) The process of decocting Chinese herbal medicines in water to obtain Chinese herbal medicine extracts;

[0018] 2) In the presence of ultraviolet rays, the process of performing activation treatment with bentonite, plant ash, sodium chloroplatinate and molybdenum disulfide to obtain an activated product;

[0019] 3) Under acidic conditions, the process of mixing the activator with the amino acid and performing modification treatment to obtain the modified activator;

[0020] 4) Conduct a contact reaction of acrylic emulsion, polystyrene, dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and then add emulsifiers, modified activators, and Chinese herbal medicine extracts to the reaction system The process of mixing the liquid to make the anti-mildew coating;

[0021] 5) The process of applying the anti-mold coating to the surface of the car...

Embodiment 1

[0035] 1) Put Artemisia argyi, Peucedanum, Campanulaceae, Fried Perilla, Chuanxiong, Codonopsis, Angelica, Pueraria, Golden Boil, Coptidis, and water according to 100:55:68:58:32:95:39:28:68:92: 500 weight ratio, and decocting at 160°C for 5 hours to obtain Chinese herbal medicine extract;

[0036] 2) In the presence of ultraviolet rays with a wavelength of 230nm, mix bentonite, plant ash, sodium chloroplatinate and molybdenum disulfide in a weight ratio of 100:59:22:35, and perform activation treatment at 80°C for 14 hours to obtain an activated product;

[0037] 3) Under the condition of pH 5, the activated substance was mixed with amino acid (weight ratio 100:55) and modified at 55°C for 8 hours to obtain the modified activated substance;

[0038] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight: 5000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and mix them at 100°C and a vacuum of 8MPa The contact reaction was carried out fo...

Embodiment 2

[0042] 1) Put Artemisia argyi, Peucedanum, Platycodon grandiflorum, Fried perilla, Chuanxiong, Codonopsis pilosula, Angelica, Pueraria lobata, Coptis chinensis, Coptis chinensis, water according to 100:48:62:55:24:80:36:22:55:88: 400 weight ratio mixed, and decocted at 150 ° C for 4 hours to obtain the Chinese herbal medicine extract;

[0043] 2) In the presence of ultraviolet light with a wavelength of 200nm, mix bentonite, plant ash, sodium chloroplatinate and molybdenum disulfide in a weight ratio of 100:55:14:32, and perform activation treatment at 75°C for 12 hours to obtain an activated product;

[0044] 3) Under the condition of pH 4, the activated substance was mixed with amino acid (weight ratio 100:47) and then modified at 50°C for 6 hours to obtain the modified activated substance;

[0045] 4) Mix acrylic emulsion, polystyrene (weight-average molecular weight: 3000), dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite, and mix them at 95°C and a vacuum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bentonite-modified mould-proof cardboard and a preparation method thereof. The preparation method includes 1), decocting Chinese herbal medicines in water to obtain Chinese herbal medicine extract; 2), in the presence of ultraviolet rays, activating bentonite, plant ash, sodium chloroplatinate and molybdenum disulfide to obtain activators; 3), subjecting the activators and amino acids to modification under an acidic condition to obtain modified activators; 4), subjecting acrylic emulsion, polystyrene, dioctyl phthalate, aluminum oxide, boron nitride and sodium nitrite to contact reaction, and adding emulsifying agents, the modified activators and the Chinese herbal medicine extract into a reaction product with mixing to obtain a mould-proof coating; 5), applying the surfaces of a cardboard body with the mould-proof coating prior to drying so as to obtain the bentonite-modified mould-proof cardboard. The bentonite-modified mould-proof cardboard has the excellent mechanical, waterproof and antibacterial properties.

Description

technical field [0001] The invention relates to a cardboard, in particular to a bentonite-modified mildew-resistant cardboard and a preparation method thereof. Background technique [0002] Carton is currently the most common form of outer packaging for most products, and it is the first line of defense to protect product appearance, function, integrity, etc., and because water is the biggest culprit that causes damage to the appearance and function of many products, consumers are very concerned about cartons. Water resistance has extremely high requirements. [0003] The method of enhancing the waterproofness of cartons is mainly to add a waterproof coating layer on the surface of the carton, and the method of adding coating is mainly organic printing, manual brushing, spraying, etc. Existing waterproof coatings for cartons generally contain a large amount of macromolecules. After the cartons are used for a long time, the coating layer on the surface of the cartons will be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/10D21H21/14D21H19/64
CPCD21H19/64D21H21/14D21H27/10
Inventor 解和锋沐磊
Owner 铜陵锋帆彩色印务股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap