Preparation method for chlorinated polyethylene/polyvinyl chloride composite foaming material

A technology of chlorinated polyethylene and polyvinyl chloride, which is applied in the field of preparation of chlorinated polyethylene/polyvinyl chloride composite foaming materials, can solve the problems of uneven distribution of cells, wide range of pore sizes, and low strength, and achieve The effect of low density, easy operation and increased strength

Inactive Publication Date: 2016-09-07
仇颖莹
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem mainly solved by the present invention: aiming at the problems that the currently commonly used polyvinyl chloride foaming material has high density, the polyvinyl chloride foaming material prepared by the existing method has a wide pore size range, uneven cell distribution and low strength, Provides a polyvinyl chloride absorbs dioctyl phthalate to swell to make it soft and elastic, then blends with crosslinking agent dicumyl oxide and stearyl acrylate, and adds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0020] First, weigh 95 parts of polyvinyl chloride, 55 parts of dioctyl phthalate, and 5 parts of zinc oxide in parts by mass. After fully mixing, they are placed in a drying oven at 75°C for swelling until the mixture is Soft, to obtain pre-swelled polyvinyl chloride; then put the above-mentioned pre-swelled polyvinyl chloride into the internal mixer for plasticization for 3min, the temperature of the mixing room is 140°C, the rotor speed is 60r / min, and then 100 parts of chlorine Polyethylene, 0.5 parts of dicumyl peroxide, 5 parts of stearyl acrylate and 5 parts of nano-calcium carbonate were added to the internal mixer, mixed for 7 minutes, and the temperature of debinding was controlled at 170 ° C, discharged, cooled to room temperature, and obtained Chlorinated polyethylene / polyvinyl chloride masterbatch; Next, put the above-mentioned chlorinated polyethylene / polyvinyl chloride masterbatch on a flat vulcanizing machine, heat it in a mold at 185°C, press it for 10min under...

example 2

[0023] First, weigh 98 parts of polyvinyl chloride, 58 parts of dioctyl phthalate, and 5.5 parts of zinc oxide in parts by mass. After fully mixing, they are placed in a drying oven at 78°C for swelling until the mixture is Soft and soft to obtain pre-swelled polyvinyl chloride; then put the above-mentioned pre-swelled polyvinyl chloride into the mixer for plasticization for 4min, the temperature of the mixing room is 143°C, the rotor speed is 65r / min, and then 105 parts of chlorine Polyethylene, 0.55 parts of dicumyl peroxide, 5.5 parts of stearyl acrylate and 5.5 parts of nano-calcium carbonate were added to the internal mixer, mixed for 8 minutes, and the temperature of debinding was controlled at 175 ° C, discharged, cooled to room temperature, and obtained Chlorinated polyethylene / polyvinyl chloride masterbatch; Next, put the above chlorinated polyethylene / polyvinyl chloride masterbatch on a flat vulcanizer, heat it in a mold at 188°C, press it for 11 minutes under a press...

example 3

[0026] First, weigh 100 parts of polyvinyl chloride, 60 parts of dioctyl phthalate, and 6 parts of zinc oxide according to the number of parts by mass. After fully mixing, they are placed in a drying oven at 80°C for swelling until the mixture is Soft and soft to obtain pre-swelled polyvinyl chloride; then put the above-mentioned pre-swelled polyvinyl chloride into the internal mixer for plasticization for 5min, the temperature of the mixing room is 145°C, the rotor speed is 70r / min, and then 110 parts of chlorine Polyethylene, 0.6 parts of dicumyl peroxide, 6 parts of stearyl acrylate and 6 parts of nano-calcium carbonate were added to the internal mixer, mixed for 10 minutes, and the debinding temperature was controlled to be 180 ° C, discharged, cooled to room temperature, and obtained Chlorinated polyethylene / polyvinyl chloride masterbatch; Next, put the above-mentioned chlorinated polyethylene / polyvinyl chloride masterbatch on a flat vulcanizing machine, heat it in a mold ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a chlorinated polyethylene/polyvinyl chloride composite foaming material, which belongs to the technical field of foaming material preparation. In the present invention, polyvinyl chloride absorbs dioctyl phthalate and swells to make it soft and elastic, and then blends it with crosslinking agent dicumyl oxide and stearyl acrylate, and adds nucleating agents calcium carbonate, chlorine The chlorinated polyethylene/polyvinyl chloride masterbatch is obtained by cooling and discharging the chlorinated polyethylene/polyvinyl chloride masterbatch. The chlorinated polyethylene/polyvinyl chloride masterbatch is heated and formed in a mold, and then the non-polluting supercritical carbon dioxide is used as a physical foam agent, increase the expansion ratio, and generate uniform and fine cells, thereby obtaining the method of chlorinated polyethylene/polyvinyl chloride composite foam material. Examples prove that the reaction of the preparation process of the present invention is mild, and while maintaining the advantages of low cost and high flame retardancy, the density of the prepared chlorinated polyethylene/polyvinyl chloride composite foam material is the smallest, the cell distribution is uniform, and the strength is also high. has been significantly improved.

Description

technical field [0001] The invention discloses a preparation method of a chlorinated polyethylene / polyvinyl chloride composite foaming material, which belongs to the technical field of foaming material preparation. Background technique [0002] Polyvinyl chloride (PVC) is a general-purpose thermoplastic with excellent performance, and it is one of the plastic varieties with the largest output in my country. Polyvinyl chloride has the advantages of good flame retardancy, corrosion resistance, high mechanical strength, good electrical insulation, and low cost, but at the same time, it also has disadvantages such as poor light and heat stability, low impact strength, poor processing and forming performance, and high density. Therefore, various stabilizers, processing aids and impact modifiers must be added during the processing of PVC to improve its light / heat stability, processing performance and impact resistance. By adding foaming agent and processing aids to polyvinyl chlo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/28C08L27/06C08K13/02C08K5/12C08K3/22C08K5/14C08K3/26C08J9/12
CPCC08L23/286C08J9/122C08J2203/06C08J2323/28C08J2427/06C08K2201/011C08L2201/02C08L2203/14C08L2205/03
Inventor 仇颖莹张明王龙
Owner 仇颖莹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap