Epoxy self-leveling terrace paint

An epoxy, leveling technology, applied in the field of floor paint, can solve the problems of high substrate humidity and environmental humidity, low paint film compactness, small market share, etc., to achieve good fullness, good water solubility, surface Easier cleaning effect

Inactive Publication Date: 2016-08-31
SUZHOU KEMIAO NEW MATERIAL
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solvent-based floor coatings have high requirements for substrate humidity and environmental humidity during construction; solvent-free water-based floors do not have much requirements for substrate and environmental humidity. Storage, construction and other links are safer and more environmentally friendly. However, compared with solvent-based floor coatings, water-based floors have disadvantages such as low paint film density and poor workability, and their market share is small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The epoxy self-leveling floor paint of this embodiment includes the following components in parts by weight: 68 parts of water-based epoxy resin, 18 parts of copolycondensation resin, 5 parts of alkyl sulfate, 6 parts of octyl glycidyl ether, anatase nanometer 5 parts of titanium dioxide, 4.5 parts of epoxy curing agent, 2.4 parts of dodecylbenzene sulfonic acid, 4 parts of dodecyl alcohol ester, 4 parts of citric acid, 5 parts of epoxy dispersant, 4 parts of phenyl phthalate, 9 parts of polyvinyl acetate, 18 parts of acrylic emulsion, and 5 parts of oxidized polyethylene wax.

Embodiment 2

[0013] The epoxy self-leveling floor paint of this embodiment includes the following components in parts by weight: 74 parts of water-based epoxy resin, 26 parts of copolycondensation resin, 10 parts of alkyl sulfate, 8 parts of octyl glycidyl ether, anatase nanometer 8 parts of titanium dioxide, 6.5 parts of epoxy curing agent, 3.6 parts of dodecylbenzene sulfonic acid, 6 parts of dodecyl alcohol ester, 7 parts of citric acid, 9 parts of epoxy dispersant, 9 parts of phenyl phthalate, 15 parts of polyvinyl acetate, 24 parts of acrylic emulsion, 9 parts of oxidized polyethylene wax, and 14 parts of liquid rosin resin.

Embodiment 3

[0015] The epoxy self-leveling floor paint of this embodiment includes the following components in parts by weight: 68 parts of water-based epoxy resin, 18 parts of copolycondensation resin, 5 parts of alkyl sulfate, 6 parts of octyl glycidyl ether, anatase nanometer 5 parts of titanium dioxide, 4.5 parts of epoxy curing agent, 2.4 parts of dodecylbenzene sulfonic acid, 4 parts of dodecyl alcohol ester, 4 parts of citric acid, 5 parts of epoxy dispersant, 4 parts of phenyl phthalate, 9 parts of polyvinyl acetate, 18 parts of acrylic emulsion, 5 parts of oxidized polyethylene wax, 10 parts of liquid rosin resin, and 8 parts of acetylene black.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses epoxy self-leveling terrace paint. The terrace paint is prepared from, by weight, 68-74% of waterborne epoxy resin, 18-26 parts of co-condensed resin, 5-10 parts of alkyl sulfate, 6-8 parts of ethylhexyl glycidyl ether, 5-8 parts of anatase nanometer titanium dioxide, 4.5-6.5 parts of epoxy curing agent 2.4-3.6 parts of dodecylbenzene sulfonic acid, 4-6 parts of 2,2,4-Trimethyl-1,3-pentanediolmono(2-methylpropanoate), 4-6 parts of salicylic acid, 4-7 parts of citric acid, 5-9 parts of epoxy dispersion agent, 4-9 parts of salicylic acid phenyl ester, 9-15 parts of polyvinyl acetate, 18-24 parts of acrylic emulsion and 5-9 parts of oxidized polyethlene wax. The epoxy self-leveling terrace paint has the advantages of being good in water solubility, good in fullness and the like, guarantees high solid content and low viscosity of a product, and makes the product have good leveling performance. Meanwhile, the terrace paint is high in abrasion resistance and anti-fouling performance, application property is improved, the surface is easier to clean, no water stains are left, and market value is very good.

Description

technical field [0001] The invention relates to a floor paint, in particular to an epoxy self-leveling floor paint. Background technique [0002] Self-leveling floor paint was first invented in Germany in 1934. It is mainly made of oil, tree materials, colors, solvents, etc. It is mainly divided into decorative floor paint, heavy-duty floor paint, heavy-duty floor paint, etc. . Floor paint is made up of many different substances through many production processes such as mixing, dissolving, and dispersing. Floor paint has the characteristics of bright, real, beautiful, wear-resistant, waterproof, and anti-corrosion. Floor paint is made up of many different substances through many production processes such as mixing, dissolving, and dispersing. According to the different functions of each component of floor paint, it can generally be divided into main film-forming substances, secondary film-forming substances and auxiliary film-forming substances. Since the middle and late...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D133/00C09D131/04C09D5/16C09D7/12
CPCC08K2201/011C08L2205/035C09D5/1662C09D5/1687C09D7/61C09D7/63C09D7/65C09D163/00C08L101/00C08L31/04C08L33/00C08K13/02C08K2003/2241C08K5/092C08L93/04C08K3/04C08K3/26
Inventor 党斌
Owner SUZHOU KEMIAO NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products