A kind of toughened glass ink for inkjet printing and preparation method thereof
A tempered glass ink and inkjet printing technology, applied in ink, applications, household appliances, etc., can solve the problems of high consumption of raw materials and environmental pollution, low utilization rate of inorganic glazes, difficulty in making patterned products, etc., and achieve acid resistance Alkaline anti-ultraviolet radiation, good inkjet printing performance, strong acid and alkali resistance
Active Publication Date: 2019-04-30
广东道氏陶瓷材料有限公司
View PDF1 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, there are many disadvantages in the method of screen printing or roller printing: 1) the color and pattern of the texture are single, and it is difficult to make complex pattern products; The cost is high and does not meet the trend requirements of energy saving and environmental protection; 3) The production requires cumbersome processes such as film making, screen printing, and engraving, with long production cycles and low yields
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] .
Embodiment 2
[0026] .
Embodiment 3
[0028] .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
surface tension | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a tempered glass ink for ink-jet printing and a preparation method thereof. The ink is prepared from low-temperature frit, inorganic pigments, a dispersant, resin, a flatting agent and a solvent. The tempered glass ink for ink-jet printing has good stability, favorable ink-jet printing performance, low viscosity which ranges from 10.0 to 40.0mPa.s and can be regulated, uniform particle size distribution, the surface tension of 25 to 35mN / m, an average particle size of 200 to 400 nm and a maximum particle size of less than 1 micrometers, and can be stored for a long time. The ink prepared by the preparation method disclosed by the invention has low sintering temperature and can be well combined with glass. The sintered surface is strongly resistant to acid, alkaline and ultraviolet radiation.
Description
technical field [0001] The invention relates to a special ink, in particular to a tempered glass ink for inkjet printing and a preparation method thereof. Background technique [0002] Colored glazed glass is to print the ink made of inorganic glaze on the glass surface, then dry, temper or thermally process, and permanently sinter the glaze on the glass surface to obtain a wear-resistant, acid and alkali resistant glass. Decorative glass products. Colored glazed glass is usually decorated with inorganic glazes on the glass surface by screen printing or roller printing. After drying and heat treatment, a permanent and firm glaze layer is finally formed on the glass surface. However, there are many disadvantages in the method of screen printing or roller printing: 1) the color and pattern of the texture are single, and it is difficult to make complex pattern products; The cost is high and does not meet the trend requirements of energy conservation and environmental protecti...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/30C09D11/38
CPCC09D11/30C09D11/38
Inventor 彭晔石教艺李向钰
Owner 广东道氏陶瓷材料有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com