Preparation method of polyvinyl chloride hose

A technology of polyvinyl chloride and polyvinyl chloride resin, applied in the direction of tubular objects, applications, household appliances, etc., can solve the problems of large intermolecular force, dehydrochlorination reaction, high softening temperature and melting temperature of PVC, and achieve flame retardant performance Good, good oil resistance, long service life

Inactive Publication Date: 2016-08-17
ANHUI JIUHUA KIMRUN COPPER IND
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyvinyl chloride hose is made of polyvinyl chloride (PVC) resin. Pure polyvinyl chloride (PVC) resin belongs to a class of strong polar polymers. Its intermolecular force is relatively large, which leads to the softening temperature and melting temperature of PVC. The temperature is high, generally need 160-210 ℃ to process; the substituted chlorine group contained in the PVC molecule is easy to cause the dehydrochlorination reaction of PVC resin
At the same time, PVC hoses still have certain defects in high temperature resistance and oil resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A preparation method of a polyvinyl chloride hose, the polyvinyl chloride hose is composed of the following components by mass: 90 parts of polyvinyl chloride resin, 8 parts of dioctyl phthalate, 35 parts of tricresyl phosphate, stearic acid 1 part of lead, 1 part of calcium stearate, 0.1 part of stearic acid, 35 parts of nitrile rubber, 3 parts of modifier, 2 parts of tribasic lead sulfate, 1 part of chlorinated paraffin, 1 part of polyethylene wax, chlorine 2 parts of polyethylene, 3 parts of light calcium carbonate.

[0015] The preparation method of polyvinyl chloride hose, its preparation steps are as follows,

[0016] 1) First select polyvinyl chloride resin, dioctyl phthalate, tricresyl phosphate, lead stearate, calcium stearate, stearic acid, nitrile rubber, modifier, three Basic lead sulfate, chlorinated paraffin, polyethylene wax, chlorinated polyethylene, light calcium carbonate, and then placed in a high-speed mixer for mixing, the temperature is 100 ° C, a...

Embodiment 2

[0021] A preparation method of a polyvinyl chloride hose, the polyvinyl chloride hose is composed of the following components by mass: 110 parts of polyvinyl chloride resin, 15 parts of dioctyl phthalate, 45 parts of tricresyl phosphate, stearic acid 3 parts of lead, 3 parts of calcium stearate, 0.5 parts of stearic acid, 45 parts of nitrile rubber, 5 parts of modifier, 5 parts of tribasic lead sulfate, 3 parts of chlorinated paraffin, 3 parts of polyethylene wax, chlorine 5 parts of polyethylene, 8 parts of light calcium carbonate.

[0022] The preparation method of polyvinyl chloride hose, its preparation steps are as follows,

[0023] 1) First select polyvinyl chloride resin, dioctyl phthalate, tricresyl phosphate, lead stearate, calcium stearate, stearic acid, nitrile rubber, modifier, three Basic lead sulfate, chlorinated paraffin, polyethylene wax, chlorinated polyethylene, light calcium carbonate, and then placed in a high-speed mixer for mixing, the temperature is 120...

Embodiment 3

[0028] A preparation method of a polyvinyl chloride hose, the polyvinyl chloride hose is composed of the following components by mass: 100 parts of polyvinyl chloride resin, 10 parts of dioctyl phthalate, 40 parts of tricresyl phosphate, stearic acid 2 parts of lead, 2 parts of calcium stearate, 0.3 parts of stearic acid, 40 parts of nitrile rubber, 4 parts of modifier, 4 parts of tribasic lead sulfate, 2 parts of chlorinated paraffin, 2 parts of polyethylene wax, chlorine 3 parts of polyethylene, 5 parts of light calcium carbonate.

[0029] The preparation method of polyvinyl chloride hose, its preparation steps are as follows,

[0030] 1) First select polyvinyl chloride resin, dioctyl phthalate, tricresyl phosphate, lead stearate, calcium stearate, stearic acid, nitrile rubber, modifier, three Basic lead sulfate, chlorinated paraffin, polyethylene wax, chlorinated polyethylene, light calcium carbonate, and then placed in a high-speed mixer for mixing, the temperature is 110...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a polyvinyl chloride hose. The polyvinyl chloride hose is prepared from 90-110 parts of polyvinyl chloride resin, 8-15 parts of dioctyl phthalate, 35-45 parts of tritolyl phosphate, 1-3 parts of lead stearate, 1-3 parts of calcium stearate, 0.1-0.5 part of stearic acid, 35-45 parts of nitrile rubber, 3-5 parts of modifier, 2-5 parts of tribasic lead sulfate, 1-3 parts of chlorinated paraffin, 1-3 parts of polyethylene wax, 2-5 parts of chlorinated polyethylene and 3-8 parts of light calcium carbonate. The preparation method of the polyvinyl chloride hose comprises the following steps: adding the heat stabilizer, plasticizer, lubricant, modifier and filler into the polyvinyl chloride resin, and carrying out high-speed mixing, granulation, extrusion, cooling for setting, drawing, cutting and detection to prepare the polyvinyl chloride hose. The polyvinyl chloride hose has the characteristics of high temperature resistance, favorable oil resistance, aging resistance, high strength, high toughness, corrosion resistance, long service life and favorable flame retardancy.

Description

technical field [0001] The invention relates to the technical field of PVC pipe production, in particular to a preparation method of a polyvinyl chloride hose. Background technique [0002] As one of the products of scientific and technological development, PVC pipes are readily available in daily life. PVC pipes have the characteristics of light weight, corrosion resistance, high compressive strength, safety and convenience. Polyvinyl chloride hose is made of polyvinyl chloride (PVC) resin. Pure polyvinyl chloride (PVC) resin belongs to a class of strong polar polymers. Its intermolecular force is relatively large, which leads to the softening temperature and melting temperature of PVC. The temperature is relatively high, and generally requires 160-210°C to process; the substituted chlorine groups contained in PVC molecules can easily lead to dehydrochlorination of PVC resin. At the same time, PVC hoses still have certain defects in high temperature resistance and oil resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L9/02C08L91/06C08L23/06C08L23/28C08K13/02C08K5/12C08K5/523C08K5/098C08K5/09C08K3/30C08K3/26B29C47/92B29C47/88B29L23/00B29C48/92
CPCB29C48/10B29C48/92B29C2948/9259B29C2948/92704B29L2023/005C08K2201/014C08L27/06C08L2201/08C08L2203/18C08L9/02C08L91/06C08L23/06C08L23/286C08K13/02C08K5/12C08K5/523C08K5/098C08K5/09C08K2003/3045C08K2003/265
Inventor 何孔高
Owner ANHUI JIUHUA KIMRUN COPPER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com