High-hardness anti-cracking mica powder modified silica matrix EPC coating and preparation method thereof

A mica powder and anti-cracking technology, which is applied in coatings, manufacturing tools, casting and molding equipment, etc., can solve the problems of uneven peeling performance, uneven bending strength, and affecting gas discharge, so as to reduce local cracking and disperse Improved stability and reduced porosity in castings

Inactive Publication Date: 2016-08-10
MAANSHAN XINGLONG FOUNDRY CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the poor dispersion and suspension of mica in the coating can easily lead to uneven flexural strength after sintering and uneven peeling performance, and the mica becomes flakes, which will block the pores, affect the gas discharge, and cause the pores of the casting, which needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A high hardness anti-cracking mica powder modified quartz-based lost foam coating, made of the following raw materials in parts by weight (kg): quartz powder 100, modified starch 0.9, carboxymethyl cellulose 0.9, sodium bentonite 2.4, mica powder 0.9, tetraacicular zinc oxide whiskers 0.8, silica sol 0.9, ethanol 10, water, flake niobium pentoxide 0.8, graphite foam 2, nano-alumina 2.

[0015] The preparation method of described high-hardness anti-cracking mica powder modified quartz-based lost foam coating comprises the following steps:

[0016] (1) Add silica sol to ethanol, stir evenly, then add mica powder and stir evenly, heat to 60°C, add four needle-shaped zinc oxide whiskers while stirring, heat to 70°C, ultrasonically disperse for 3 minutes, continue stirring until After ethanol volatilization is completed, pulverize and pass through a 100-mesh sieve to obtain modified mica powder;

[0017] (2) Mix flaky niobium pentoxide and graphite foam, grind evenly, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-hardness anti-cracking mica powder modified silica matrix EPC coating. The high-hardness anti-cracking mica powder modified silica matrix EPC coating is prepared from the following raw materials in parts by weight: 100-102 parts of silica powder, 0.9-1.1 parts of modified starch, 0.9-1.1 parts of carboxymethyl cellulose, 2.4-2.6 parts of sodium bentonite, 0.9-1 part of mica powder, 0.8-0.9 part of tetrapod-shaped ZnO whiskers, 0.9-1.1 parts of silica sol, 10-13 parts of ethyl alcohol, an appropriate amount of water, 0.8-1 part of lamellar niobium pentoxide, 2-2.5 parts of graphite foam and 2-2.5 parts of nanometer aluminum oxide. According to the high-hardness anti-cracking mica powder modified silica matrix EPC coating, by utilizing the lamellar niobium pentoxide and the graphite foam, passages can be provided for gas emission during casting, so that cast blebs are reduced; meanwhile, spatial interveined arrangement is formed by the composition, and a stable structure is formed, so that the hardness and bending strength of the coating are improved; and furthermore, the heat dissipation performance of the lamellar niobium pentoxide, the graphite foam and the nanometer aluminum oxide is good, so that the phenomenon of partial cracking of the coating caused by sudden heating is reduced.

Description

technical field [0001] The invention relates to the technical field of lost foam coatings, in particular to a high-hardness anti-cracking mica powder modified quartz-based lost foam coating and a preparation method thereof. Background technique [0002] Lost foam casting is a casting technology with almost no margin, and coating is the key point of lost foam casting. The performance of coating is directly related to the quality of castings. Lost foam coatings generally consist of refractory aggregates, binders, suspending agents, carriers, and additives. As a cheap and easy-to-obtain refractory aggregate, quartz powder is widely used in lost foam casting, but its application is limited due to its poor sintering performance. The principle of the lost foam coating at the beginning of the design is to sinter and peel off. If the sintering performance of the refractory aggregate is poor at the pouring temperature, a sufficient amount of liquid phase cannot be formed. Then the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 张家俊
Owner MAANSHAN XINGLONG FOUNDRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap