A kind of method for manufacturing steel rail and steel rail using nano-bainite material containing rare earth la element

A technology of nano-bainite and bainite, which is applied in the direction of manufacturing tools, furnace types, furnaces, etc., can solve the difficulty of matching the strength, toughness, and extensibility of bainite rails at the same time, and the manufacturing and processing of rails. Restrict the popularization and application of bainite rails, etc., to achieve the effect of economical and recyclable, convenient for large-scale production, and save the heat treatment process

Active Publication Date: 2017-05-17
INNER MONGOLIA UNIV OF SCI & TECH
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The bainite rails involved in the above patents have the following technical problems: more expensive alloys Mo and Ni alloys are added to the bainite rails; ; The manufacturing, processing technology and post-sequence heat treatment process of the rail are complicated, the process is not easy to control, and it is not conducive to energy saving and emission reduction, etc.; these factors greatly limit the popularization and application of bainite rail
However, there are no relevant patents and reports on the application of rare earths in air-cooled bainite rails containing alloys such as Mn and Cr.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for manufacturing steel rail and steel rail using nano-bainite material containing rare earth la element
  • A kind of method for manufacturing steel rail and steel rail using nano-bainite material containing rare earth la element
  • A kind of method for manufacturing steel rail and steel rail using nano-bainite material containing rare earth la element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] Another aspect of the present invention provides a method for preparing a nano-bainite rail containing rare earth La element, comprising the following steps:

[0044] The smelting step: specifically includes: 1) deoxidation and desulfurization step, deoxidation and desulfurization of the material matrix, so as to obtain a pure material structure; 2) element addition step, in the pure material structure, the added elements and content weight percentage They are: carbon C: 0.18%-0.30%, manganese Mn: 1.4%-1.8%, silicon Si: 0.8%-1.0%, chromium Cr≤1.0%, molybdenum Mo: 0.25-0.32%, lanthanum La: 0.0050%- 0.015%, the rest is iron Fe and impurities, satisfying the relationship: 3.0%≤Mn+Si+Cr+Mo≤3.82%; 3) refining step, after adding alloy elements, enter the LF furnace (LADLE FURNACE, ladle refining furnace) for refining, After adding different contents of rare earth La, VD furnace (Vacuum Degassing, vacuum degassing furnace) is used for vacuum degassing treatment, and then conti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing a steel rail through a nano bainite material containing the rare earth La element and the steel rail. The method includes the steps that smelting is carried out, wherein smelting comprises the deoxidation and desulfuration step, the element adding step and the refining and vacuum degassing step; rolling is carried out; and cooling is carried out. According to the preparing method, as the rare earth La is added, the rare earth La and Mn, Cr and Si alloy elements will jointly strengthen the hardenability effect, and therefore the strengthening effect is improved; in addition, expensive alloy Ni is not added, grading cooling control after rolling is used in a combined manner, and therefore the strength of steel is further improved; and meanwhile, the toughness of the steel is improved through the effects of modifying inclusion, grain boundary purification, bainite wattle refining, dislocation generation promoting and the like of the rare earth in the bainite steel, and therefore the steel rail has the excellent toughness.

Description

technical field [0001] The invention relates to a manufacturing method of a steel rail and the steel rail thereof, in particular to a method for manufacturing the steel rail and the steel rail thereof by using a nano-bainite material containing rare earth La element. Background technique [0002] With the vigorous development of high-speed railways in the world, the comprehensive performance of high-speed railway rails is increasingly demanding. Bainite rail is a new generation of ultra-high-strength rail developed by my country according to the needs of railway development and its own resource characteristics. It has ultra-high strength (up to 1500MPa) due to its unique composition design. The composition feature is that Mn, Cr, Alloys such as Mo and Ni can improve the air-cooling hardenability of bainite, inhibit the precipitation of carbides, and make C solid solution, which can make the greatest contribution to the strength; its air-cooling self-hardening characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C22C38/04C22C38/02C22C38/18C22C38/12C21D8/00C21D9/04
CPCC21D6/005C21D8/005C21D9/04C21D2211/002C22C33/04C22C38/005C22C38/02C22C38/04C22C38/12C22C38/18
Inventor 包喜荣王晓东陈林田仲良
Owner INNER MONGOLIA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com