TPE (thermal plastic elastomer) and application thereof

An elastomer and elastic technology, applied in the field of polymer thermoplastic elastomers, can solve the problems of heavy and environmental protection, anti-aging performance of EPDM particles, color fastness, tensile strength, flame retardant elasticity, etc. The effect of high tensile strength

Inactive Publication Date: 2016-06-22
山东世纪联合新材料科技有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] EPDM particles used in sports venues, that is, EPDM granules, anti-aging performance, color fastness, tensile strength, flame retardancy, and elasticity cannot normally meet the needs of high-end sports venues, and the rebound rate and resistance to stretching caused by ground cracks Impact, color fading, and grain aging after one year have brought many disadvantages to sports venues. Most lawn grains are filled with black rubber grains, which are heavy and not environmentally friendly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TPE (thermal plastic elastomer) and application thereof
  • TPE (thermal plastic elastomer) and application thereof
  • TPE (thermal plastic elastomer) and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Prepare the following raw materials in parts by mass: chlorinated polyethylene 100, calcium carbonate 15, crosslinking agent 1, auxiliary agent 0.5, zinc oxide 0.5, azodicarbonamide 1.5.

[0032] The above-mentioned raw materials in parts by mass are added to an internal mixer, and are compacted at 105 degrees to make TPE elastomers.

Embodiment 2

[0034] Prepare the following raw materials in parts by mass: chlorinated polyethylene 90, calcium carbonate 10, crosslinking agent 0.5, auxiliary agent 0.3, zinc oxide 0.3, azodicarbonamide 1.5.

[0035] The above-mentioned raw materials in parts by mass are added to an internal mixer, and are compacted at 105 degrees to make TPE elastomers.

Embodiment 3

[0037] Prepare the following raw materials in parts by mass: chlorinated polyethylene 110, calcium carbonate 20, crosslinking agent 1.5, auxiliary agent 1.5, zinc oxide 1.5, azodicarbonamide 2.1.

[0038] The above-mentioned raw materials in parts by mass are added to an internal mixer, and are compacted at 105 degrees to make TPE elastomers.

[0039] Embodiment 1 is a preferred version of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a TPE (thermal plastic elastomer) and application thereof, and belongs to the technical field of the macromolecular TPE. The TPE is characterized by being prepared by adding the following raw materials in parts by weight into an internal mixer to be subjected to 105-DEG C internal mixing: 90 to 110 parts of chlorinated polyethylene, 10 to 20 parts of calcium carbonate, 0.5 to 1.5 parts of cross-linking agents, 0.3 to 1.5 parts of accessory ingredients, 0.3 to 1.5 parts of zinc oxide and 1.5 to 2.1 parts of azodicarbonamide. The TPE has the characteristics of aging resistance, color change avoidance, flame-retardant performance, high tensile strength and the like, and can be applied to runway color particles, lawn color particles, lawn buffer ground pads and prefabricated runway coiled materials.

Description

technical field [0001] The invention relates to a TPE elastomer and its application, and belongs to the technical field of polymer thermoplastic elastomers. Background technique [0002] Thermoplastic elastomer is a type of elastomer that has the elasticity of rubber at room temperature and can be plasticized at high temperature. Thermoplastic elastomer has the physical and mechanical properties of vulcanized rubber and the processability of thermoplastics. It is a new type of polymer material between rubber and resin, and is often called the third-generation rubber. [0003] TPE elastomer has some defects. Its heat resistance is not as good as that of rubber. As the temperature rises, the physical properties decrease greatly, so the scope of application is limited. At the same time, the compression deformation, resilience, and durability are inferior to those of rubber, and the price is often higher than that of similar rubber. But generally speaking, the advantages of TP...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08K13/02C08K3/26C08K3/22C08K5/14C08J9/10
CPCC08J9/103C08J2203/04C08J2323/28C08K3/22C08K3/26C08K5/14C08K13/02C08K2003/2296C08K2003/265C08L2201/02C08L2201/08C08L2203/14C08L2207/04C08L23/286
Inventor 张振秀路玲
Owner 山东世纪联合新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products