Electric power engineering construction tool box and preparation method thereof

A construction tool and power engineering technology, applied in the field of power equipment, can solve the problems of insulation performance, flame retardant performance and mechanical strength that cannot meet the requirements, and achieve the effects of improving resin compatibility, low production cost, and improving thermal conductivity and corrosion resistance

Inactive Publication Date: 2016-06-22
JUNAN POWER SUPPLY CO OF STATE GRID SHANDONG ELECTRIC POWER CO +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The insulation properties, flame retardant properties and mechanical strength of the existing power engineering toolbox materials cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric power engineering construction tool box and preparation method thereof
  • Electric power engineering construction tool box and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A power engineering construction tool box, which includes a box body, and the box body is prepared according to the following method:

[0020] Step 1) ball milling, step 2) crushing and grinding, step 3) resin modification, step 4) calcining and mixing, step 5) stirring, melting and injection molding;

[0021] Specifically, the box body is prepared according to the following method:

[0022] Step 1) Ball milling: Mix borax, silicon carbide and active agent evenly according to the mass ratio of 50:30:1, and put them into the ball milling tank. The ball milling time is 6 hours, the ball mill speed is 1000 rpm, and the ball milling is until the powder particle size is 200 meshes to obtain mixture 1;

[0023] Step 2) Crushing and grinding: add perlite and sepiolite to the crusher at a mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 200 meshes, which is the mixture 2;

[0024] Step 3) Resin modification: add Mixture 1, Mixture 2, a...

Embodiment 2

[0029] A power engineering construction tool box, which includes a box body, and the box body is prepared according to the following method:

[0030] Step 1) ball milling, step 2) crushing and grinding, step 3) resin modification, step 4) calcining and mixing, step 5) stirring, melting and injection molding;

[0031] Specifically, the box body is prepared according to the following method:

[0032] Step 1) Ball milling: Mix borax, silicon carbide and active agent evenly according to the mass ratio of 50:30:1, and put them into the ball milling tank. The ball milling time is 6 hours, the ball mill speed is 1000 rpm, and the ball milling is until the powder particle size is 200 meshes to obtain mixture 1;

[0033] Step 2) Crushing and grinding: add perlite and sepiolite to the crusher at a mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 200 meshes, which is the mixture 2;

[0034] Step 3) Resin modification: add Mixture 1, Mixture 2, a...

Embodiment 3

[0039] Box material performance test of the present invention:

[0040] 1. The box body material prepared in embodiment 1-2 is made standard test piece according to test standard, carries out following performance test, and the results are shown in Table 1:

[0041] Table 1

[0042]

[0043] 2. Corrosion resistance test: Take salt solution as an example, soak the test material in 10% sodium chloride solution for 240 hours, and measure the main performance parameters, see Table 2:

[0044] Table 2

[0045] group Flame retardant properties Insulation performance retention rate (%) Tensile strength retention (%) Elongation at break (%) Example 1 V0 96.3 98.7 98.1 Example 2 V0 96.2 98.9 98.3

[0046] 3. High temperature resistance performance test: The performance test of the box material prepared in Examples 1 and 2 under high temperature conditions: the selected temperature is 90°C, and the cable material is placed at this temperature fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of electric equipment and discloses an electric power engineering construction tool box.The box comprises a box body.The box is characterized by being prepared through the method comprising the steps of 1, ball milling; 2, smashing and grinding; 3, resin modification; 4, calcination and mixing; 5, stirring, fusion and injection molding.The tool box is prepared from high-performance plastic materials, and has the better insulation and flame retardant performance, the excellent mechanical performance, corrosion resistance and high temperature resistance.

Description

technical field [0001] The invention relates to the field of power equipment, in particular to a power engineering construction tool box and a preparation method thereof. Background technique [0002] The power engineering construction tool box is used to hold the power engineering construction tools. There are many kinds of materials for the tool box, the common ones are plastic, injection molding, blow molding, etc. In electric power construction work, in order to ensure operational safety and reliability of power supply, power tools are widely used. Power tools are collectively referred to as power engineering construction safety operation tools, live working tools and insulation protection tools, usually including insulating gloves, insulating boots, ground guns, electroscope pens, and insulating rods. The insulation performance of damp or polluted power tools will be reduced, which will seriously endanger the life safety of workers and the operation safety of power gri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/00C08L69/00C08L29/04C08L91/00C08K13/06C08K9/00C08K3/04C08K5/521C08K3/34C08K3/22
CPCC08L23/00C08K2201/003C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2205/035C08L69/00C08L29/04C08L91/00C08K13/06C08K9/00C08K3/04C08K5/521C08K3/34C08K2003/2227C08K3/346
Inventor 孙运东纪荣
Owner JUNAN POWER SUPPLY CO OF STATE GRID SHANDONG ELECTRIC POWER CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products