Conduit for molten glass, container for molten glass, manufacturing method thereof, glass article manufacturing apparatus, and glass article manufacturing method

A glass melting and manufacturing method technology, applied in the field of glass article manufacturing and glass article manufacturing device, can solve the problems of difficulty in suppressing bubbles, difficulty in bubbles, and high viscosity, and achieve the effects of preventing the residue of bubbles and preventing the generation of bubbles

Active Publication Date: 2017-09-26
ASAHI GLASS CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the air bubbles thus generated remain in the manufactured glass product, the quality of the glass product deteriorates
[0007] Especially in the case of alkali-free glass substrates that do not substantially contain alkali metal oxides such as liquid crystal displays (LCD), organic electroluminescence-displays (OLED), inorganic electroluminescence-displays, etc., due to the melting point of alkali-free glass High, high viscosity compared with alkali-containing glass, so the bubbles in the glass melt are difficult to float up, so it is difficult to suppress the bubbles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conduit for molten glass, container for molten glass, manufacturing method thereof, glass article manufacturing apparatus, and glass article manufacturing method
  • Conduit for molten glass, container for molten glass, manufacturing method thereof, glass article manufacturing apparatus, and glass article manufacturing method
  • Conduit for molten glass, container for molten glass, manufacturing method thereof, glass article manufacturing apparatus, and glass article manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0117] (Example 1 (evaluation of porosity))

[0118] In this example, in order to study the state of the thermal spray coating after sintering, a thermal spray coating was formed on a refractory brick, and after exposure to an oxygen-containing atmosphere (atmospheric atmosphere) at 1400°C for 5 hours, the following procedure was performed: The state of the structure of the thermal spray coating was observed. Observation was performed by cutting out a cross section of the thermal spray coating, polishing it, etching it, and then magnifying it 50 times with an optical microscope. The porosity indicating the state of the structure was calculated from the area ratio of the pores after binarizing the luminance. In this binarization, the length and width of the target area are set to 0.6 mm and 0.3 mm, respectively. When calculating, randomly select five locations from the section of the thermal spray coating, and use the average value.

[0119] In addition, in order to study th...

example 2

[0155] (Example 2 (Suppressing effect of air bubbles 1))

[0156] Using the raw material C above, a thermal spray coating was formed on the outer surface of an aluminum cylindrical mold. Thereafter, the aluminum mold was dissolved and removed to obtain a bottomed cylindrical container formed only of the thermal spray coating. The opening diameter of the container was 30 mm, the height was 30 mm, and the thickness was 0.3 mm.

[0157] The cullet was put into the container, and heated under the following conditions to melt the cullet. The cullet is the following non-alkali glass, the water content in the glass β-OH is 0.5mm -1 .

[0158] Expressed in mass percent based on oxides,

[0159] SiO 2 : 60%,

[0160] Al 2 o 3 : 17%,

[0161] B 2 o 3 :8%,

[0162] MgO: 3%,

[0163] CaO: 4%,

[0164] SrO: 8%

[0165] (initial melting condition)

[0166] The temperature was raised from room temperature to 300° C. for 2 hours at a heating rate of 150° C. / hour. Afterwards, ...

example 3

[0172] (Example 3 (Suppression effect of air bubbles 2))

[0173] Using the raw material C described above, a thermal spray coating was formed on the side surface other than the bottom surface inside a bottomed cylindrical container made of platinum. The width of the container was 45 mm, the depth was 45 mm, and the height was 45 mm, and the shape of the upper opening was rectangular. The film thickness of the thermal spray coating formed inside was 0.3 mm.

[0174] The cullet was added to the vessel and the cullet was melted under the above initial melting conditions. The depth of the molten glass was 15mm. Then, generation of air bubbles at the interface between the glass melt and the container wall surface was evaluated under the above-mentioned main test conditions.

[0175] As a result, a large number of bubbles were confirmed at the interface between the bottom surface of the inner side where the thermal spray coating was not formed and the molten glass, and no air bu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
strain pointaaaaaaaaaa
strain pointaaaaaaaaaa
Login to View More

Abstract

　The present invention pertains to a method for producing a conduit for a glass melt or a container for a glass melt by forming, on at least a portion of the inner surface of a platinum or platinum alloy hollow tube, a coating obtained by thermal spraying and satisfying conditions (1)-(4) below, and subsequently exposing the coating to an oxygen-containing atmosphere at 1300-1800°C. (1) The average film thickness of the coating is 0.1-0.5 mm; (2) A starting material containing a platinum alloy and at least one element selected from the group consisting of zirconium (Zr) and yttrium (Y) is used in the formation of the coating; (3) The platinum alloy in (2) is an alloy of platinum (Pt) and at least one element selected from the group consisting of rhodium (Rh), iridium (Ir), gold (Au), palladium (Pd), and ruthenium (Ru), and the total content of the element(s) other than platinum is 5-40 mass% relative to the total mass of the platinum alloy; (4) In the starting material in (2), the total content of the element(s) other than the platinum alloy relative to the total mass of the platinum alloy is 0.05-3 mass%.

Description

technical field [0001] The present invention relates to a conduit for molten glass or a container for molten glass used as a conduit for molten glass in a glass article manufacturing apparatus, and to a manufacturing method thereof. [0002] Moreover, this invention relates to the manufacturing apparatus of a glass article using the conduit for glass melts, or the container for glass melts. [0003] Moreover, this invention relates to the manufacturing method of a glass article using this glass manufacturing apparatus. Background technique [0004] Platinum or platinum and other precious metal elements such as rhodium (Rh) and gold (Au) are used as constituent materials of glass manufacturing equipment (melting tank, clarification tank, adjustment tank, stirring tank, cooling tank, etc., and their connecting passages). , an alloy of palladium (Pd), iridium (Ir), and ruthenium (Ru) (hereinafter, platinum and platinum alloys are collectively referred to as platinum materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B5/43
CPCC03B5/43C03B5/42C23C4/06C23C4/16C23C4/18C23C4/134Y02P40/50
Inventor 岛崎刚
Owner ASAHI GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com