High-performance flame-retardancy insulating plastic material and preparation method thereof

A plastic material and high-performance technology, applied in the field of plastic materials, can solve problems such as flammability, short service life, and aging resistance

Inactive Publication Date: 2016-06-15
JIN BAOLI TECH SUZHOU
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional plastic products have the advantages of easy processing, free coloring, toughness, non-thermal conduction, non-conduction, corrosion resistance, etc., but at the same time, these plastic products have disadvantages such as flammability, aging resistance, and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0009] The preparation method of the high-performance flame-retardant insulating plastic material comprises the following steps:

[0010] (1) Weigh each raw material according to parts by weight;

[0011] (2) Mix polyphenylene sulfide, polybutylene terephthalate, cellulose acetate, polylactic acid, polycarbonate, glass fiber, and polytetrafluoroethylene, add 20% ethanol solution, and heat at 8000r / m Stir for 15-30 minutes in the state to obtain the mixed solution A;

[0012] (3) Mix graphite, ceramic powder, magnesium oxide, aluminum oxide, boron nitride, talc powder, and barium sulfate, add 0.9% acetic acid solution, adjust the pH to 6.5, and stir at 8000r / m for 15-30 minutes , to get the mixture B;

[0013] (4) Mix mixed solution A and mixed solution B, heat to 80-100°C, add epoxy silane, flame retardant and stabilizer, and stir for 45-60 minutes at 500-1000r / m to obtain mixed solution C ;

[0014] (5) Heat the mixed solution C to 150-200°C, then add sodium trichlorophos...

Embodiment 1

[0021] (1) Weigh each raw material according to parts by weight: 10 parts of polyphenylene sulfide, 5 parts of polybutylene terephthalate, 10 parts of acetate fiber, 10 parts of polylactic acid, 10 parts of polycarbonate, 5 parts of glass fiber , 5 parts of polytetrafluoroethylene, 5 parts of graphite, 5 parts of ceramic powder, 5 parts of magnesium oxide, 5 parts of aluminum oxide, 5 parts of boron nitride, 5 parts of talcum powder, 2 parts of barium sulfate, 5 parts of sodium trichlorophosphate, 5 parts of epoxy silane, 5 parts of triphenyl phosphate, 5 parts of sodium stearate;

[0022] (2) Mix polyphenylene sulfide, polybutylene terephthalate, cellulose acetate, polylactic acid, polycarbonate, glass fiber, and polytetrafluoroethylene, add 20% ethanol solution, and heat at 8000r / m State stirring for 15 minutes to obtain the mixed solution A;

[0023] (3) Mix graphite, ceramic powder, magnesium oxide, aluminum oxide, boron nitride, talc powder, and barium sulfate, add 0.9% ...

Embodiment 2

[0029] (1) Weigh each raw material according to parts by weight: 12 parts of polyphenylene sulfide, 6 parts of polybutylene terephthalate, 12 parts of cellulose acetate, 12 parts of polylactic acid, 12 parts of polycarbonate, 6 parts of glass fiber , 6 parts of polytetrafluoroethylene, 6 parts of graphite, 6 parts of ceramic powder, 6 parts of magnesium oxide, 6 parts of aluminum oxide, 6 parts of boron nitride, 6 parts of talcum powder, 3 parts of barium sulfate, 6 parts of sodium trichlorophosphate, 6 parts of epoxy silane, 6 parts of polyphosphate amine, 6 parts of zinc stearate;

[0030] (2) Mix polyphenylene sulfide, polybutylene terephthalate, cellulose acetate, polylactic acid, polycarbonate, glass fiber, and polytetrafluoroethylene, add 20% ethanol solution, and heat at 8000r / m State stirring for 20 minutes to obtain the mixed solution A;

[0031] (3) Mix graphite, ceramic powder, magnesium oxide, aluminum oxide, boron nitride, talcum powder, and barium sulfate, add 0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance flame-retardancy insulating plastic material which comprises the following raw materials in parts by weight: 10-20 parts of polyphenylene sulfide, 5-15 parts of poly (butylene terephthalate), 10-35 parts of cellulose acetate fiber, 10-15 parts of polylactic acid, 10-25 parts of polycarbonate, 5-20 parts of glass fiber, 5-10 parts of polytetrafluoroethylene, 5-10 parts of graphite, 5-10 parts of ceramic powder, 5-10 parts of magnesium oxide, 5-10 parts of aluminum oxide, 5-10 parts of boron nitride, 5-15 parts of talcum powder, 2-5 parts of barium sulfate, 5-10 parts of trichlorine sodium phosphate, 5-10 parts of epoxy silane, 5-10 parts of a flame retardant and 5-10 parts of a stabilizing agent. The flame retardancy of a plastic material can be improved, and the insulating function of the plastic material can be improved. The invention further discloses a corresponding preparation method.

Description

technical field [0001] The invention relates to the technical field of plastic materials, in particular to a high-performance flame-retardant insulating plastic material and a preparation method thereof. Background technique [0002] Plastic materials are traditionally made of polymers as the basic component, and after adding additives, they are processed and molded or cross-linked and solidified under a certain temperature and pressure. Since most polymers have good insulating properties, it is widely used as an insulating material. Plastics are mainly divided into general-purpose plastics, engineering plastics and hybrid plastics. Traditional plastic products have the advantages of easy processing, free coloring, toughness, non-thermal conduction, non-conduction, corrosion resistance, etc., but at the same time, these plastic products have disadvantages such as flammability, aging resistance, and short service life. Therefore, there is an urgent need to develop a plastic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08L1/12C08L67/04C08L69/00C08L67/02C08L27/18C08K13/04C08K7/14C08K3/04C08K3/22C08K3/38C08K3/34C08K3/30B29C47/92B29C48/92
CPCB29C48/92B29C2948/9258C08L1/12C08L67/04C08L69/00C08L81/02C08L2201/02C08L2205/02C08L2205/035C08L67/02C08L27/18C08K13/04C08K7/14C08K3/04C08K2003/222C08K2003/2227C08K2003/385C08K3/34C08K2003/3045
Inventor 李明华
Owner JIN BAOLI TECH SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap