Potassium silicate binder

A potassium water glass and binder technology, applied in the direction of adhesives, inorganic adhesives, polymer adhesive additives, etc., can solve the problem of poor water resistance, low bonding strength and long curing time of pure water glass adhesives. problem, to achieve the effect of improving compactness and flame retardancy, good dispersibility and low price

Inactive Publication Date: 2016-03-30
LUOYANG LVREN ENVIRONMENTAL EQUIP
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the pure water glass adhesive has defects such as poor water resistance, low bonding strength, easy pulverization, and long curing time.
Therefore, its application is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1 of the present invention provides a potassium silicate binder, which includes the following raw materials in parts by mass: 50 parts of potassium silicate, 8 parts of white carbon black, 28 parts of magnesium oxide, 10 parts of magnesium chloride, 10 parts of magnesium sulfate, condensation Aluminum phosphate 5 parts, Pingping plus O5 parts.

[0012] The preparation method of the above-mentioned potassium water glass binder provided by the present embodiment comprises the following steps: first potassium water glass and water are placed in a three-necked flask, stirred for 10 minutes; then white carbon black, magnesium oxide, magnesium chloride and magnesium sulfate are added , Stir for 15 minutes; After that, add condensed aluminum phosphate and stir for 5 minutes, then pour it out and cool to room temperature; finally add Pingping and O and stir evenly to obtain a potassium silicate binder. The entire preparation process is heated in a 60° C. water bath b...

Embodiment 2

[0015] Embodiment 2 of the present invention provides a potassium silicate binder, which includes the following raw materials in parts by mass: 55 parts of potassium silicate, 10 parts of white carbon black, 24 parts of magnesium oxide, 8 parts of magnesium chloride, 8 parts of magnesium sulfate, condensation 6 parts of aluminum phosphate, 8 parts of flat plus O.

[0016] The preparation method of the above-mentioned potassium water glass binder provided by the present embodiment comprises the following steps: first potassium water glass and water are placed in a three-necked flask, stirred for 12 minutes; then white carbon black, magnesium oxide, magnesium chloride and magnesium sulfate are added , stirred for 20 minutes; after that, added condensed aluminum phosphate and stirred for 10 minutes, then poured out, cooled to room temperature; finally added Pingping plus O and stirred evenly to obtain a potassium silicate binder. The entire preparation process is heated in a 50° ...

Embodiment 3

[0019] Embodiment 3 of the present invention provides a potassium silicate binder, which includes the following raw materials in parts by mass: 60 parts of potassium silicate, 11 parts of white carbon black, 21 parts of magnesium oxide, 8 parts of magnesium chloride, 7 parts of magnesium sulfate, condensation 8 parts of aluminum phosphate, 9 parts of Pingping plus O.

[0020] The preparation method of the above-mentioned potassium water glass binder provided by the present embodiment comprises the following steps: first potassium water glass and water are placed in a three-necked flask, stirred for 14 minutes; then white carbon black, magnesium oxide, magnesium chloride and magnesium sulfate are added , stirred for 20 minutes; after that, added condensed aluminum phosphate and stirred for 15 minutes, then poured out, cooled to room temperature; finally added Pingping plus O and stirred evenly to obtain a potassium silicate binder. The entire preparation process is heated in a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a potassium silicate binder. The potassium silicate binder is characterized by comprising raw materials in parts by mass as follows: 30-50 parts of potassium silicate, 8-14 parts of white carbon black, 14-28 parts of magnesium oxide, 5-10 parts of magnesium chloride, 5-10 parts of magnesium sulfate, 5-10 parts of condensed aluminum phosphate, 2-8 parts of peregal O and 6-12 parts of water. The potassium silicate binder has the advantages as follows: the price is low, the application range is wide, normal-temperature curing is realized, water resistance is good, high temperature resistance is realized, flame retardancy is good, binding strength is high, the raw materials are foamed, the dosage is saved, the cost is reduced and the like.

Description

technical field [0001] The invention belongs to the technical field of bonding materials, in particular to a potassium silicate bonding agent. Background technique [0002] With the improvement of social economy and living standards, binders are playing an increasingly important role in people's daily life and production. At present, most of the binders on the market are organic binders. However, organic binders will cause some environmental pollution problems in the process of production and use, which will cause great harm to human health and the environment. Moreover, the organic binder has poor high temperature resistance and is easy to burn, so the fire resistance is poor. So these disadvantages limit the further application of organic binders. The inorganic binder not only has excellent high temperature resistance, but also does not produce harmful substances to pollute the environment during the production and preparation process. The most widely used inorganic bin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J1/02C09J11/04C09J11/08
Inventor 肖建军许道立刘改正张国峰
Owner LUOYANG LVREN ENVIRONMENTAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com