Lithium secondary battery electrolyte and lithium secondary battery containing same

A secondary battery and electrolyte technology, applied in the field of lithium secondary battery electrolyte and lithium secondary battery containing the same, can solve the problems of high volatility and high flammability, and achieve the improvement of battery swelling, discharge capacity, and high flammability. The effect of capacity recovery rate

Active Publication Date: 2018-08-28
SK ON CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, such an organic electrolyte is usually volatile and highly flammable. Therefore, when it is applied to a lithium-ion secondary battery, when internal heat is generated due to overcharging or overdischarging, internal short circuits may occur. Safety issues under high temperature such as fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium secondary battery electrolyte and lithium secondary battery containing same
  • Lithium secondary battery electrolyte and lithium secondary battery containing same
  • Lithium secondary battery electrolyte and lithium secondary battery containing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0114] [Example 1] Tetrakis (2,2,3,3,3-pentafluoropropyl) diboronic acid ester (tetrakis (2,2,3,3,3-pentafluoropropyl) hypodiborate, hereinafter, also known as 'PEA65 ')Synthesis

[0115]

[0116] In a 100ml round bottom flask, 6.00g of 2,2,3,3,3-pentafluoro-1-propanol (2,2,3,3,3-pentafluoro-1-propanol, 40mmol) and 3.96 g of tetrakis(dimethylamino)diboron (tetrakis(dimethylamino)diboron, 20mmol) was dissolved in 30ml of heptane, and then the temperature was raised to 50°C under nitrogen atmosphere. After reacting at 50° C. for 24 hours, the temperature was lowered to normal temperature. After filtering the crystals generated at normal temperature, the filtrate was vacuum-dried to obtain 8.0 g of the title compound.

[0117] 1 H-NMR (400MHz, CDCl 3 )δ: 4.18(t, J=20.9Hz, 8H)

Embodiment 2-7 and comparative example 1-2

[0119] Dissolve LiPF in a mixed solution of ethylene carbonate (EC): ethylmethyl carbonate (EMC) at a volume ratio of 3:7 6 , to obtain a 1.0M solution, and use this solution as the basic electrolyte (1M LiPF 6 , EC / EMC=3:7), and further put in the components described in the following Table 1 to prepare the electrolyte solution.

[0120] A method for preparing a battery using the non-aqueous electrolyte solution is as follows.

[0121] As the positive active material, LiNiCoMnO 2 and LiMn 2 o 4 Mixed at a weight ratio of 1:1, mixed with polyvinylidene fluoride (PVdF) as a binder and carbon as a conductive agent at a weight ratio of 92:4:4 and dispersed in N-methyl-2 -pyrrolidone, thereby preparing positive electrode slurry. This slurry was coated on an aluminum foil having a thickness of 20 μm, dried and rolled to prepare a positive electrode. Mix artificial graphite as the negative electrode active material, styrene-butadiene rubber as the binder, and carboxymethyl cel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a lithium secondary battery electrolyte and a lithium secondary battery containing the same, and specifically, provides a secondary battery electrolyte with excellent high temperature stability, low temperature discharge capacity and life characteristics, the secondary battery The electrolyte contains a lithium salt; a non-aqueous organic solvent; and a boron derivative shown in the following chemical formula 1: in the chemical formula 1, R1 to R4 are independently (C1-C10) alkyl, (C6-C12) aryl or (C6-C12) aryl (C1-C10) alkyl, the alkyl, aryl and aralkyl groups of R1 to R2 can be further selected from cyano, hydroxyl, halogen, (C1-C10) alkyl and (C6-C12) One or more substituents in the aryl group are substituted.

Description

technical field [0001] The present invention relates to an electrolyte solution for a lithium secondary battery and a lithium secondary battery containing the same, more specifically, to a lithium secondary battery electrolyte containing boron derivatives and a lithium secondary battery containing the same. Background technique [0002] Recently, with the wide spread of mobile electronic devices, and with the miniaturization, thinning and light weight of these mobile electronic devices, people are focusing on the miniaturization and weight reduction of secondary batteries used as their power sources, and the ability to make batteries Extensive research has been carried out on long-term charging and discharging. [0003] Lithium secondary batteries generate electrical energy through oxidation and reduction reactions when lithium ions are inserted and removed from the positive and negative electrodes. Between the positive electrode and the negative electrode, an organic elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/0567H01M10/0525C07F5/02
CPCC07F5/02H01M10/0525H01M10/0567H01M10/0568H01M10/0569H01M2220/30H01M2300/0034H01M2300/0037Y02E60/10H01M10/052
Inventor 金镇诚金喆禹吴承娟李光国李成日
Owner SK ON CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap