Aluminum-based in-situ composite material formed based on laser 3D printing and preparation method of aluminum-based in-situ composite material

An in-situ composite material and 3D printing technology, which is applied in the direction of additive processing, process efficiency improvement, energy efficiency improvement, etc., can solve the problems that the mechanical properties such as strength and wear resistance of aluminum alloy cannot be effectively improved, and achieve excellent Comprehensive mechanical properties, improvement of overall mechanical properties, and the effect of improving mechanical properties

Active Publication Date: 2016-02-17
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the existing aluminum-based in-situ composite materials and the existing technical means for preparing aluminum-based in-situ composite materials cannot effectively improve the mechanical properties of aluminum alloys such as strength and wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum-based in-situ composite material formed based on laser 3D printing and preparation method of aluminum-based in-situ composite material
  • Aluminum-based in-situ composite material formed based on laser 3D printing and preparation method of aluminum-based in-situ composite material
  • Aluminum-based in-situ composite material formed based on laser 3D printing and preparation method of aluminum-based in-situ composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The invention is a method for preparing an aluminum-based in-situ composite material based on laser 3D printing, including:

[0048] Equipped with raw materials, Al-Si-Mg alloy powder with a mass fraction ratio of 4:1 of 99.7% purity and an average particle size of 30um and Al with a purity of 99.5% and an average particle size of 5um 2 o 3 The powder is mixed to obtain a mixture; wherein, the composition and mass percentage of the Al-Si-Mg alloy powder are 7.2% Si, 0.28% Mg, 2 o 3 The role of powder wettability promotes the uniformity of the dispersion of raw materials in the subsequent 3D printing process.

[0049] Ball milling, the mixture is milled by batch ball milling process, the diameter is Φ 8mm Al 2 o 3 The ceramic ball is a ball milling medium, the weight ratio of the ball milling medium to the mixture is 5:1, every 10 minutes of ball milling is air-cooled for 5 minutes, and the particle size of the ball milling until the mixture is 1um; the speed of the ...

Embodiment 2

[0056] The invention is a method for preparing an aluminum-based in-situ composite material based on laser 3D printing, including:

[0057] Equipped with raw materials, Al-Si-Mg alloy powder with a mass fraction ratio of 5:1 of 99.8% purity and an average particle size of 30um and Al with a purity of 99.7% and an average particle size of 5um 2 o 3 The mixture obtained by mixing powders; wherein, the composition and mass percentage of Al-Si-Mg alloy powder are 9.2% Si, 0.48% Mg, <0.1% other impurity elements, and the balance is Al .

[0058] Ball milling, the mixture is milled by batch ball milling process, the diameter is Φ 10mm Al 2 o 3 The ceramic ball is a ball milling medium, the weight ratio of the ball milling medium to the mixture is 10:1, every 30 minutes of ball milling is air-cooled for 10 minutes, and the particle size of the ball milling to the mixture is 10 μm; the speed of the balls of the intermittent ball mill is 400r / min, Ball milling time 9h.

[0059] T...

Embodiment 3

[0064] The invention is a method for preparing an aluminum-based in-situ composite material based on laser 3D printing, including:

[0065] Equipped with raw materials, Al-Si-Mg alloy powder with a mass fraction ratio of 6:1 of 99.7% purity and an average particle size of 30um and Al with a purity of 99.5% and an average particle size of 5um 2 o 3 The mixture obtained by mixing powders; wherein, the composition and mass percentage of Al-Si-Mg alloy powder are 8% Si, 0.29% Mg, <0.1% other impurity elements, and the balance is Al.

[0066] Ball milling, the mixture is milled by batch ball milling process, the diameter is Φ 9mm Al 2 o 3 The ceramic ball is a ball milling medium, the weight ratio of the ball milling medium to the mixture is 8:1, every 20 minutes of ball milling is air-cooled for 8 minutes, and the particle size of the ball milling to the mixture is 8um; the speed of the balls of the intermittent ball mill is 380r / min, Ball milling time 6h.

[0067] The mixed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of particle-reinforced aluminum-based in-situ composite materials and discloses an aluminum-based in-situ composite material formed based on laser 3D printing and a preparation method of the aluminum-based in-situ composite material. The preparation method includes the steps that a mixture of Al-Si-Mg alloy powder and Al2O3 powder is prepared; the mixture is ball-milled through an intermittent ball-milling process; a three-dimensional CAD model established through a workpiece is subjected to layered slicing treatment; laser beams are adopted for scanning the laid powder line by line to form a two-dimensional section of the workpiece; and the steps are repeated till the workpiece is machined, and the aluminum-based in-situ composite material with an Al2Si4O10 reinforced element scattered on an Al matrix is formed. The operation method is easy and convenient to carry out, Al-Si-Mg alloy and Al2O3 generate the Al2Si4O10 reinforced phase in situ under the effect of high-energy lasers in the laser forming process, the interface wettability is improved, and then the interface strength of the composite material is enhanced.

Description

technical field [0001] The invention relates to the technical field of particle-reinforced aluminum-based in-situ composite materials, in particular to an aluminum-based in-situ composite material formed based on laser 3D printing and a preparation method thereof. Background technique [0002] Aluminum and its alloy materials have a series of excellent characteristics such as light density, good elasticity, high specific stiffness and specific strength, good impact resistance, good electrical and thermal conductivity, good forming and processing performance, and high recycling and regeneration. They are considered to be " "Sunrise Materials" have been widely used in transportation, aerospace, mineral processing and other fields. However, aluminum and its alloys have problems such as low hardness and poor wear resistance, which greatly limit the application of aluminum and its alloys, and become the bottleneck of research and development in the field of aluminum alloys. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22F3/105B33Y10/00C22C21/00C22C32/00
CPCB22F3/105C22C21/00C22C32/001Y02P10/25
Inventor 顾冬冬决久斌戴冬华
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com