False tooth material composition
A composition and denture technology, applied in the fields of medical science, dentistry, dental preparations, etc., can solve problems such as dentures being difficult to hold, and achieve the effects of low cost, good adaptability and strong transparency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A denture material composition, comprising the following components: 95g of polymethyl methacrylate monomer, 105g of polymethyl methacrylate, 0.10g of polysulfone resin, 0.8g of a mixture of benzyl salicylate and ethanol ( The volume ratio of benzyl salicylate to ethanol is 1:1), and 0.1 g of zinc oxide.
[0020] The method of preparing dentures using the above denture material composition is as follows: using injection molding method, the components are mixed uniformly and heated to 80°C to soften them into a viscous fluid state to obtain a molten liquid, and then the molten liquid is filled into the injection tube , Installed on a special injection machine, pressurized to inject the viscous fluid state into the mold box with the denture female mold, and take out the denture after cooling.
Embodiment 2
[0022] A composition of denture material, comprising the following components: 105g of polymethyl methacrylate monomer, 95g of polymethyl methacrylate, 0.15g of polysulfone resin, a mixture of benzyl salicylate and ethanol (salicylic acid) The volume ratio of benzyl acid to ethanol is 5:1;) 0.5g, zinc oxide 0.3g.
[0023] The method for preparing a denture using the composition of the above denture material is as follows: using an injection molding method, the components are mixed uniformly and heated to 100°C to soften them into a viscous fluid state to obtain a molten liquid, and then the molten liquid is filled into the injection tube , Installed on a special injection machine, pressurized to inject the viscous fluid state into the mold box with the denture female mold, and take out the denture after cooling.
Embodiment 3
[0025] A composition of denture material, comprising the following components: 100 g of polymethyl methacrylate monomer, 102 g of polymethyl methacrylate, 0.12 g of polysulfone resin, a mixture of dibutyl phthalate and ethanol ( The volume ratio of dibutyl phthalate to ethanol is 2:1) 0.6g and zinc oxide 0.2g.
[0026] The method of preparing dentures using the above denture material composition is as follows: using injection molding method, the components are mixed uniformly and heated to 85°C to soften them into a viscous fluid state to obtain a molten liquid, and then the molten liquid is filled into the injection tube , Installed on a special injection machine, pressurized to inject the viscous fluid state into the mold box with the denture female mold, and take out the denture after cooling.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com